Coating containing tea dust and tea polyphenol and preparation method of coating

A technology of tea powder and tea polyphenols, which is applied in anti-corrosion coatings, anti-fouling/underwater coatings, polyurea/polyurethane coatings, etc., can solve the problem of high mortality from sepsis and achieve the effect of preventing environmental pollution

Inactive Publication Date: 2013-05-15
河北百年巧匠文化传播股份有限公司
View PDF6 Cites 28 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Tea polyphenols have a significant inhibitory effect on Staphylococcus aureus, Proteus, and Pseudomonas aeruginosa that cause purulent infections, burns, and trauma. These three strains are prone to drug resistance, and the resulting sepsis Mortality rate as high as 80%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] 1.1 Coating composition

[0063] water 20%

[0064] Water-based emulsion 38.4%

[0065] Titanium dioxide 25%

[0066] Tea powder 5%

[0067] Tea polyphenols 5%

[0068] Defoamer 0.5%

[0069] Dispersant 0.6%

[0070] pH regulator 0.4%

[0071] Coalescent 3%

[0072]Thickener 2%

[0073] Antifungal agent 0.1%

[0074] 1.2 Preparation method

[0075] (1) First, the tea powder is ultrafinely pulverized until the particle size is less than 10 μm.

[0076] (2) Add the water in the formula to the container, add dispersant, defoamer, pH regulator, titanium dioxide in sequence at a stirring speed of 800r / min, after adding, adjust the speed to 2500r / min, the dispersion fineness to below 25μm,

[0077] (3) At a stirring speed of 800r / min, add tea powder, tea polyphenols, antifungal agent, water-based emulsion and film-forming aid in sequence, stir for 10 minutes, then adjust the speed to 400r / min, and stir for 30 minutes.

[0078] (4) Add thickener and continue to st...

Embodiment 2

[0088] 2.1 Coating composition

[0089] water 45%

[0090] Water-based emulsion 42.6%

[0091] Titanium dioxide 10%

[0092] Tea powder 1%

[0093] Tea polyphenols 1%

[0094] Defoamer 0.1%

[0095] Dispersant 0.2%

[0096] pH regulator 0.1%

[0097] 2.2 Preparation method

[0098] (1) First, the tea powder is ultrafinely pulverized until the particle size is less than 10 μm.

[0099] (2) Add the water in the formula to the container, and add the dispersant, defoamer, pH regulator, titanium dioxide in sequence at a stirring speed of 500r / min, and adjust the speed to 1500r / min after adding, and the dispersion fineness to below 25μm,

[0100] (3) At a stirring speed of 500r / min, add tea powder, tea polyphenols, and water-based emulsion in sequence, stir for 10 minutes, then adjust the speed to 300r / min, and stir for 20 minutes.

[0101] (4) Continue to stir for 15 minutes, then adjust the pH to 7.5~9 with a pH regulator, and then pack it after stirring for 10 minutes t...

Embodiment 3

[0111] 3.1 Coating Composition

[0112] Water 20.5%

[0113] Water-based emulsion 50%

[0114] Titanium dioxide 20%

[0115] Tea powder 3%

[0116] Tea polyphenols 3%

[0117] Defoamer 0.3%

[0118] Dispersant 0.4%

[0119] pH regulator 0.25%

[0120] Coalescent 1.5%

[0121] Thickener 1%

[0122] Antifungal agent 0.05%

[0123] 3.2 Preparation method

[0124] (1) First, the tea powder is ultrafinely pulverized until the particle size is less than 10 μm.

[0125] (2) Add the water in the formula to the container, add dispersant, defoamer, pH regulator, titanium dioxide in sequence at a stirring speed of 700r / min, and adjust the rotating speed to 2000r / min after adding, the dispersion fineness to below 25μm,

[0126] (3) At a stirring speed of 700r / min, add tea powder, tea polyphenols, antifungal agent, water-based emulsion and film-forming aid in sequence, stir for 10 minutes, then adjust the speed to 350r / min, and stir for 25 minutes.

[0127] (4) Add a thickener...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating containing tea dust and tea polyphenol. The coating is composed of water, waterborne emulsion, titanium dioxide, a mildew preventive, a dispersing agent, a deforming agent, a pH regulator, a coalescing agent, a thickening agent, the tea dust and the tea polyphenol. Preferably, the coating is composed of 20-45% of water, 20-50% of waterborne emulsion, 10-25% of titanium dioxide, 1-5% of tea dust, 1-5% of tea polyphenol, 0.1-0.5% of deforming agent, 0.2-0.6% of dispersing agent, 0.1-0.4% of pH regulator, 0-3% of coalescing agent, 0-2% of thickening agent and 0-0.1% of mildew preventive. The tea dust and the tea polyphenol are added into the coating, so that the waste tea dust is reused on the one hand, and environment pollution can be prevented on the other hand; the coating prepared by the invention not only can be used for killing bacteria of the coating and bacteria generated in the preparation process, but also can be used for inhibiting and killing indoor bacteria when being applied to indoor decoration; and in addition, the coating can also be used for removing formaldehyde in wood and indoor formaldehyde so as to play a role of purifying air.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a coating added with tea powder and tea polyphenols and a preparation method thereof. Background technique [0002] Paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, or oil, or emulsion, with or without adding pigments, fillers, and adding corresponding Additives, viscous liquids prepared with organic solvents or water. [0003] Coating refers to a type of liquid or solid material that can form a thin film on the surface of an object under certain conditions for protection, decoration or other special functions (insulation, rust prevention, mildew resistance, heat resistance, etc.). Because most of the early paints used vegetable oil as the main raw material, they are also called paints. The synthetic resin has replaced the vegetable oil, so it is called paint. Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/14C09D5/08C09D133/00C09D175/04C09D183/04
Inventor 郭漫笳裴艳丽
Owner 河北百年巧匠文化传播股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com