Synthesis method and preparation process of hyperbranched polymer resin for intaglio ink

A technology of hyperbranched polymers and engraving gravure inks, which is applied in the field of linking materials, can solve the problems of hyperbranched polyester synthesis and modification that have not been reported, and meet the requirements of inks and printability, moderate fixation time, and promote fast bonding. degree of effect

Active Publication Date: 2015-04-08
CHINA BANKNOTE INK +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this patent introduces hyperbranched polyester into the system as an auxiliary agent, and the synthesis and modification of hyperbranched polyester have not been reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthesis method and preparation process of hyperbranched polymer resin for intaglio ink
  • Synthesis method and preparation process of hyperbranched polymer resin for intaglio ink
  • Synthesis method and preparation process of hyperbranched polymer resin for intaglio ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Put 0.1mol of phthalic anhydride, 0.89mol of triethylene glycol, 0.1mol of ethanol and 0.005mol of concentrated sulfuric acid into a 500ml four-neck flask equipped with a reflux condensing tube, and pass through an inert gas protection, stir and raise the temperature to 100-160°C for reaction After 12 hours, the by-product was evaporated under reduced pressure, and after cooling, 300ml of ether was added to precipitate and wash to obtain a colorless to light yellow liquid, which was a polyhydroxyl hyperbranched polymer. The yield was 94%, and the weight-average molecular weight was 1750. The molecular weight distribution is 2.2.

Embodiment 2

[0044] Under the same reaction condition of embodiment 1, drop into 0.1mol benzene tetracarboxylic acid and 1.34mol4-hydroxyl isophthalic acid, obtain white solid, be polycarboxy hyperbranched polymer, yield is 92%, and weight-average molecular weight is In 2000, the molecular weight distribution was 2.8.

Embodiment 3

[0046] Select 0.1 mol and 0.8 mol of soy oil from Example 1 and put them into a 500ml four-neck flask, pass inert gas protection, stir and raise the temperature to 140°C for 10 hours to obtain an amber liquid with an acid value of 35mgKOH / g and a viscosity of 0.5PaS , the weight average molecular weight is 5500, and the molecular weight distribution is 3.5. (Infrared spectrum see figure 1 ).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a synthesis method and preparation process of hyperbranched polymer resin for intaglio ink. A hyperbranched polymer connection material for the intaglio ink can reduce the contents of volatile organic solvents (VOC) in the ink, can promote the bonding firmness between paper and ink, and meets the ink requirement and the printing adaptability of intaglio printing. The hyperbranched polymer resin has the advantages of good storage stability, shallow color, moderate fixing time and the like; and the prepared intaglio ink has good printing adaptability, drying property, materialization resistance and machine washing resistance; moreover, the contents of the VOC are reduced effectively. The connection material has a structure general formula described in the specification.

Description

technical field [0001] The invention relates to a vehicle for engraving gravure printing ink. Background technique [0002] As the laws and regulations on environmental protection in various countries in the world are increasingly standardized and perfected, such as REACH, RoHS and GHS of the European Union, the environmental protection industry standard of the People's Republic of China HJ / T 371-2007, and the strict requirements of on-site operators on the operating environment, ink Environmental protection issues are increasingly concerned, and the development of gravure inks with low organic solvent (VOC) content has attracted the attention and research of domestic and foreign industries. [0003] At present, the binder made of soybean oil, tung oil, linseed oil, castor oil, tall oil and other vegetable oil modified alkyd resins has been widely used in engraving gravure inks, but the existing engraving gravure inks contain high volatile non-toxic organic solvents. These...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G18/67C08G18/42C08F283/02C09D11/10C09D11/102
Inventor 易方平蒋煜刘雷孙明珠孙军飞赵长富
Owner CHINA BANKNOTE INK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com