Glass kiln-used dry type micro-expansion heat preservation coating

A thermal insulation coating and micro-expansion technology, applied in the field of refractory materials, can solve the problems of cracking or even falling off, wide application area, low targeting, etc., and achieve the effect of reducing cracks and through-holes, stabilizing combination and strength, and ensuring pulp quality.

Active Publication Date: 2014-07-16
山西高科耐火材料股份有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the common industrial thermal insulation coatings on the market are mostly slurry coatings, which have problems such as high shrinkage at high temperature, which may easily cause a large number of through pores and reduce the thermal insulation effect; coatings are prone to powdering, cracking or even falling off during long-term use; use Wide coverage and low pertinence, unsuitable use temperature leads to poor actual use effect; complex production process, high production cost and high difficulty in storage and transportation; paint is greatly affected by ambient temperature and other problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] The present embodiment contains the following raw materials in parts by weight: 51 parts of expanded perlite, 20 parts of superfine surface active ground calcium carbonate, 10 parts of aluminum silicate fiber, 4 parts of siliceous fine powder, 3 parts of hollow fiber, 9.5 parts of composite binder Parts, 2.5 parts of chemical additives, of which the hollow fiber is a mixture of 1.2 parts of aluminum silicate hollow fiber and 1.8 parts of polypropylene hollow fiber; the composite binder is 1.5 parts of fused aluminate cement, 1 part of silica sol, carboxymethyl 2 parts of base cellulose, 4 parts of high temperature resistant expansion glue, and 1 part of acrylate; chemical additives are 0.6 parts of general-purpose powder defoamer, 0.4 parts of hexamethylenetetramine, 0.5 parts of thermoplastic phenolic resin, Anionic polyacrylamide mixed with 1 part.

[0022] Weigh the prepared raw materials according to the above parts by weight, put the expanded perlite, superfine sur...

Embodiment 2

[0024] This embodiment contains the following raw materials in parts by weight: 48 parts of expanded perlite, 23 parts of superfine surface active ground calcium carbonate, 8 parts of aluminum silicate fiber, 5 parts of siliceous fine powder, 5 parts of hollow fiber, and 8.6 parts of composite binder 2.8 parts of chemical additives, of which the hollow fiber is a mixture of 3 parts of aluminum silicate hollow fiber and 2 parts of polyester hollow fiber; the composite binder is 1.4 parts of fused aluminate cement, 0.9 part of silica sol, carboxymethyl 1.8 parts of cellulose, 3.6 parts of high temperature resistant expansion rubber, 0.9 parts of vinyl acetate; chemical additives are 0.5 parts of general-purpose powder defoamer, 0.5 parts of hexamethylenetetramine, 0.8 parts of thermoplastic phenolic resin, anion Mixed with 1 part polyacrylamide.

[0025] Weigh the prepared raw materials according to the above parts by weight, put the expanded perlite, superfine surface active gr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dry-type micro-expansion thermal insulation coating for a glass kiln, which is characterized in that it contains the following raw materials in parts by weight: 30-60 parts of expanded perlite, 20-40 parts of superfine surface-active heavy calcium carbonate, silicon 5-10 parts of aluminum acid fiber, 2-5 parts of siliceous fine powder, 2-5 parts of hollow fiber, 5-13 parts of composite binder, 1-4 parts of chemical additives; Active ground calcium carbonate, aluminum silicate fiber, siliceous fine powder, and hollow fiber are put into the mixer in turn and mixed evenly, and then the remaining composite binder and chemical additives are added into the mixer and stirred until they are fully mixed. The dry thermal insulation coating made from the above-mentioned raw materials in the present invention not only reduces the stagnant material defoaming and standing link after foaming, but also avoids the problems of deterioration and dehydration caused by long-distance transportation of traditional slurry coatings. It has the characteristics of remarkable heat preservation and energy saving effect, convenient construction and so on.

Description

technical field [0001] The invention belongs to the field of refractory materials, and in particular relates to a dry micro-expansion thermal insulation coating for a glass kiln. Background technique [0002] With the rapid development of the market economy, the consumption of resources and energy has increased significantly. Energy saving and consumption reduction has become the common goal of enterprises. The use of thermal insulation products is the most common and effective means for high-temperature production enterprises to achieve energy conservation and consumption reduction. Driven by market demand, many experts and scholars have done a lot of fruitful work. Thermal insulation and energy-saving products have developed rapidly, product performance has been significantly improved, and product applications have gradually become refined, but there are still certain deficiencies. At present, the common industrial thermal insulation coatings on the market are mostly slurr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/66C03B5/43
Inventor 侯俊高峰王虹
Owner 山西高科耐火材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products