Mirror face plastic printing ink for OPS (oriented polystyrene) thermoshrinkable film and preparation method thereof
A technology of plastic printing and heat shrinkable film, applied in the field of plastic printing ink, can solve the problems of mirror effect, low adhesion, poor printing effect and the like that cannot be printed on heat shrinkable plastic film
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0033] Implementation 1: A mirror plastic printing ink for OPS heat shrinkable film, the raw materials in its components are respectively:
[0034] Raw material name Mass ratio
[0035] 1. Ethanol 30
[0036] 2. Isopropanol 25
[0037] 3. n-Propyl acetate 5.5
[0038]4. Propylene glycol methyl ether 0
[0039] 5. PVB (polyvinyl butyral) resin 10
[0040] 6. Acrylic 3
[0041] 7. Ultrafine flaky aluminum silver paste 23
[0042] 8. Fixative 2
[0043] 9. Silicone leveling agent 1.5
[0044] This formula is a fast drying formula, suitable for high-speed printing process. Its preparation method is the same as above.
Embodiment 2
[0045] Implementation 2: A mirror plastic printing ink for OPS heat shrinkable film, the raw materials in its components are respectively:
[0046] Raw material name Mass ratio
[0047] 1. Ethanol 20
[0048] 2. Isopropanol 31
[0049] 3. n-Propyl acetate 5.5
[0050] 4. Propylene glycol methyl ether 3.5
[0051] 5. PVB (polyvinyl butyral) resin 10
[0052] 6. Acrylic 3
[0053] 7. Ultrafine flaky aluminum silver paste 23
[0054] 8. Fixative 2
[0055] 9. Silicone leveling agent 2
[0056] This formula is medium-speed drying formula, suitable for medium-speed printing process. Its preparation method is the same as above.
Embodiment 3
[0057] Implementation 3: A mirror plastic printing ink for OPS heat shrinkable film, the raw materials in its components are respectively:
[0058] Raw material name Mass ratio
[0059] 1. Ethanol 15
[0060] 2. Isopropanol 30
[0061] 3. n-Propyl acetate 8
[0062] 4. Propylene glycol methyl ether 5
[0063] 5. PVB (polyvinyl butyral) resin 11
[0064] 6. Acrylic 3
[0065] 7. Ultrafine flaky aluminum silver paste 25
[0066] 8. Styling agent 1.5
[0067] 9. Silicone leveling agent 1.5
[0068] This formula is low-speed drying formula, suitable for low-speed printing process. Its preparation method is the same as above.
[0069] In the present invention, by controlling the environmental protection performance of the ink, and then matching the non-toxic and environmentally friendly OPS heat shrinkable film, the new body-fitting packaging material that fully meets the environmental protection requirements, is safe, non-toxic, and recyclable is finally produced; ...
PUM
Property | Measurement | Unit |
---|---|---|
shrinkage | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com