Impregnation rolling process of plant treatment fire-proof plate

A plant fiber and fireproof board technology, which is applied in the direction of impregnating wood, wood impregnation, and manufacturing tools, can solve the problems of insufficient board strength and non-fireproof boards, and achieve the effects of low cost, improved quality, and easy processing

Active Publication Date: 2014-08-20
GUANGDONG YIXIN HOUSEHOLD MATERIALS GROUP CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above process adopts the impregnation process, it is mainly to impregnate the raw materials, and then process them according to the general paving process, so the produced boards have the defects of not being fireproof and not having enough strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The dipping and rolling process of plant fiber fireproof board comprises the following steps:

[0029] A. Coconut palm fiber with a length of 5-30cm is used as raw material, and the paving machine is used to pave the coconut palm fiber, including carding, laying, needle-punching, spraying glue, drying, and then hot pressing into a slab, the density of the slab is 0.1g / cm3;

[0030] B. Soak the slab in the inorganic gelling slurry, which is made by mixing magnesium chloride, magnesium oxide and water at a molar ratio of 1:5:13, and adding an appropriate amount of water-soluble boric acid to the slurry salt, soaking time is 5 minutes;

[0031] C, the slab after soaking is sent into the roll pressing machine for rolling, the density of the pressed plate is 0.4g / cm3, the moving speed of the plate in the rolling process is 50m / min, and the pressure of the pressing roller is 2500N / cm.

[0032] D. The rolled plate is cured and dried, and the finish is cut to make a plant fib...

Embodiment 2

[0048] The dipping and rolling process of plant fiber fireproof board comprises the following steps:

[0049] A. Coconut palm fiber with a length of 5-30cm is used as raw material, and the paving machine is used to process the coconut palm fiber through the paving process, including carding, laying, needle-punching, spraying glue, drying, and reheating Pressed into a slab, the density of the slab is 0.2g / cm3;

[0050] B. Soak the slab in the inorganic gelling slurry, which is made by mixing magnesium chloride, magnesium oxide and water in a weight ratio of 1:8:9, and adding an appropriate amount of water-soluble boric acid to the slurry salt, soaking time is 10 minutes;

[0051] C, the slab after soaking is sent into the roll pressing machine for rolling, the density of the plate after pressing is 1g / cm3, the moving speed of the plate in the rolling process is 20m / min, and the pressure of the pressing roller is 3500N / cm.

[0052] D. The rolled plate is cured and dried, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dipping and rolling process for a plant fiber fireproof board, comprising the following steps: A. using a paving machine to make a slab with plant fiber silk as a raw material through the paving process, and the density of the slab is 0.1 to 0.2g / cm3; B. Soak the slab in the inorganic gelling slurry with a mass percentage concentration of 50% to 70%; C. Roll the soaked slab; D. Make the rolled slab through curing and drying, etc. into plant fiber fireproof panels. The inorganic gelling slurry is a slurry formed by mixing magnesium chloride, magnesium oxide and water. Due to the above-mentioned production process, not only the board has the characteristics of light weight, anti-corrosion, easy processing, and low cost, but also adds fireproof performance, and at the same time increases the strength of the board; the use of this process also solves the problem of long fiber winding in At the same time, the phenomenon of knotting or entanglement occurs, thereby ensuring the production efficiency of the board and improving the quality of the processed board.

Description

technical field [0001] The invention relates to a production process of a fiber board, in particular to a production process of a fireproof board which is processed and produced with plant fibers as raw materials. Background technique [0002] The current production process of various cement fiberboards is basically the method of mixing, mixing, pouring, and injection molding. The material is formed by fully combining, laying, and pouring molds. However, for long fibers, the above-mentioned production process is not suitable, because long fibers are easily entangled during the process of laying long fibers using the above-mentioned process. , There is a phenomenon of knotting or entanglement, which not only affects the production efficiency of the sheet, but also affects the quality of the processed sheet. [0003] In addition, the Chinese Patent Office has published the patent application document "Production Method of Reed Fiberboard" with the patent application number of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27K3/02B27K3/32B27N3/08
Inventor 黄志平
Owner GUANGDONG YIXIN HOUSEHOLD MATERIALS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com