Moisture-curing epoxy zinc phosphate over-rust primer

A technology of epoxy zinc phosphate and rust primer, which is applied in the direction of epoxy resin coating, coating, anti-corrosion coating, etc., to achieve the effect of improving anti-rust performance, good film-forming property, and fine particles

Active Publication Date: 2013-01-30
江苏纽克莱涂料有限公司
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the rainy and humid seasons and coastal areas with alternating dry and wet, the relative humidity of the air is above 80%, which provides conditions for the action of oxygen and water. The corrosion of metal substrates is obviously intensified, and the curing rate of coatings is slower than that of substrates. Speed, the water film is easy to form between the coating and the surface of the substrate, which affects the adhesion of the substrate, and the cross-linking density of the coating film decreases, which affects the service life and anti-corrosion effect of the coating.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moisture-curing epoxy zinc phosphate over-rust primer
  • Moisture-curing epoxy zinc phosphate over-rust primer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The specific implementation of the present invention will be described below in conjunction with the examples.

[0033] See Table 1 for the components and contents of the moisture-curing epoxy zinc phosphate rust primer in Examples 1 to 4.

[0034] Table 1

[0035]

[0036] The preparation technology of moisture curing epoxy zinc phosphate band rust primer in embodiment 1~embodiment 4 is as follows:

[0037] Weigh the components contained in component A as shown in Table 1, first put epoxy resin E44, cyclohexanone, and n-butanol into the mixer in sequence, stir at 800~1000 rpm for 10 minutes, and then add 209 zinc chrome yellow , 309 zinc chrome yellow, 109 zinc chrome yellow, iron oxide red, zinc phosphate, aluminum tripolyphosphate, and diphenylguanidine chromate were put into the mixer, stirred at 1000~1800 rpm for 30 min, put into the grinder and ground to 25 μm, Add xylene at last, and get A component after mixing.

[0038] Weigh each component contained in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
Login to view more

Abstract

The invention provides a moisture-curing epoxy zinc phosphate over-rust primer which is prepared by mixing a component A and a component B in a weight ratio of 8:1, wherein the component A comprises 35-50% of epoxy resin, 5-7% of 509 zinc chrome yellow, 5-7% of 309 zinc chrome yellow, 5-7% of 109 zinc chrome yellow, 5-8% of iron oxide red, 6-8% of zinc phosphate, 5-9% of aluminum tripolyphosphate, 6-9% of diphenyl guanidine chromate, 6-8% of dimethylbenzene, 2-4% of n-butanol and 5-8% of cyclohexanone; and the component B comprises 85-90% of ketoimine modified fatty acid epoxy resin, 5-10% of dimethylbenzene and 3-5% of n-butanol. The invention has the advantages of excellent film-forming property, excellent anticorrosive and anti-rust properties, favorable adhesive force for the substrate, favorable flexibility and favorable impact resistance, and can quickly cure to form a film in a high-humidity environment (the relative humidity is less than or equal to 95%).

Description

technical field [0001] The invention belongs to the technical field of painting, and in particular relates to a moisture-curing epoxy zinc phosphate primer with rust. [0002] Background technique [0003] At present, solvent-based rust-resistant anti-corrosion coatings such as epoxy resin and chlorinated rubber are widely used in harbors, ship repairing, marine development projects, Anticorrosion of metal components in power stations, bridge engineering, petrochemical and other industries. However, in the rainy and humid seasons and coastal areas with alternating dry and wet, the relative humidity of the air is above 80%, which provides conditions for the action of oxygen and water. The corrosion of metal substrates is obviously intensified, and the curing rate of coatings is slower than that of substrates. Speed, the water film is easy to form between the coating and the surface of the substrate, which affects the adhesion of the substrate, and the crosslinking density of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D5/08C09D7/12
Inventor 解军刘斌宣飞燕蒋军
Owner 江苏纽克莱涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap