Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Ethylene-propylene-diene monomer modified bitumen waterproof coiled material and preparation method thereof

A technology of modified asphalt and waterproof membrane, which is applied in the direction of asphalt layered products, chemical instruments and methods, building insulation materials, etc., and can solve water seepage, water channeling, poor adhesion between waterproof membrane and building base, etc. problem, to achieve the effect of reducing cost and high elongation rate

Inactive Publication Date: 2013-03-06
天津市耀新科技发展有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the existing EPDM waterproofing membrane is laid, due to the poor adhesion between the waterproofing membrane and the base of the building, water channeling and water seepage are prone to occur.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1, a kind of modified asphalt waterproof roll material, is made of following raw materials by weight percentage as follows:

[0019] 50 parts of 20# asphalt;

[0020] 20 parts of engine oil;

[0021] 8 parts of SBS glue;

[0022] 10 parts of EPDM rubber material;

[0023] 15 parts of reinforcing agent;

[0024] The preparation method of the EPDM modified waterproof coiled material is characterized in that it comprises the following steps:

[0025] Step 1. Put the bitumen into a high-speed mixer for heating and dehydration.

[0026] Step 2, adding machine oil into the mixer, stirring and heating up.

[0027] Step 3. At 180°C, add SBS rubber and EPDM rubber to continue stirring, and the stirring time is controlled at 1.5-2.5 hours;

[0028] Step 4. Input the mixture evenly stirred through the above steps into the oil immersion tank, and add active calcium carbonate as a reinforcing agent at the same time, and control the temperat...

Embodiment 2

[0030] Embodiment 2, a kind of modified asphalt waterproof roll material, is made of the following raw materials according to weight percentage ratio as follows:

[0031] 50 parts of 20# asphalt;

[0032] 20 parts of engine oil;

[0033] 10 parts of SBS glue;

[0034] 12 parts of EPDM rubber material;

[0035] Reinforcing agent 15 parts

[0036] The preparation method of the EPDM modified waterproof coiled material is characterized in that it comprises the following steps:

[0037] Step 1. Put the bitumen into a high-speed mixer for heating and dehydration.

[0038] Step 2, adding machine oil into the mixer, stirring and heating up.

[0039] Step 3. At 180°C, add SBS rubber and EPDM rubber to continue stirring, and the stirring time is controlled at 1.5-2.5 hours;

[0040] Step 4. Input the mixture evenly stirred through the above steps into the oil immersion tank, and add active calcium carbonate as a reinforcing agent at the same time, and cont...

Embodiment 3

[0042] Embodiment 3, a kind of modified asphalt waterproof roll material, is made of the following raw materials according to weight percentage ratio as follows:

[0043] 50 parts of 20# asphalt;

[0044] 20 parts of engine oil;

[0045] 8 parts of SBS glue;

[0046] 10 parts of EPDM rubber material;

[0047] Reinforcing agent 16 parts

[0048] The preparation method of the EPDM modified waterproof coiled material is characterized in that it comprises the following steps:

[0049] Step 1. Put the bitumen into a high-speed mixer for heating and dehydration.

[0050] Step 2, adding machine oil into the mixer, stirring and heating up.

[0051] Step 3. At 180°C, add SBS rubber and EPDM rubber to continue stirring, and the stirring time is controlled at 1.5-2.5 hours;

[0052] Step 4. Input the mixture evenly stirred through the above steps into the oil immersion tank, and add active calcium carbonate as a reinforcing agent at the same time, and contr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ethylene-propylene-diene monomer modified bitumen waterproof coiled material and a preparation method thereof. The ethylene-propylene-diene monomer modified bitumen waterproof coiled material is prepared by taking bitumen as a base stock and adding an ethylene-propylene-diene monomer, an SBS (styrene butadiene styrene block copolymer) sizing material, a reinforcing agent and the like. The ethylene-propylene-diene monomer modified bitumen waterproof coiled material provided by the invention has lots of excellent integrated economic and technical performance indexes such as excellent waterproofing, flame retardance, seepage resistance, weather resistance, high tensile strength, high percentage of elongation, ageing resistance, well deformation adaptability, wide temperature application range, high cementation, long service life, easy construction and low cost of construction. The ethylene-propylene-diene monomer modified bitumen waterproof coiled material can be used for waterproof engineering of building roofs, bridge floor concrete, undergrounds, roads and the like.

Description

technical field [0001] The invention belongs to the field of building waterproof materials, and in particular relates to an EPDM modified asphalt waterproof coiled material and a preparation method thereof. Background technique [0002] Waterproof membrane is a commonly used building material in building construction. In underground engineering and bridge engineering, waterproof membrane can effectively reduce leakage and protect the main structure of the building. The existing EPDM waterproofing membrane has excellent properties such as high strength, high elongation, high tear strength, high and low temperature resistance, ozone resistance, and aging resistance, so it is widely used in building construction. However, after the existing EPDM waterproofing membrane is laid, water channeling and water seepage are prone to occur due to poor adhesion between the waterproofing membrane and the building base. Contents of the invention [0003] The purpose of the present invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01D19/08B32B11/02C08L95/00C08L23/16C08L53/02C08K3/26
Inventor 刘耀俭孙燕峰
Owner 天津市耀新科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com