Er-containing high-niobium Ti-Al intermetallic compound material and preparation method thereof

An intermetallic compound, high niobium technology, applied in the intermetallic compound material, Er-containing high niobium TiAl intermetallic compound material and its preparation field

Inactive Publication Date: 2013-05-01
BEIJING UNIV OF TECH
View PDF3 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no reports on the preparation of high-Nb TiAl intermetallic materials con

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Er-containing high-niobium Ti-Al intermetallic compound material and preparation method thereof
  • Er-containing high-niobium Ti-Al intermetallic compound material and preparation method thereof
  • Er-containing high-niobium Ti-Al intermetallic compound material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0016] Example 1

[0017] The preparation of the Er-containing high-niobium TiAl intermetallic compound material of this embodiment is achieved by the following steps: 1. Weigh the following raw materials: sponge titanium, high-purity aluminum, aluminum-niobium master alloy and aluminum-erbium master alloy, of which Ti45.8at.% , Al46at.%, Nb8at.%, Er0.2at.%; 2. Add the raw materials weighed in step 1 into the water-cooled copper crucible vacuum induction melting furnace. The layers from bottom to top are respectively sponge titanium layer and high Pure aluminum layer, aluminum-niobium intermediate alloy layer, aluminum-erbium intermediate alloy layer and sponge titanium layer; 3. Before smelting, preheat the metal mold at a temperature of 350℃, and evacuate the water-cooled copper crucible vacuum induction melting furnace to 3.0× 10 -3 mbar; 4. Increase the smelting power of the water-cooled copper crucible vacuum induction melting furnace to 180kw at a growth rate of 10kw / min, t...

Example Embodiment

[0019] Example 2

[0020] (1) Weigh the following raw materials: sponge titanium, high-purity aluminum, aluminum-niobium master alloy and aluminum-erbium master alloy; among them, control the molar percentage of Al, Nb, Er and Ti to 41%~46% Al, 8~10% Nb, 0.2-0.4% Er, the balance Ti and impurities;

[0021] (2) The raw materials weighed in step (1) are added into a water-cooled copper crucible vacuum induction melting furnace in layers. The layers from bottom to top are sponge titanium layer, high-purity aluminum layer, aluminum-niobium intermediate alloy layer, aluminum Erbium master alloy layer and sponge titanium layer; preheat the metal mold to 300~350℃ before smelting, and vacuum the water-cooled copper crucible vacuum induction melting furnace to 2.0~3.0×10 -3 mbar, increase the smelting power of the water-cooled copper crucible vacuum induction melting furnace to 160-180kw at a growth rate of 5-10kw / min, then stop increasing the power, and then smelt at a constant power for 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Sizeaaaaaaaaaa
Grain sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses an Er-containing high- niobium Ti-Al intermetallic compound material and a preparation method thereof, and belongs to intermetallic compound materials. The material is composed of the following elements in mole percent: 41-46 percent of Al, 5-15 percent of niobium, no more than 0.4 percent of Er, and the balance of Ti and unavoidable impurities. The preparation method comprises the following steps: adding titanium sponge, high-purity aluminium, Al- niobium intermediate alloy and Al-Er intermediate alloy into a water cooled copper crucible vacuum induction smelting furnace as per the composition, vacuumizing to 2.0-3.0*10<-3>mbar, rising the smelting power to 160-180 kW at the speed of 5-10 kW/min and stopping at 160-180 kW, smelting for 1-3 minutes at a constant power, obtaining melt, mixing the melt uniformly; and casting the melt into a metal mold preheated to 300-350 DEG C, forming an Er-containing high-niobium Ti-Al intermetallic compound material ingot, and cooling together with the smelting furnace. The method enables the crystal size and layer space of the Ti-Al intermetallic chemical combination to be smaller and thinner.

Description

technical field [0001] The invention relates to a rare earth element-containing intermetallic compound and a preparation process thereof, in particular to an Er-containing high-niobium TiAl intermetallic compound material and a preparation method thereof, belonging to the intermetallic compound material. Background technique [0002] Due to its low density, low expansion coefficient, high specific strength, high elastic modulus, and good high-temperature creep and oxidation resistance, TiAl intermetallic compounds are highly valued in the fields of aviation, aerospace, and automobiles. However, the disadvantages of TiAl intermetallic compounds, such as low room temperature plasticity and poor hot processability, limit their wide application. Scholars at home and abroad have done a lot of research work on the microstructure, plasticity and deformation of TiAl intermetallic compounds. The results show that refining the microstructure is an important means to improve the mecha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C14/00C22C30/00C22C1/03
Inventor 陈子勇宫子琪柴丽华相志磊
Owner BEIJING UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap