A kind of ammonia storage active mixture and preparation

A technology of active mixture and mixture, which is applied in the field of ammonia storage active mixture and preparation, can solve the problems that technicians cannot implement and do not have clear claim details, etc., and achieve the effects of avoiding agglomeration, improving richness, and increasing transmission channels

Active Publication Date: 2016-03-09
CHINA FIRST AUTOMOBILE
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent uses solid material for direct compression molding, uses binder, only declares that it may be silica fiber binder, and does not add the proportion, and other claims and examples only state that the solid material may include Composition of granular materials, porous materials, crystalline materials, amorphous materials or their combinations, without clear claim details, it is almost impossible for those skilled in the industry to implement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ammonia storage active mixture and preparation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Mix 71 parts of magnesium chloride, 3 parts of carbon fiber, 6 parts of silica sol and 12 parts of water in a high-speed mixer for 1 hour, add 8 parts of ethanol, and continue to stir mechanically for 3 hours to make a uniform mixture of wet materials and fill them into the tank , added to 80% of the tank volume, and mechanically shaken for 10 minutes to eliminate the air gap;

[0027] The whole tank is put into a vacuum oven, such as figure 1 Under the normal pressure shown, increase the temperature to 120°C at a rate of 2°C / min, keep the temperature for 6 hours, remove water and ethanol, evacuate step by step to 550mbar, keep the temperature and pressure for 1h, take out the tank, seal the feeding port, and make ammonia storage The active mixture is a monolithic porous solid block.

Embodiment 2

[0029] Mix 2 parts of carbon fiber, 18 parts of silica sol, and 15 parts of water in a high-speed mixer for 1 hour, add 58 parts of magnesium chloride and mix for 1 hour, add 10 parts of ethanol, and continue to stir mechanically for 3 hours to make a uniform mixture. In the tank, add to 75% of the tank volume, and mechanically shake for 10 minutes to eliminate the air gap;

[0030] Put the whole tank into a vacuum oven, raise the temperature to 120 °C at a rate of 2 °C / min under normal pressure, keep the temperature for 6 hours, remove water and ethanol, evacuate step by step to 550 mbar, keep the temperature and pressure for 1 hour, take out the tank, The feeding port is sealed to form an integral porous solid block of the ammonia storage active mixture.

Embodiment 3

[0032] Mix 5 parts of silica sol and 6 parts of water in a high-speed mixer for 1 hour, add 80 parts of magnesium chloride and mix for 1 hour, add 3 parts of carbon fiber and mix for 1 hour, add 6 parts of ethanol, and continue mechanical stirring for 3 hours to make a uniform mixture wet material , filled into the tank, added to 80% of the volume of the tank, and mechanically shaken for 10 minutes to eliminate the air gap;

[0033] Put the whole tank into a vacuum oven, raise the temperature to 100 °C at a rate of 5 °C / min under normal pressure, keep the temperature constant for 8 hours, remove water and ethanol, evacuate step by step to 550 mbar, keep the constant temperature and pressure for 2 hours, take out the tank, The feeding port is sealed to form an integral porous solid block of the ammonia storage active mixture.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to an ammonia storage mixture and its preparation, which is characterized in that: industrial anhydrous magnesium chloride salt powder is used, mixed with an appropriate amount of silica sol, carbon fiber, deionized water and industrial alcohol, and mechanically stirred to make it semi-dry Mix the wet material evenly, fill it into the tank body, and make a whole porous solid block. The ammonia gas transmission channels in the solid block are rich, and there are several large pores in the macroscopic view, which has faster ammonia filling and better ammonia storage performance. It can release ammonia gas quickly, can be recycled without breaking, has high-efficiency adsorption and desorption characteristics, is suitable for the adsorption and storage of ammonia gas, and is used in SCR and FCEV systems to meet the application requirements of the future automotive industry.

Description

technical field [0001] The invention relates to an ammonia storage active mixture and its preparation, which is applied to the SCR post-treatment system of automobile tail gas and the FCEV fuel cell system. Background technique [0002] At present, the world is facing comprehensive challenges of energy and environment. People are still facing many difficulties in the selection of technical means to meet the emission standards of traditional vehicles, and in the fuel supply technology of new energy vehicles. [0003] The SCR post-treatment system relies on the accurate supply of urea reducing agent and decomposes it into ammonia gas at the front end of the catalyst to remove NOX hazards, so as to purify the exhaust gas and achieve the vehicle's National 4 or above standards. However, in actual use Among them, there are many deficiencies and difficulties in the metered injection of liquid urea that relies on urea decomposed into ammonia gas. For example, the problem of urea s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01C1/00H01M8/06B01J20/18B01J20/30B01D53/56B01D53/76H01M8/0662
CPCY02E60/50
Inventor 张克金崔龙荣常如米新艳张苡铭张喆魏晓川刘国军
Owner CHINA FIRST AUTOMOBILE