Template integrated thermal insulation board and its processing method

A technology of thermal insulation board and formwork, applied in the field of building supplies, can solve the problems of cumbersome construction process, poor thermal insulation performance, unable to meet actual requirements, etc., and achieve the effect of simplifying construction steps and ensuring thermal insulation performance.

Active Publication Date: 2012-11-28
QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The integrated thermal insulation boards in the prior art mostly use foamed cement, or the simple compound of foamed cement and rock wool board, which has poor thermal insulation performance and cannot meet the actual requirements. At the same time, the construction process is cumbersome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A method for processing a formwork integrated insulation board, comprising the following steps

[0018] (1) Weigh each component in the following parts by weight

[0019] 65 parts of gypsum, 0.01 part of fiber, 0.5 part of organic adhesive material, 5 parts of inorganic powder,

[0020] The fiber is a mixture of polypropylene fiber and straw fiber in any proportion, the length of the polypropylene fiber and straw fiber is 3mm, and the diameter is 3μm, and the organic bonding material is redispersible polymer Material glue powder, described inorganic powder is the mixture that ash calcium, heavy calcium and fly ash are formed according to any proportion, after weighing each raw material component, fully mix, obtain mixture;

[0021] (2) Fully mix the mixture obtained in step (1) with water according to the ratio of 1::1, and fully stir until the mixture is evenly mixed. The required time is 10 minutes, and the mixture slurry is obtained for use; then use a foaming machi...

Embodiment 2

[0025] A method for processing a formwork integrated insulation board, comprising the following steps

[0026] (1) Weigh each component in the following parts by weight

[0027] 80 parts of gypsum, 0.8 parts of fiber, 0.8 parts of organic bonding material, 12 parts of inorganic powder,

[0028] The fiber is a polypropylene fiber with a length of 4 mm and a diameter of 6 μm, the organic bonding material is a redispersible polymer rubber powder, and the inorganic powder is composed of ash calcium and heavy calcium in any proportion After weighing each raw material component, fully mix to obtain the mixture;

[0029] (2) Fully mix the mixture obtained in step (1) with water according to the ratio of 1::1, and fully stir until the mixture is evenly mixed. The required time is 10 minutes, and the mixture slurry is obtained for use; then use a foaming machine to Water is used for foaming, wherein water and foaming agent are mixed in a ratio of 1:25, foamed under a pressure of 0.2M...

Embodiment 3

[0032] A method for processing a formwork integrated insulation board, comprising the following steps

[0033] (1) Weigh each component in the following parts by weight

[0034] 90 parts of gypsum, 1 part of fiber, 3 parts of organic bonding material, 20 parts of inorganic powder,

[0035] The fiber is straw fiber with a length of 5 mm and a diameter of 7 μm, the organic bonding material is redispersible polymer rubber powder, the inorganic powder is fly ash, and the raw material components are weighed After that, mix thoroughly to obtain a mixture;

[0036] (2) Fully mix the mixture obtained in step (1) with water according to the ratio of 1::1, and fully stir until the mixture is evenly mixed. The required time is 10 minutes, and the mixture slurry is obtained for use; then use a foaming machine to Water is used for foaming, wherein water and foaming agent are mixed in a ratio of 1:25, foamed under a pressure of 0.2Mpa, and the foamed liquid is mixed with a spare mixture s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a template integrated thermal insulation board and its processing method. The board comprises the following components by weight: 65-90 parts of gypsum, 0.01-1 part of a fiber, 0.5-3 parts of an organic bonding material, and 5-20 parts of inorganic powder. The board is processed by subjecting the components to mixing, foaming and other processes. The template integrated thermal insulation board provided in the invention has the advantages of: ensuring the thermal insulation performance of the integrated board, and simplifying the construction procedure during construction, thus meeting the actual demands.

Description

technical field [0001] The invention relates to a template-integrated thermal insulation board and a processing method thereof, belonging to the field of building supplies. Background technique [0002] The integrated thermal insulation boards in the prior art mostly use foamed cement, or a simple composite of foamed cement and rock wool boards, which has poor thermal insulation performance and cannot meet actual requirements, and the construction process is cumbersome. Contents of the invention [0003] In order to overcome the defects of the prior art, the invention provides a polystyrene particle vacuum insulation board and a processing method thereof. Technical scheme of the present invention is: [0004] A template-integrated thermal insulation board is characterized in that it comprises the following components in parts by weight: 65-90 parts of gypsum, 0.01-1 part of fiber, 0.5-3 parts of organic bonding material, and 5-20 parts of inorganic powder. [0005] T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/14
Inventor 翟传伟李壮贤
Owner QINGDAO CREEK NEW ENVIRONMENTAL PROTECTION MATERIAL
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com