Process for antistatic and antibacterial polyamide 6DTY high elastic filament

A polyamide, high elastic yarn technology, applied in the field of spinning materials, can solve the problems of rough hand, poor softness, easy to pilling, etc., and achieve good antibacterial and antistatic effects.

Inactive Publication Date: 2012-11-07
WUJIANG YATAI CHEM TEXTILE
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, fabrics are generally used, because of their thick fibers, rough hand feeling, poor softness, poor air permeability, poor water absorption, and easy to fluff and pilling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The DTY high elastic yarn is prepared by using the POY-DTY process with polyamide 6 chips and additives as raw materials, wherein in the POY-DTY process, the POY process route is: screw extruder→prefilter→static mixer →metering pump→spinning assembly→spinning→side blowing and oiling→corridor→POY winding yarn; among them: melt spinning temperature: 270-278℃; side blowing conditions: wind speed is 0.2-0.5 m / s, wind temperature 25-30 ℃, relative humidity 60-75%; oiling rate 0.70-1.50%; spinning speed 3500-4500 m / min; DTY production process route: yarn guide→feeding roller→first Hot box→cooling plate→false twister→output roller→oiling device→DTY winding wire; wherein, the temperature of the first hot box is 140-175 ℃, the D / Y ratio is 1.2-1.8, and the drafting ratio is 1.20-1.30. Based on the weight of the polyamide 6 slices, the additives include 0.35wt% sodium methacrylate, 0.12wt% lithium bromide, 0.4wt% dibutyltin laurate, 0.20wt% silver-loaded dioxide Silica gel, 1.2...

Embodiment 2

[0017] The DTY high elastic yarn is prepared by using the POY-DTY process with polyamide 6 chips and additives as raw materials, wherein in the POY-DTY process, the POY process route is: screw extruder→prefilter→static mixer →metering pump→spinning assembly→spinning→side blowing and oiling→corridor→POY winding yarn; among them: melt spinning temperature: 270-278℃; side blowing conditions: wind speed is 0.2-0.5 m / s, wind temperature 25-30 ℃, relative humidity 60-75%; oiling rate 0.70-1.50%; spinning speed 3500-4500 m / min; DTY production process route: yarn guide→feeding roller→first Hot box→cooling plate→false twister→output roller→oiling device→DTY winding wire; wherein, the temperature of the first hot box is 140-175 ℃, the D / Y ratio is 1.2-1.8, and the drafting ratio is 1.20-1.30. Based on the weight of the polyamide 6 slices, the additives include 0.72wt% sodium methacrylate, 0.25wt% lithium bromide, 0.8wt% dibutyltin laurate, 0.25wt% silver-loaded dioxide Silica gel, 1.8...

Embodiment 3

[0019] The DTY high elastic yarn is prepared by using the POY-DTY process with polyamide 6 chips and additives as raw materials, wherein in the POY-DTY process, the POY process route is: screw extruder→prefilter→static mixer →metering pump→spinning assembly→spinning→side blowing and oiling→corridor→POY winding yarn; among them: melt spinning temperature: 270-278℃; side blowing conditions: wind speed is 0.2-0.5 m / s, wind temperature 25-30 ℃, relative humidity 60-75%; oiling rate 0.70-1.50%; spinning speed 3500-4500 m / min; DTY production process route: yarn guide→feeding roller→first Hot box→cooling plate→false twister→output roller→oiling device→DTY winding wire; wherein, the temperature of the first hot box is 140-175 ℃, the D / Y ratio is 1.2-1.8, and the drafting ratio is 1.20-1.30. Based on the weight of the polyamide 6 slices, the additives include 0.5wt% sodium methacrylate, 0.2wt% lithium bromide, 0.6wt% dibutyltin laurate, 0.23wt% silver-loaded dioxide Silica gel, 1.5wt...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a process for an antistatic and antibacterial polyamide 6DTY high elastic filament, which is prepared from raw materials comprising polyamide 6 chips and additives by a POY-DTY process on high-speed spinning equipment. The prepared DTY high elastic filament has antistatic and antibacterial function and good stability, and can meet different requirements of post-weaving finishing.

Description

technical field [0001] The invention belongs to the field of spinning materials, and in particular relates to a DTY high elastic yarn process for producing polyamide 6 by slicing. Background technique [0002] At present, synthetic fibers generally include polyester (polyester), nylon (polyamide), polypropylene (polypropylene), spandex (polyurethane), acrylic (polyacrylonitrile) and the like. These fibers have different properties and thus different uses. But at present generally take fabric, because its fiber is thicker, feel rough, softness is poor, air permeability is poor, water absorption is poor, easy to pilling. With the improvement of people's living standards, the requirements for textiles are getting higher and higher. [0003] Polyamide fiber is the earliest synthetic fiber variety put into industrial production in the world. It is made of polyamide synthesized by polycondensation reaction of aliphatic dibasic acid and diamine or aliphatic amino acid, and then ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/90D01F1/09D01F1/10D01D5/092D01D5/096D01D10/02
Inventor 赵广兵
Owner WUJIANG YATAI CHEM TEXTILE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com