Flue gas purified anticorrosive conductive coating
An anti-corrosion conductive and flue gas purification technology, applied in anti-corrosion coatings, conductive coatings, coatings, etc., can solve the problems of corrosion protection of flue gas purification equipment, reduce anti-corrosion costs, etc., so that the performance of dust removal, desulfurization and denitration is not affected and reduced Anti-corrosion cost, good index effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Implementation case 1, bisphenol A vinyl ester resin conductive coating composition is as follows:
[0028] Bisphenol A type vinyl ester resin 100 parts
[0029] Graphite 22 parts
[0030] Carbon black 8 parts
[0031] 2 parts of methyl ethyl ketone peroxide
[0032] Cobalt naphthenate liquid 1.5 parts
[0033] Styrene 5 parts
[0034] 3 parts of dimethyl silicone oil
[0035] Paint temperature 90℃, specific resistance 10 4 Ω·cm, the coating adhesion is level 1, the flexibility is 1~2mm, the impact resistance is 45cm, and the corrosion resistance of hot acid and alkali solutions with a concentration of 5% at 60°C. Surface dry time <4h, actual dry time ≤ 20h.
Example Embodiment
[0036] Implementation case 2, phenolic vinyl ester resin conductive coating composition is as follows:
[0037] Phenolic vinyl ester resin 100 parts
[0038] Graphite 15 parts
[0039] 3 parts of methyl ethyl ketone peroxide
[0040] 2 parts of cobalt isooctanoate liquid
[0041] Vapor phase SiO 2 1.5 servings
[0042] 1 part of dimethyl silicone oil
[0043] Red lead 3 parts
[0044] Paint temperature 160℃, specific resistance 10 6 Ω·cm, the coating adhesion is level 1, the flexibility is 1mm, the impact resistance is not less than 45cm, and the corrosion resistance of hot acid and alkali solutions with a concentration of 5% at 80°C. Surface drying time≤3h, actual drying time≤18h.
Example Embodiment
[0045] Implementation case 3, modified vinyl ester resin HCGP-1 conductive coating composition is as follows:
[0046] Modified vinyl ester resin HCGP-1 100 parts
[0047] Graphite 35 parts
[0048] Carbon black 10 parts
[0049] 5 parts of cyclohexanone peroxide paste
[0050] 4 parts of cobalt isooctanoate liquid
[0051] Dimethicone 0.5 parts
[0052] Paint temperature 200℃, specific resistance 10 2 Ω·cm, the coating adhesion is 1-2; flexibility is 1-2mm; impact resistance is 50cm. It is resistant to corrosion by hot acid and alkali solutions with a concentration of 5% at 80°C. Surface drying time≤1.5h, actual drying time≤14h.
PUM
Property | Measurement | Unit |
---|---|---|
Heat resistant | aaaaa | aaaaa |
Specific resistance | aaaaa | aaaaa |
Flexibility | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap