Composite molded nanoplate and preparation method thereof

A composite mold, nano-board technology, used in building components, thermal insulation and other directions, to achieve the effects of high tensile strength, reduced thermal conductivity, and high combustion grade

Active Publication Date: 2014-10-22
湖北邱氏节能建材高新技术股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing building insulation panels, such as Chinese patent application number: 201210290547.0 (formwork integrated thermal insulation board and its processing method); such as Chinese patent application number: 201220144731.X (a continuous foam insulation fireproof board); such as Chinese patent Application number: 201230106460.4 (polystyrene foam for heat insulation (EPS insulation board - black)); they mainly use styrene, gypsum, foaming agent, fiber and other materials, but their thermal conductivity, combustion performance level, water absorption, Comprehensive properties such as tensile strength and flexibility need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite molded nanoplate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Composite molded nanoplates, which consist of styrene, deionized water, dibenzoyl peroxide (BPO), tert-butyl perbenzoate (T-BPB), hydroxyethyl cellulose (HEC), calcium hydroxyphosphate ( TCP), sodium pyrophosphate, pentane, sodium butylnaphthalene sulfonate and expandable graphite raw materials are produced by batch suspension polymerization process to form an expandable polymer, and then pre-foamed and molded into a board that is convenient for engineering construction type (i.e. composite molded nano-plate); the mass parts of each raw material are: 100 parts of styrene, 120 parts of deionized water, 0.4 parts of dibenzoyl peroxide (BPO), tert-butyl perbenzoate (T -BPB) 0.07 parts, hydroxyethyl cellulose (HEC) 0.1 parts, hydroxycalcium phosphate (TCP) 0.4 parts, sodium pyrophosphate 0.02 parts, pentane 8 parts, butyl naphthalene sodium sulfonate 8 parts, expandable graphite 1.0 share.

[0047] The styrene is produced by BASF (China) Co., Ltd.

[0048] Described diben...

Embodiment 2

[0075] Basically the same as Example 1, the difference is that the mass parts of each raw material are different, the present embodiment: the mass parts of each raw material are: 100 parts of styrene, 120 parts of deionized water, dibenzoyl peroxide (BPO) 0.3 parts, tert-butyl perbenzoate (T-BPB) 0.08 parts, hydroxyethyl cellulose (HEC) 0.1 parts, hydroxycalcium phosphate (TCP) 0.5 parts, sodium pyrophosphate 0.02 parts, pentane 8 parts , 8 parts of sodium butylnaphthalene sulfonate, and 1.5 parts of expandable graphite.

[0076] Its preparation method is the same as in Example 1 (only the mass parts of each raw material are different).

[0077] The composite molded nanoplate prepared in this embodiment is tested as follows:

[0078] 1. Thermal conductivity test: According to GB / T10294 test, the experimental result is 0.0279W / ﹙m*k﹞, which shows that the thermal conductivity of the present invention is low.

[0079] 2. Breaking bending load test: test according to GB / T8812. ...

Embodiment 3

[0087] Basically the same as Example 1, the difference is that the mass parts of each raw material are different, the present embodiment: the mass parts of each raw material are: 100 parts of styrene, 120 parts of deionized water, dibenzoyl peroxide (BPO) 0.4 parts, tert-butyl perbenzoate (T-BPB) 0.06 parts, hydroxyethyl cellulose (HEC) 0.1 parts, hydroxycalcium phosphate (TCP) 0.4 parts, sodium pyrophosphate 0.02 parts, pentane 8 parts , 8 parts of sodium butylnaphthalene sulfonate, and 1.2 parts of expandable graphite.

[0088] Its preparation method is the same as in Example 1 (only the mass parts of each raw material are different).

[0089] The composite molded nanoplate prepared in this embodiment is tested as follows:

[0090] 1. Thermal conductivity test: According to GB / T10294 test, the experimental result is 0.0279W / ﹙m*k﹞, which shows that the thermal conductivity of the present invention is low.

[0091] 2. Breaking bending load test: test according to GB / T8812. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of architectural heat-preservation materials. A composite molding nano plate is characterized in that the nano plate is prepared from the following raw materials in parts by mass: 100 parts of styrene, 120 parts of deionized water, 0.3-0.5 part of dibenzoyl peroxide, 0.04-0.08 part of t-butyl perbenzoate, 0.1-0.2 part of hydroxyethyl cellulose, 0.3-0.5 part of hydroxyapatite, 0.02 part of sodium pyrophosphate, 8 parts of pentane, 2-8 parts of sodium butylnaphthalenesulfonate, and 1.0-1.5 parts of graphite. The composite molding nano plate has the effects of nano pore diameter, low heat conductivity coefficient, good flexibility, good chemical resistance, high combustion level, high tensile strength and low water absorption, and is convenient for architectural heat-preservation engineering construction.

Description

technical field [0001] The invention belongs to the technical field of building thermal insulation materials, and in particular relates to a composite molded nanometer board and a preparation method thereof. Background technique [0002] In recent years, the method of using insulation panels on the walls of buildings to ensure the energy-saving performance of buildings has been more and more widely used. Existing building insulation panels, such as Chinese patent application number: 201210290547.0 (formwork integrated thermal insulation board and its processing method); such as Chinese patent application number: 201220144731.X (a continuous foam insulation fireproof board); such as Chinese patent Application number: 201230106460.4 (polystyrene foam for heat insulation (EPS insulation board - black)); they mainly use styrene, gypsum, foaming agent, fiber and other materials, but their thermal conductivity, combustion performance level, water absorption, Comprehensive propert...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08F112/08C08F2/18C08K3/04C08J9/228C08J9/20C08J9/14E04B1/80
Inventor 邱杰儒
Owner 湖北邱氏节能建材高新技术股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com