Composite combined filament yarn and method for producing combined filament yarn for spinning by utilizing composite filament yarn

A technology of blending and spinning, applied in the field of composite blended yarn, can solve the problems of unstable quality and low production speed, and achieve the effects of stable product quality, improved quality and reduced spinning cost

Inactive Publication Date: 2012-10-03
张家港保税区长江塑化有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It adopts different stretching process conditions for two bundles of filaments, and winds them at the same time at the end, which will inevitably lead to unstable quality and low production speed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite combined filament yarn and method for producing combined filament yarn for spinning by utilizing composite filament yarn

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] (1) Be that 60% weight part bio-based PTT material (polytrimethylene terephthalate material 1) slice is a raw material with consumption, enter material continuous drying tower, make the PTT material dry slice of moisture content<30ppm, pass through the first The melt extrusion of the first screw extruder becomes the melt A of the spinnable PTT material. The melt extrusion process of the first screw extruder is equipped with 3 to 5 heating zones, and the heating temperature of each zone is 245°C, 250°C, 253°C, 255°C, 255°C (five-zone screw), and the PTT material melt A is delivered to the spinning box (the PTT material melt A passes through between the first screw extruder and the spinning box) The pre-filter removes the large particle impurities in the PTT material melt A), and further evenly distributes it to the 8-shaped composite spinning pack, which is the first component.

[0014] (2) The PA6 material (polyamide 6 material 2) chip is the second raw material B with ...

Embodiment 2

[0017] (1) Be that 70% weight part bio-based PTT material (polytrimethylene terephthalate material 1) slice is a raw material with consumption, enter material continuous drying tower, make the PTT material dry slice of moisture content<30ppm, pass through the first The melt extrusion of the first screw extruder becomes the melt A of the spinnable PTT material. The melt extrusion process of the first screw extruder is equipped with 3 to 5 heating zones, and the heating temperature of each zone is 245°C, 250°C, 253°C, 255°C, 255°C (five-zone screw), and the PTT material melt A is delivered to the spinning box (the PTT material melt A passes through between the first screw extruder and the spinning box) The pre-filter removes the large particle impurities in the PTT material melt A), and further evenly distributes it to the 8-shaped composite spinning pack, which is the first component.

[0018] (2) The PA6 material (polyamide 6 material 2) chips in an amount of 30% by weight are...

Embodiment 3

[0021] (1) Be that 90% weight part bio-based PTT material (polytrimethylene terephthalate material 1) slice is a raw material with consumption, enter material continuous drying tower, make the PTT material dry slice of moisture content<30ppm, pass through the first The melt extrusion of the first screw extruder becomes the melt A of the spinnable PTT material. The melt extrusion process of the first screw extruder is equipped with 3 to 5 heating zones, and the heating temperature of each zone is 245°C, 250°C, 253°C, 255°C, 255°C (five-zone screw), and the PTT material melt A is delivered to the spinning box (the PTT material melt A passes through between the first screw extruder and the spinning box) The pre-filter removes the large particle impurities in the PTT material melt A), and further evenly distributes it to the 8-shaped composite spinning pack, which is the first component.

[0022] (2) The PA6 material (polyamide 6 material 2) chip is the second raw material B with ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method with steady production process for producing a composite combined filament yarn with steady quality. The method comprises the steps of: fusing dry slices of a PTT (Polytrimethylene Terephthalate) material accounting for 60%-90% of the total weight to form a spinning PTT material melt; fusing dry slices of a PA6 (polyamide 6) material accounting for10%-40% of the total weight to form a spinning PA6 material melt; extruding the PTT material melt and the PA6 material melt after passing through respective spinning melt channels by an eight-shaped spinning component; then cooling, oiling and forming the composite combined filament yarn after the melt passes through a spinning channel, a pre-networking device and a hot roller drawing device; then enabling the composite combined filament yarn to pass through an NaOH solution with a percentage by weight of 0.5-10% in a boiling water state; and thereby separating the composite combined filament yarn into the combined filament yarns for spinning. According to the composite combined filament yarn and the method for producing the combined filament yarn for spinning by utilizing the composite combined filament yarn, disclosed by the invention, the production process of the combined filament yarn is simplified, and output and quality of the combined filament yarn are improved greatly.

Description

technical field [0001] The invention relates to a compound mixed fiber yarn and a method for manufacturing the mixed fiber yarn for textile by using the composite mixed fiber yarn. Background technique [0002] For example, the patent specification of application number: 200510039169.9 discloses a polyester-based mixed fiber yarn, which is ejected from cationic dyeable polyester and polyethylene terephthalate through different spinneret holes of the same spinneret. coiled. It must be affected by the different drawing and processing properties of two groups of separate fibers during spinning, and the production in the spinning process is unstable and the production speed is low. [0003] For example, the patent No.: 00803097.9 discloses a method for manufacturing polyester-based mixed fiber yarns. After the same polymer is extruded in the same component, the tow is divided into two strands, and one of the tows is in the fiber-opened state. And carry out non-contact heat tre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92
Inventor 张辉陆燕祥
Owner 张家港保税区长江塑化有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap