Nickel-chromium-based alloy for porcelain teeth and preparation method thereof

A nickel-chromium-based, porcelain-based tooth technology, used in dental preparations, dentistry, dental prostheses, etc., can solve the problems of easy breakage, reduced performance, and can not be reused, and achieve the effect of consistent appearance and color and firm bonding

Active Publication Date: 2013-03-20
洛阳北苑新材料技术有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The main problems of most nickel-chromium-based alloys are: 1) high strength and hardness, but poor toughness and easy fracture; 2) various properties are reduced after secondary melting, so they cannot be reused

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] Below in conjunction with embodiment this patent is further explained and illustrated. But the scope of protection of this patent is not limited to the specific implementation.

[0011] Dosing (mass %) according to the following chemical groups:

[0012] No. Nickel Chromium Molybdenum Tungsten Aluminum Niobium Titanium Silicon Cerium Boron

[0013] A 61.2 23 5 6 1 0.5 1 2 0.2 0.1

[0014] B 62.1 25 4 2 2 1 2 1 0.5 0.4

[0015] C 59.5 22 8 4 2 0.8 1.5 1.5 0.4 0.3

[0016] D 59.3 24 6 5 1.5 0.7 1.8 1.2 0.3 0.2

[0017] E 60.6 23.5 7 3 1.8 0.6 1.3 1.8 0.2 0.2

[0018] Put the ingredients of the above chemical components into a high-temperature crucible, and heat and melt in a vacuum intermediate frequency or high-frequency furnace; stir the high-temperature molten liquid for 5-10 seconds; cast the uniformly stirred molten liquid into a square mold of 10×10×10mm or Ф In a cylindrical mold of 10×10mm, an ingot is formed after natural cooling; the ingot is sandblasted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a nickel-chromium-based alloy for porcelain teeth and a preparation method thereof. The alloy includes by weight: 22-25%chromium, 4-8% of molybdenum, 2-6% tungsten, 1-2% of aluminum, 0.5-1% of niobium, 1-2% of titanium, 1-2% of silicon, 0.2-0.5% of cerium, 0.1-0.4% of boron, and the balance being nickel. The ingredients in accordance with the chemical compositions of the claim 1 are loaded into a high temperature ceramic crucible and heated to melt in a vacuum intermediate frequency or high frequency furnace. The high-temperature molten solution is stirred for 5-10 seconds. The uniformly stirred molten solution is cast into a square mold or cylindrical mold. An ingot is formed after natural cooling. The surface attachments of the ingot are removed by sandblasting. Lastly the ingot is polished to the nickel-chromium-based alloy for the porcelain teeth. The strength, hardness and toughness of the alloy are moderate, the performances are close to imported products, the glaze layer and the metal substrate are solidly combined after porcelain, and the appearance is consistent in color, lifelike, and perfect.

Description

technical field [0001] The invention relates to an alloy material technology, in particular to a nickel-chromium-based alloy used for ceramic teeth and a preparation method thereof. Background technique [0002] Nickel-chromium-based alloys are the main alloys used to make porcelain teeth, which can be used to cast crowns, brackets and other metal parts. The main problems of most nickel-chromium-based alloys are: 1) high strength and hardness, but poor toughness and easy fracture; 2) various properties are reduced after secondary melting, so they cannot be reused. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a nickel-chromium-based alloy for porcelain teeth and its preparation method, and provide a nickel-chromium-based alloy for making porcelain crowns and brackets with simple procedures and convenient operation. [0004] In order to achieve the purpose of solving the above technical problems, the present in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C19/05A61K6/04
Inventor 李军孙学义雷复兴
Owner 洛阳北苑新材料技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com