Method for synthesizing citricacide-titatnium chelate by microwave chelation process by using new metatitanic acid precipitate

A technology of titanium citrate and metatitanic acid, applied in carboxylate preparation, organic chemistry, etc., can solve the problem of no metatitanic acid and other problems, and achieve the effect of high purity, simple process and stable performance

Inactive Publication Date: 2012-07-11
福建超大现代农业集团有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] After retrieving published patent documents and academic papers related to metatitanic acid, it was not found that using an ice solution in ice water to neutralize titanium salts with alkali to prepare metatitanic acid soluble in citric acid, and to newly precipitate metatitanic acid As a report on the synthesis of titanium citrate as a titanium source, there is no report on the synthesis of titanium citrate by microwave hot-melt chelation process

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] (1) Preparation of titanic acid:

[0046] A. Add 1000ml of ice water at a 1500ml burn of 0 ° C ~ 5 ° C. Under the stirring of the electric mixer, add 10 mL hydrochloric acid and 20ml titanium chloride, generate tetrachloride hydrochloride solution, and use 10%of 10%In the sodium hydroxide solution and titanium titanium titanium hydrochloride, control the temperature of the solution ≤5 ° C, and the pH value of 7.0 ~ 8.0, so that the titanic acid is precipitated in cold water at ≤5 ° C;

[0047] B. The new precipitated titanic acid is washed with distilled water to remove the chlorine ion;

[0048] C. Washing and removing titanic acid that removes chloride ions can be used for acidic chelating after removing part of the centrifuge.

[0049] (2) Preparation of titanium titanium chelars:

[0050] A, citric acid-preparation of titanic acid suspension mixed solution:

[0051]The titanium titanic acid prepared by 20ml titanium titanium contains 8.7g of titanium, and according to t...

Embodiment 2

[0057] (1) Preparation of titanic acid:

[0058] A. Add 1000ml of ice water at a 1500ml burn of 0 ° C ~ 5 ° C. Under the stirring of the electric mixer, add 10 mL hydrochloric acid and 20ml titanium chloride, generate tetrachloride hydrochloride solution, and use 10%of 10%In the sodium hydroxide solution and titanium titanium titanium hydrochloride, control the temperature of the solution ≤5 ° C, and the pH value of 7.0 ~ 8.0, so that the titanic acid is precipitated in cold water at ≤5 ° C;

[0059] B. The new precipitated titanic acid is washed with distilled water to remove the chlorine ion;

[0060] C. Washing and removing titanic acid that removes chloride ions can be used for acidic chelating after removing part of the centrifuge.

[0061] (2) Preparation of titanium titanium chelars:

[0062] A, citric acid-preparation of titanic acid suspension mixed solution:

[0063] The titanium titanic acid prepared by 20ml titanium titanium contains 8.7g of titanium, according to the ...

Embodiment 3

[0069] (1) Preparation of titanic acid:

[0070] A. Add 1000ml of ice water at a 1500ml burn of 0 ° C ~ 5 ° C. Under the stirring of the electric mixer, add 10 mL hydrochloric acid and 20ml titanium chloride, generate tetrachloride hydrochloride solution, and use 10%of 10%In the sodium hydroxide solution and titanium titanium titanium hydrochloride, control the temperature of the solution ≤5 ° C, and the pH value of 7.0 ~ 8.0, so that the titanic acid is precipitated in cold water at ≤5 ° C;

[0071] B. The new precipitated titanic acid is washed with distilled water to remove the chlorine ion;

[0072] C. Washing and removing titanic acid that removes chloride ions can be used for acidic chelating after removing part of the centrifuge.

[0073] (2) Preparation of titanium titanium chelars:

[0074] A, citric acid-preparation of titanic acid suspension mixed solution:

[0075] The titanium titanic acid prepared by 20ml titanium titanium contains 8.7g of titanium, according to the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for synthesizing citricacide-titatnium chelate by a microwave chelation process by using new metatitanic acid precipitate. The method is characterized in that: the new metatitanic acid precipitate is prepared by neutralizing an iced solution of titanium salt by using alkali; the new metatitanic acid precipitate replacing titanium chloride and sulfate is used as raw materials for synthesizing the citricacide-titatnium chelate; and the citricacide-titatnium chelate is synthesized by a microwave hot melting chelation process by using the new metatitanic acid precipitate as a titanium source and citric acid as an acid solvent and chelant. The synthesized citricacide-titatnium chelate is high in purity, does not contain foreign ions such as chlorine ions or sulfur ions, is stable in performance, and can be placed for a long time; titanium gel precipitate is not separated out after the citricacide-titatnium chelate is diluted; and the citricacide-titatnium chelate can be compounded with multiple kinds to metal ions and organic matter, can be reacted with peroxide to form titanium peroxide complex, and can also be compounded into various functional materials. A process is simple and is easy to control.

Description

Technical field [0001] The present invention is a new technology prepared by titanium citrate. It specifically involves new precipitated polar acid that is not contained in chlorine and sulfur ions and can dissolve in citric acid as the source of titanium.New methods of titanium citrate without chlorine and sulfur ions with chelating reactions. Background technique [0002] Titanium citric acid has a wide range of application prospects, such as titanium citrate as a new type of crop growth regulator and functional micro -fertilizer. Titanium titanium titanium has been promoted; citrate titanium titanium titanium is not harmful, and toxic chromium tannants also replacedIt is promoted and applied; titanium titanium has also been proven to have drug effects to resist tumors. [0003] At the same time, titanium titanium is still preparing the front -drive body of titanium -based functional materials such as light catalytic self -cleaning materials, air purification materials, antibac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C59/265C07C51/41
Inventor 徐福乐翁莹冰张美娟林秀翁仁发
Owner 福建超大现代农业集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com