Lean hematite tailing concrete light body building block brick and preparation method thereof

A technology of lean hematite tailings and concrete, applied in the field of lean hematite tailings concrete light block bricks and its preparation, to achieve the effects of eliminating pollution, saving energy and reducing fire hazards

Active Publication Date: 2012-08-08
ANSTEEL GRP MINING CO LTD
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of product structure uniform, dense, high strength, energy-saving, environmental protection, low cost, long service life lean hematite tailings concrete light body block brick, to solve the problem of not using clay, using poor Technical problems of preparing light-weight block bricks from industrial waste such as iron ore tailings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below in conjunction with embodiment.

[0034] Select the following dry raw material components (wt%) of lean hematite tailings concrete light body block bricks and the technical performance indicators achieved are shown in Table 1.

[0035]

[0036] As can be seen from the foregoing examples, the present invention adopts the light body block brick of the above-mentioned dry raw material component (wt%), and through raw material mixing and stirring, compression molding, maintenance, and finished product, its product structure is uniform, and its compressive strength , water absorption rate, anti-freeze-thaw cycle 50 mass loss rate, anti-freeze-thaw cycle 50 strength loss rate and other properties fully meet the requirements of GB / T15229-2002 "light aggregate concrete small hollow block".

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
power levelaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of building bricks and in particular relates to a lean hematite tailing concrete light body building block brick and a preparation method thereof. The hematite tailing concrete light body building block brick is manufactured by dry raw materials by weight percentage: 20%-30% of portland cement, 35%-45% of lean hematite tailing, 10%-20% of ceramsite and 15%-25% coal ash. The preparation method comprises the following process flows: pretreating the dry raw materials, mixing and stirring the materials, preparing wet material slurry, pressing and forming and obtaining end product building block green bricks. The preparation method turns to utilization of lean hematite tailing from earth excavation and field destroy, achieves comprehensive utilization and turns waste into wealth. The light body building block brick manufactured by lean hematite tailing can be used for building tailing ponds, thereby eliminating pollution of tailing on the environment, achieving comprehensive utilization of resource and protecting ecological environment.

Description

technical field [0001] The invention belongs to the technical field of building bricks, and in particular relates to a light-weight block brick made of lean hematite tailings concrete and a preparation method thereof. Background technique [0002] Lean hematite ore is an important type of iron ore in my country, and its beneficiation plays an important role in iron ore beneficiation in my country. Poor hematite tailings are industrial wastes with a large amount of iron content of 10-17% and silica content of 75-85%. A large amount of industrial waste has not been developed and utilized, resulting in a large amount of tailings occupying cultivated land, rivers, and polluting the environment. It is a social public hazard that needs to be solved urgently. The comprehensive utilization of lean hematite tailings can not only eliminate the harm of tailings to the environment, It can also be recycled as a resource, which has good environmental effects and high economic benefits. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/04C04B18/12
CPCY02W30/91
Inventor 于宝新吴庆深徐冬林王长艳
Owner ANSTEEL GRP MINING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products