A technology of resin glass fiber and resin, applied in the field of industrial waste recycling, can solve the problems of secondary pollution, high cost, and consumption of land resources

Inactive Publication Date: 2013-04-03
清远市宏保环保科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Random dumping will cause secondary pollution, incineration and landfill will generate high costs and consume land resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The formula provided by the invention comprises the following components in parts by weight:

[0019] Resin glass fiber powder: 90kg

[0020] Epoxy resin: 20kg

[0021] The copper-containing rate of the resin glass fiber powder is 3%.

[0022] The recycling method of the resin glass fiber powder in the formula is to crush, heat, and screen one or more mixtures of waste electronic circuit boards, scraps of copper-clad laminates, or defective products, and extract the metal powder to obtain a copper content of less than 5. % resin glass fiber powder.

Embodiment 2

[0024] Resin glass fiber powder: 90kg

[0025] Epoxy resin: 20kg

[0026] The copper-containing rate of the resin glass fiber powder is 1.8%, the lead-containing rate is 0.15%, and the zinc-containing rate is 0.2%.

Embodiment 3

[0028] Resin glass fiber powder: 86kg

[0029] Epoxy resin: 14kg

[0030] The copper-containing rate of the resin glass fiber powder is 1.8%, the lead-containing rate is 0.15%, and the zinc-containing rate is 0.2%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a resin glass fiber formulation and a flowerpot made thereby. The resin glass fiber formulation comprises the following components in part by weight: 80-95 parts of resin glass fiber powder and 5-20 parts of epoxide resin, wherein the resin glass fiber powder has the copper content of smaller than 5%. The resin glass fiber flowerpot is made from the following components in part by weight: 80-95 parts of resin glass fiber powder and 5-20 parts of epoxide resin, wherein the resin glass fiber powder has the copper content of smaller than 5%. Due to characteristics of the resin glass fiber powder, the flowerpot made from the resin glass fiber powder as a raw material has the characteristics of water resistance, corrosion resistance, moth resistance, acid and alkali resistance, aging resistance, light weight (compared with a clay flowerpot), low probability of breakage and the like; and a small amount of heavy metal exists in the resin glass fiber powder, so that during slow release of the heavy metal, the color and luster of a flower can be more bright and beautiful and the flowering phase can be prolonged.

Description

technical field [0001] The invention relates to the recycling of industrial waste, in particular to a resin glass fiber formula derived from industrial waste and a flower pot made from the formula. Background technique [0002] With the vigorous development of the electronics industry, the processing of waste electronic circuit boards, waste copper-clad laminate scraps and defective products is increasing day by day. Correspondingly, the treatment and disposal of industrial solid waste, such as resin glass fiber powder remaining after metal extraction, has become a thorny problem. Random dumping will cause secondary pollution, and incineration and landfill will generate high costs and consume land resources. How to properly dispose and effectively comprehensively utilize resin glass fiber powder has become an important issue to solve environmental protection problems. Contents of the invention [0003] The object of the present invention is to propose a kind of appro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L101/00C08L63/00C08K7/14A01G9/02
Inventor 严志龙代强
Owner 清远市宏保环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap