Environment-friendly acrylate grouting material as well as preparation method and application thereof

A technology of acrylate and grouting materials, applied in the field of grouting materials, can solve the problems of low water expansion rate, poor durability, poor water solubility, etc., and achieve the problem of material strength, good hydrolysis resistance and aging resistance performance, improve the effect of crushing strength

Inactive Publication Date: 2014-12-03
湖南博旺水电建设有限公司
View PDF6 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide an environment-friendly acrylate grouting material and its preparation method and application, so as to solve the problem that existing organic grouting materials cannot be mixed with inorganic grouting materials for grouting, and the existing grouting materials have insufficient durability. Good, low strength, poor water solubility, low water expansion rate, high toxicity technical problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An environment-friendly acrylic grouting material is composed of the following components according to the mass ratio:

[0036] Main agent: 100 parts of β-hydroxyethyl methacrylate;

[0037] Crosslinking agent: 30 parts of polyethylene glycol diallyl ether;

[0038] Initiator: 2 parts of ammonium persulfate;

[0039] Accelerator: 1 part of triethanolamine;

[0040] Solvent: 130 parts of water.

[0041] Mix β-hydroxyethyl methacrylate, polyethylene glycol diallyl ether, and triethanolamine uniformly to form liquid A; then mix ammonium persulfate and water to form liquid B, and use liquid A and liquid B are mixed to form an environmentally friendly acrylic grouting slurry, which is finally cross-linked and solidified.

[0042] The average molecular weight of polyethylene glycol in polyethylene glycol diallyl ether is 160.

[0043] The physical properties of the slurry are as follows:

[0044]1) Appearance of slurry: colorless or light yellow transparent homogeneous ...

Embodiment 2

[0054] An environment-friendly acrylic grouting material is composed of the following components according to the mass ratio:

[0055] Main agent: 100 parts of β-hydroxyethyl methacrylate;

[0056] Crosslinking agent: 10 parts of polyethylene glycol diallyl ether;

[0057] 4 parts of ethoxylated bisphenol A diallyl ether;

[0058] Initiator: 3 parts of potassium persulfate;

[0059] Accelerator: 0.5 parts of sodium thiosulfate;

[0060] Auxiliary: 15 parts of sodium acrylate

[0061] Additive: Potassium ferricyanide 0.02 parts

[0062] Solvent: 25 parts of water.

[0063] Wherein, the average molecular weight of polyethylene glycol in the polyethylene glycol diallyl ether is 480, and the number of ethoxylated functional groups in the ethoxylated bisphenol A diallyl ether is 8.

[0064] After mixing β-hydroxyethyl methacrylate, polyethylene glycol diallyl ether, ethoxylated bisphenol A diallyl ether, sodium thiosulfate, water, sodium acrylate, and potassium ferricyanide, ...

Embodiment 3

[0076] An environment-friendly acrylic grouting material is composed of the following components according to the mass ratio:

[0077] Main ingredient: 100 parts of β-hydroxyethyl methacrylate;

[0078] Crosslinking agent: 20 parts of polyethylene glycol diallyl ether;

[0079] 4 parts of ethoxylated bisphenol A diallyl ether;

[0080] Initiator: 2 parts of potassium persulfate and ammonium persulfate;

[0081] Accelerator: 0.9 parts of sodium thiosulfate and sodium bicarbonate;

[0082] Solvent: 200 parts of water.

[0083] The average molecular weight of polyethylene glycol in the polyethylene glycol diallyl ether is 1600, and the number of ethoxylated functional groups in the ethoxylated bisphenol A diallyl ether is 12.

[0084] Mix homogeneously β-hydroxyethyl methacrylate, polyethylene glycol diallyl ether, ethoxylated bisphenol A diallyl ether, sodium thiosulfate, sodium bicarbonate, and water to form liquid A; Then potassium persulfate, ammonium persulfate and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
osmotic coefficientaaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly acrylate grouting material, as well as a preparation method and an application thereof. The material mainly comprises the following components in parts by weight: a main agent, namely 100 parts of methacrylic acid-beta-hydroxyethyl ester, a crosslinking agent which includes 5-30 parts of hydrophilic compound containing a diallyl ether functional group, 1-5 parts of initiator and 0.5-3 parts of accelerant, 0-20 parts of an adjuvant, and a solvent, namely 2-1,000 parts of water. The method comprises the following steps: firstly, mixing the main agent, the crosslinking agent, the accelerant, the adjuvant and a part of solvent evenly to form a solution A in use; then dissolving the initiator into a residual solvent to form a solution B; and finally mixing the solution A with the solution B evenly, and solidifying at room temperature. According to the grouting material disclosed by the invention, the technical problem that the existing organic grouting material cannot be grouted once after being mixed with an inorganic grouting material, and the technical problem that the existing grouting material has poor durability, low strength, poor water solubility, low water expansion rate and high toxicity are solved.

Description

technical field [0001] The invention relates to a grouting material for seepage prevention and plugging in geotechnical engineering, in particular to an environmentally friendly acrylic grouting material suitable for seepage prevention and reinforcement of foundation treatment engineering, water stop and reinforcement of deformation joint leakage and Its preparation method and application. Background technique [0002] In the anti-seepage and reinforcement treatment of foundation treatment engineering, acrylate grouting materials and modified epoxy resin grouting materials are often used as grouting materials for anti-seepage and reinforcement treatment. However, the price of organic grouting materials is relatively high, resulting in high construction costs. For this reason, the construction unit hopes to mix organic grouting materials and conventional inorganic grouting materials such as cement slurry, clay cement slurry, bentonite cement slurry, etc. for grouting, and us...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F283/06C08F220/28C08F216/12C08F2/10C08F4/40C04B28/00
Inventor 宾斌彭春雷贺茉莉王雪龙周林丁剑波舒友良刘军
Owner 湖南博旺水电建设有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com