Reinforcing yarn size for glass fibers and preparation method thereof

A glass fiber and sizing technology, applied in the field of sizing and its preparation, reinforced textile glass fiber sizing and its preparation, can solve problems such as high bending, high folding resistance, high friction, and poor textile performance, and achieve Reduce the coefficient of friction, fast soaking, strong bonding effect

Active Publication Date: 2012-10-24
SICHUAN FIBERGLASS GRP
View PDF7 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The sizing involved in this formula is used in the drawing production of polyurethane plastic-coated yarns, and its reinforcing effect is obvious, but its textile perf

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0053] A kind of reinforced textile glass fiber sizing, comprising the following components by weight percentage:

[0054] Film former emulsion 4.0%

[0055] Lubricant 1.7%

[0056] Water-soluble epoxy resin binder 0.5%

[0057] Inorganic antistatic agent 0.2%

[0058] Aminosilane coupling agent 0.5%

[0059] Demineralized water balance;

[0060] Described film-forming agent emulsion comprises following components:

[0061] PEG-4000, boron trifluoride ether, epoxy resin E-44, epoxy resin E-20 and water, the ratio is 1:0.005:1:0.8:8.

Embodiment 2

[0063] A kind of reinforced textile glass fiber sizing, comprising the following components by weight percentage:

[0064] Film former emulsion 5.5%

[0065] Lubricant 4%

[0066] Water-soluble epoxy resin binder 1.5%

[0067] Inorganic antistatic agent 1.0%

[0068] Aminosilane coupling agent 1.5%

[0069] Demineralized water balance;

[0070] Described film-forming agent emulsion comprises following components:

[0071] PEG-4000, boron trifluoride ether, epoxy resin E-44, epoxy resin E-20 and water, the ratio is 2:0.01:1.5:1.2:10.

Embodiment 3

[0073] A kind of reinforced textile glass fiber sizing, comprising the following components by weight percentage:

[0074] Film former emulsion 4.75%

[0075] Lubricant 2.85%

[0076] Water-soluble epoxy resin binder 1.0%

[0077] Inorganic antistatic agent 0.6%

[0078] Aminosilane coupling agent 1.0%

[0079] Demineralized water balance;

[0080] Described film-forming agent emulsion comprises following components:

[0081] PEG-4000, boron trifluoride ether, epoxy resin E-44, epoxy resin E-20 and water, the ratio is 1.5:0.0075:1.25:1.0:9.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a reinforcing yarn size for glass fibers and a preparation method thereof, and belongs to the technical field of sizes for glass fibers. The size comprises 4.0-5.5% of a filmogen emulsion, 1.7-4% of a lubricating agent, 0.5-1.5% of a water soluble epoxy resin binder, 0.2-1.0% of an inorganic antistatic agent, 0.5-1.5% of an aminosilane coupling agent and the balance softened water. The filmogen emulsion comprises polyethylene glycol-4000 (PEG-4000), boron trifluoride diethyl etherate, epoxy resin E-44, epoxy resin E-20 and water with a ratio of (1-2): (0.005-0.01): (1-1.5): (0.8-1.2): (8-10). Glass fibers drawn through the size can bear repeatedly bending deformation and have a good textile performance, and woven glass fiber cloth can be applied to production of composite materials without heat treatment and is quick in soakage and high in binding force when compounded with matrix resin.

Description

technical field [0001] The invention relates to a sizing agent and a preparation method thereof. More specifically, the invention relates to a textile-reinforced glass fiber sizing agent and a preparation method thereof, belonging to the technical field of glass fiber sizing agents. Background technique [0002] The sizing agent can not only effectively lubricate the glass fiber surface, but also integrate hundreds or even thousands of glass fiber monofilaments into a bundle, and can also change the surface state of the glass fiber, which not only satisfies the processing performance of the glass fiber precursor in the subsequent process requirements, and it can also promote the combination of glass fiber and reinforced polymer in composite materials. [0003] All countries attach great importance to the research and development of sizing agents, and invest a lot of manpower and financial resources in the research and development of new sizing agents with better performance....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C25/36
Inventor 李军叶书祥唐昌万李曹郭炯
Owner SICHUAN FIBERGLASS GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap