Method for preparing alkali-resistant glass fibre jet yarn impregnating compound

A technology of alkali-resistant glass fiber and jet yarn, which is applied in the field of preparation of glass fiber surface treatment agents, can solve the problems of poor bundling, low stiffness, and easy hairiness of the sizing, and achieve good bundling and good chopping properties Effect

Active Publication Date: 2013-12-11
陕西汇友友基新材料有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] (1) The sizing protective layer coated on the surface of the glass fiber has poor textile resistance and is prone to hairiness when unwinding and plying;
[0011] (2) The sizing agent coated on the surface of the glass fiber has poor clustering property, the bonding between the fibers is not strong, and it is easy to open the fibers when spraying under pressure, which affects the uniformity of dispersion;
[0012] (3) The stiffness is low, which affects the short-cut dispersion of fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) Add 1 kg of 80-90°C deionized water to 0.1 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir until a uniform transparent liquid;

[0043] (2) Add 0.1 kg of 30-50°C deionized water to 0.05 kg of antistatic agent SN, and stir until a uniform transparent liquid;

[0044] (3) Add 3 kilograms of 50-70 ℃ deionized water to 0.1 kilogram of lithium nitrate and 1 kilogram of lithium nitrate lithium chloride mixture, stir until a uniform transparent liquid;

[0045] (4) Add 6 kilograms of deionized water to 3.0 kilograms of modified polyacrylate film-forming agent YG11l (produced by Xi'an Youji Composite Material Co., Ltd.);

[0046] Add 4 kilograms of deionized water to 4.0 kilograms of water-soluble epoxy film-forming agent YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.);

[0047] Add 8 kilograms of deionized water to 4.0 kilograms of polyvinyl acetate and acrylate copolymer film-forming agent ...

Embodiment 2

[0052] (1) Add 3.0 kg of 80-90°C deionized water to 0.3 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir until a uniform transparent liquid;

[0053] (2) Add 1.5 kg of 30-50°C deionized water to 0.15 kg of antistatic agent SN, and stir until a uniform transparent liquid;

[0054] (3) Add 4.5 kilograms of 50-70 DEG C deionized water to the mixture of 0.1 kilogram of lithium nitrate, 0.1 kilogram of lithium chloride and 0.1 kilogram of ammonium chloride, and stir until a uniform transparent liquid;

[0055] (4) Add 13.5 kilograms of deionized water to 4.5 kilograms of modified polyacrylate film-forming agent YG11l (produced by Xi'an Youji Composite Material Co., Ltd.);

[0056] Add 8.0 kilograms of deionized water to 4.0 kilograms of water-soluble epoxy film-forming agent YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.);

[0057] Add 11.0 kilograms of deionized water to 5.5 kilograms of polyvinyl ac...

Embodiment 3

[0062](1) Add 4.0 kg of 80-90°C deionized water to 0.4 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir until a uniform transparent liquid;

[0063] (2) Add 2.5 kg of 30-50°C deionized water to 0.25 kg of antistatic agent SN, and stir until a uniform transparent liquid;

[0064] (3) Add 4.5 kg of 50-70°C deionized water to 0.25 kg of lithium nitrate, 0.1 kg of lithium chloride and 0.1 kg of ammonium chloride, and stir until a uniform transparent liquid;

[0065] (4) Add 14.0 kilograms of deionized water to 7.0 kilograms of modified polyacrylate film-forming agent YG11l (produced by Xi'an Youji Composite Materials Co., Ltd.);

[0066] Add 10.0 kilograms of deionized water to 5.0 kilograms of water-soluble epoxy film-forming agent YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.);

[0067] Add 14.0 kg of deionized water to 7.0 kg of polyvinyl acetate and acrylate copolymer film-forming agent YG2016 (...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for preparing an alkali-resistant glass fibre jet yarn impregnating compound. The method comprises the following steps: adding 10-20 times deionized water with temperature of 80-90 DEG C to imidazoline cation lubricant and stirring to obtain uniform and transparent liquid; adding 5-10 times deionized water with temperature of 30-50 DEG C to an antistatic agent SN and stirring to obtain uniform and transparent liquid; adding 10-20 times deionized water with temperature of 50-70 DEG C to one or mixture of lithium nitrate, lithium chloride and ammonium chloride and stirring to obtain uniform and transparent liquid; respectively adding 1-3 times deionized water to a polyacrylate film-forming agent, a water-soluble epoxy film-forming agent, polyvinyl acetate and an acrylate copolymer film-forming agent; and mixing all matters obtained in the previous steps, then adding the rest of deionized water, and stirring for 30-40 minutes at the stirring speed of 50-60rpm.

Description

technical field [0001] The invention relates to a preparation method of a glass fiber surface treatment agent containing organic materials. Background technique [0002] Alkali-resistant glass fiber jet yarn is mainly used to strengthen cement products (referred to as GRC). The processing technology is that glass balls containing ZrO2 (13%-16%) flow out from the orifice at the bottom of the crucible after being melted in the crucible. After drawing and coating with sizing agent, it is rolled into a raw silk tube, then dried at 120-160 ° C, unwound and plied into continuous fibers. The fiber is chopped and dispersed on the abrasive tool by spray gun under certain air pressure. Therefore, when producing continuous fibers, it is necessary to use a sizing agent with excellent performance to ensure the bundling, stiffness, and lubricity of the glass fibers in unwinding and plying, and at the same time ensure the chopping and dispersibility of the fibers in the jetting. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/42
Inventor 任川荣张棋任二室
Owner 陕西汇友友基新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap