Manufacturing method for terylene strengthened filament weaving pattern rubber bottom coiled material

A manufacturing method and a technology for reinforcing filaments are applied in the field of coil manufacturing, which can solve the problems of radiation, dirt storage, poor foot feel, etc., and achieve the effects of good dimensional stability, no formaldehyde, and rich patterns.

Active Publication Date: 2013-01-30
上海大巨龙蓬盖新材料有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Floor tiles: poor foot feel, radiation, poor sound absorption, not high-end fee...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for terylene strengthened filament weaving pattern rubber bottom coiled material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for manufacturing a polyester reinforced silk braided rubber base coil, comprising the following steps:

[0031] (1) The high-strength polyester yarn is warped to form a multi-strand monomer 500D, and then the PVC paste is plasticized. The formula is: polyvinyl chloride paste resin 100, dioctyl phthalate 100, 200 solvent oil 12, carbonic acid Calcium 20, appropriate amount of color paste, stabilizer 3. Then enter the 24M infrared oven for drying and plasticizing. (Temperature 170, 190, 170°C) cooled by refrigerated water, the water temperature is less than 18°C, and the warp is collected by the large shaft again, divided into warp and weft. Then it is spun on a projectile machine, which can produce weaving patterns of different colors and densities.

[0032] (2) Make adhesive: 100% vinyl acetate resin, 70% dioctyl phthalate, 5% cross-linking agent, 1 accelerator, pour into the high-speed disperser, stir at 1400r / min for 7 minutes, filter with a 100-mesh filte...

Embodiment 2

[0037] A method for manufacturing a polyester reinforced silk braided rubber base coil, comprising the following steps:

[0038] (1) Surface layer processing: The interior is made of high-strength polyester yarn through warping to form a multi-strand monomer, the exterior is coated with PVC paste and plasticized, and then enters a 24M infrared oven for drying, plasticizing, cooling at 170 ° C, and then It is spun by a projectile machine to obtain woven surface layers of different colors and densities. Among them, the PVC paste formula includes the following components and contents: polyvinyl chloride paste resin 100kg, dioctyl phthalate 100kg, 200 No. solvent oil 12kg, calcium carbonate 20, color paste heat-resistant purple 3kg, Ca / Zn composite heat stabilizer 3kg;

[0039] (2) Making adhesive: mix 100kg of vinyl acetate resin, 70kg of dioctyl phthalate, 5kg of cross-linking agent dicumyl peroxide, and 1kg of accelerator 2-mercaptobenzothiazole and place in high-speed dispersi...

Embodiment 3

[0044] A method for manufacturing a polyester reinforced silk braided rubber base coil, comprising the following steps:

[0045] (1) Surface layer processing: The interior is made of high-strength polyester yarns through warping to form multi-strand monomers, the exterior is coated with PVC paste and plasticized, and then enters a 24M infrared oven for drying, plasticizing, cooling at 190°C, and then It is spun by a projectile machine to obtain woven surface layers of different colors and densities. Among them, the PVC paste formula includes the following components and contents: polyvinyl chloride paste resin 100kg, dioctyl phthalate 100kg, 200 No. solvent oil 12kg, calcium carbonate 20, color paste organic perylene red 3kg, Ba / Zn composite heat stabilizer 3kg;

[0046] (2) Making adhesive: 100kg of vinyl chloride resin, 70kg of dioctyl phthalate, 5kg of crosslinking agent dicumyl hydroperoxide, and 1kg of accelerator N-cyclohexyl-2-benzothiazole sulfenamide After mixing, pl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a manufacturing method for a terylene strengthened filament weaving pattern rubber bottom coiled material. The method comprises the following steps: processing a surface layer, preparing an adhesive, processing a bottom back layer, carrying out adhesion processing, and carrying out a UV surface treatment to prepare the terylene strengthened filament weaving pattern rubber bottom coiled material. Compared with the terylene strengthened filament weaving pattern rubber bottom coiled material in the prior art, the terylene strengthened filament weaving pattern rubber bottom coiled material of the present invention has advantages of wear resistance, stain resistance, easy cleaning, safety, no toxicity, no formaldehyde generation, good size stability, easy pavement, flexibility, excellent sound absorbing effect, no noise, good weathering resistance, durability and the like.

Description

technical field [0001] The invention relates to a manufacturing method of a coiled material, in particular to a manufacturing method of a polyester reinforced silk woven pattern rubber bottom coiled material. Background technique [0002] With the development of our country's economy, the paving materials are also varied. Most of the flooring materials on the market are composite floors, floor tiles, carpets, PVC coils or sheets. They all have their limitations of use. [0003] Floor: Contains more formaldehyde, not environmentally friendly, harmful to human body, not water resistant, only suitable for indoor use. [0004] Floor tiles: poor foot feel, radiation, poor sound absorption, and not high-end feeling. [0005] Carpet: It is not easy to clean, and it is only suitable for indoor use. [0006] PVC coil or sheet: simple and unchanged, it feels like stepping on plastic, not high-end. [0007] Polyester reinforced silk braided rubber bottom roll material: overcomes a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00C09J127/06C09J131/04C08L21/00C08K13/02B32B37/06B32B37/12
Inventor 李德荣
Owner 上海大巨龙蓬盖新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap