Alkali-containing glass fiber direct roving sizing agent for spinning

A technology of alkali glass fiber and sizing, which is applied in the formulation of sizing, can solve the problems of generally low quality, complex production process, and low breaking strength, and achieve the effects of less hairiness, high breaking strength and improved performance

Inactive Publication Date: 2012-12-05
江西大华新材料股份有限公司
View PDF6 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, my country's medium-alkali glass fiber is developing rapidly, but the general quality is not high, especially in the process of processing huge direct yarn of medium-alkali glass fiber for textile. The strength is relatively low, and the production process is relatively complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] This specific embodiment adopts the following technical scheme: its formula consists of: coupling agent, lubricant A, lubricant B, epoxy resin emulsion, modified polyester resin emulsion, auxiliary film-forming agent, special additive, antistatic agent and deionized water.

[0017] The solid mass of the wetting agent accounts for 15% of the total mass of the wetting agent, and the balance is deionized water, which accounts for 85% of the total mass of the wetting agent.

[0018] The coupling agent is a vinyl silane coupling agent, an amino silane coupling agent, and an epoxy silane coupling agent, accounting for 2.0% of the solid mass of the wetting agent.

[0019] The lubricant A is a nonionic surfactant, which is one of polyoxyethylene ethers, esters, amides, and chemically modified mineral oils, accounting for 20% of the solid mass of the wetting agent.

[0020] The lubricant B is a cationic surfactant, one of polyoxyethylene ammonium salt, quaternary ammonium salt,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an alkali-containing glass fiber direct roving sizing agent for spinning, and relates to a formula of a sizing agent. The formula consists of a coupling agent, a lubricant A, a lubricant B, epoxy resin emulsion, modified polyester resin emulsion, an auxiliary filmogen, a special additive, an antistatic agent and deionized water. By the sizing agent, the performance of alkali-containing glass fiber direct roving can be improved, a small quantity of feathers are generated in weaving, the breaking tenacity of the direct roving is high, and the production performance and application performance are high.

Description

Technical field: [0001] The invention relates to a formulation of a sizing agent, in particular to a direct yarn sizing agent for medium-alkali glass fiber used in textiles. Background technique: [0002] At present, my country's medium-alkali glass fiber is developing rapidly, but the general quality is not high, especially in the process of processing huge direct yarn of medium-alkali glass fiber for textile. The strength is relatively low, and the production process is relatively complicated. Invention content: [0003] The purpose of this invention is to provide a kind of medium-alkali glass fiber direct yarn sizing agent for textile, which can improve the performance of medium-alkali glass fiber direct roving, the amount of hairiness produced by weaving is relatively small, and the breaking strength of direct roving is relatively high , with good production performance and application performance. [0004] In order to solve the existing problems of the background tec...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/40
Inventor 张晓曜张昭
Owner 江西大华新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com