Water mill for stone machining and preparation method thereof

A stone processing and water grinding wheel technology, applied in metal processing equipment, grinding/polishing equipment, abrasives, etc., to achieve high grinding efficiency, overcome scratches, and high brightness

Active Publication Date: 2015-06-17
郑州新安华砂轮有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved in the present invention is to provide a water grinding wheel for stone processing and its preparation method for the defects existing in existing stone processing materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The present invention is used for the water grinding wheel of stone material processing, and this water grinding wheel is prepared from the raw material of following weight part:

[0025] 25 parts of black silicon carbide, 15 parts of silicon dioxide, 4 parts of polyethylene glycol, 50 parts of epoxy resin, 2.0 parts of methyl ethyl ketone peroxide, 2 parts of cobalt isooctanoate and 30 parts of magnesium sulfate.

[0026] The mass percentage of Si in the raw material black silicon carbide used is ≥95%; the fineness of silicon dioxide is 300 mesh.

Embodiment 2

[0028] The present invention is used for the water grinding wheel of stone material processing, and this water grinding wheel is prepared from the raw material of following weight part:

[0029] 28 parts of black silicon carbide, 18 parts of silicon dioxide, 5 parts of polyethylene glycol, 56 parts of epoxy resin, 2.2 parts of methyl ethyl ketone peroxide, 2.5 parts of cobalt isooctanoate and 33 parts of magnesium sulfate.

[0030] The mass percentage of Si in the raw material black silicon carbide used is ≥95%; the fineness of silicon dioxide is 400 mesh.

Embodiment 3

[0032] The present invention is used for the water grinding wheel of stone material processing, and this water grinding wheel is prepared from the raw material of following weight part:

[0033] 23 parts of black silicon carbide, 13 parts of silicon dioxide, 3 parts of polyethylene glycol, 44 parts of epoxy resin, 1.8 parts of methyl ethyl ketone peroxide, 1.0 parts of cobalt isooctanoate and 28 parts of magnesium sulfate.

[0034] The mass percentage of Si in the raw material black silicon carbide used is ≥95%; the fineness of silicon dioxide is 280 mesh.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water mill for stone machining and a preparation method thereof. The water mill is prepared through black silicon carbide, silica, polyethylene glycol, epoxy resins, methyl ethyl ketone peroxide, cobalt iso-octoate and magnesium sulfate. The method comprises placing the polyethylene glycol and the epoxy resins in a reaction still to be heated and stirred evenly; putting the black silicon carbide, silica and the magnesium sulfate in a mixer to be stirred and mixed evenly; putting the evenly stirred mixtures in the mixer to be stirred evenly, adding methyl ethyl ketone peroxide and cobalt iso-octoate in the mixtures to be heated and stirred evenly to be discharged to obtain a mixed material; and putting the mixed material in a mould, and molding and drying the material naturally under the normal pressure and temperature to obtain the product water mill. The water mill prepared through the method has a higher grinding effect, surface smoothness and brightness than an ordinary grinding head, and ideal effects of users can be achieved without wool wheel polishing.

Description

technical field [0001] The invention relates to a grinding head for stone processing, in particular to a water grinding wheel for stone processing and a preparation method thereof. Background technique [0002] In real life, many products need to be polished because of surface accuracy requirements or aesthetic considerations. The main method is to move a high-speed rotating grinding head on the surface to be polished to polish the surface. Grinding head is a general term for a small grinding tool with a handle, which is used in electric grinders, hanging grinders, electric hand drills, etc. There are many types of grinding heads, mainly ceramic grinding heads, rubber grinding heads, diamond grinding heads, emery cloth grinding heads, etc. . [0003] Wherein for the processing grinding and polishing of stone, the commonly used grinding heads in the prior art are prone to scratches in the process of processing stone, and the polishing effect is relatively poor and the grindi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B24D3/28B24D18/00
Inventor 李士欣
Owner 郑州新安华砂轮有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com