Ink for ceramic ink-jet printing and method for preparing same

A ceramic inkjet and ink technology, which is applied in ink, applications, household appliances, etc., can solve the problems of insufficient ink stability, inability to spread, light color, etc., achieve good inkjet printing performance, save production costs, and particle size evenly distributed effect

Active Publication Date: 2013-03-13
GUANGDONG DOWSTONE TECH
View PDF7 Cites 36 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still some problems in the performance of domestic and foreign inks at present, such as insufficient ink stability, easy agglomeration and precipitation of colorants; The wetting condition with the green body is not good, and it is prone to failure to spread or excessive diffusion.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ink for ceramic ink-jet printing and method for preparing same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An ink for ceramic inkjet printing, composed of the following components by mass percentage: 40% black ceramic colorant, 8% polyurethane dispersant (BYK163), 5% alkyd resin (Novalkyd 2550X70C), leveling agent (BYK306) 0.1%, anti-settling agent (Disparlon NS-5501) 0.1%, defoamer (BYK051) 0.3%, ethylene glycol butyl ether 8.5%, diethylene glycol methyl ether 38%.

Embodiment 2

[0032] An ink for ceramic inkjet printing, composed of the following components by mass percentage: blue ceramic colorant 20%, polyacrylate dispersant (EFKA4400) 2%, acrylic resin (NeoCryl B-725) 3% , leveling agent (BYK333) 0.2%, anti-settling agent (Disparlon NS-5501) 0.1%, defoamer (BYK052) 0.7%, ethylene glycol butyl ether 18.5%, diethylene glycol butyl ether 55.5%.

Embodiment 3

[0034] An ink for ceramic inkjet printing, composed of the following components by mass percentage: 50% yellow ceramic pigment, 10% polyacrylate dispersant (EFKA4401), 5% acrylic resin (NeoCryl B-725), Leveling agent (BYK333) 0.2%, anti-settling agent (Disparlon NS-5501) 0.1%, defoamer (BYK052) 0.4%, butyl glycol ether 9.3%, diethylene glycol methyl ether 25%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
viscosityaaaaaaaaaa
surface tensionaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ink for ceramic ink-jet printing and a method for preparing the same, wherein the ink comprises the following components by mass percent: 20-50% of ceramic pigment, 3-8% of resin, 2-10% of dispersant, 0.1-0.2% of flatting agent, 0.3-0.7% of defoamer, 0.08-0.12% of anti-settling agent and the balance of solvent; and the dispersant is a high-molecular-weight polyurethane type dispersant or a high-molecular-weight polyacrylate type dispersant. The ink for ceramic ink-jet printing provided by the invention is good in quality stability and thereby can be stored for a long time; the ink is excellent in ink-jet printing performance, low in ink viscosity and even in particle size distribution; the viscosity of the ink is between 10.0 and 40.0 mPa.s and is controllable; and the surface tension of the ink is 28-38 mN/m, while the average particle size is 200-300 nm and the maximum particle size is less than 800 nm. The method for preparing the ink for ceramic ink-jet printing provided by the invention is simple and efficient; and a one-step mill base grinding process and an ink performance regulation process are carried out, so that the production cost is greatly saved.

Description

technical field [0001] The invention belongs to the technical field of ceramic inkjet, and relates to an ink for ceramic inkjet printing and a preparation method thereof. Background technique [0002] Ceramic inkjet technology is a non-contact digital printing technology. It is ink made of ceramic pigment powder, and small ink droplets are sprayed from a nozzle with a diameter of tens of microns onto the surface of architectural ceramics. After firing The coloring decoration method, the shape and geometric size of the decorative pattern are controlled by the computer. Ceramic inkjet technology abandons the cumbersome traditional printing methods (such as screen printing and roller printing), and directly sprays printing on the green body, which improves the printing accuracy and realizes changeable pattern shapes. Therefore, the tiles produced The image is more realistic and closer to nature. [0003] Since the introduction of the first ceramic inkjet machine in my country...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/10C09D11/326
Inventor 石教艺李向钰张翼
Owner GUANGDONG DOWSTONE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap