Material special for breathable film with antiflaming effect and preparation method thereof

A technology of breathable film and special material, applied in the field of breathable film PE special material and its preparation, can solve the problems of limited application range, poor compatibility of flame retardants, and no flame retardant effect of breathable film, achieve excellent processing characteristics, add less effect

Inactive Publication Date: 2013-06-05
福建奥峰科技有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, breathable membranes made of PE are often not flame retardant, which limits their application range.
This is because the flame retardant of PE is usually modified by a large amount of inorganic or organic flame retardants. However, due to the poor compatibility between

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0032] Example 1

[0033] 76 parts of linear low density polyethylene;

[0034] 12 parts of high pressure low density polyethylene;

[0035] Styrene thermoplastic elastomer-SEBS 5 parts;

[0036] 3 parts of flame retardant A-NOR116;

[0037] 3 parts of flame retardant B-FM-2100;

[0038] Surface treatment agent-aluminate coupling agent 2 parts;

[0039] Filler-65 parts of calcium carbonate;

[0040] Lubricant-erucamide 0.4 parts and

[0041] Antioxidant-IRGANOX 1010 0.5 parts.

[0042] The moisture permeability (WVTR) of the breathable film prepared in this embodiment can reach 2650g / (m 2 ·24hrs), the flame retardant effect can reach DIN4102-B2.

Example Embodiment

[0043] Example 2

[0044] 55 parts of linear low density polyethylene;

[0045] 15 parts of high pressure low density polyethylene;

[0046] Styrene-based thermoplastic elastomer-SBS 5 parts;

[0047] 0.5 parts of flame retardant A-NOR116;

[0048] 8 parts of flame retardant B-FM-2100;

[0049] Surface treatment agent-3 parts of stearic acid;

[0050] Filler-35 parts of talc;

[0051] Lubricant-0.4 parts of stearic acid amide and

[0052] Antioxidant-IRGANOX 1076 0.5 parts.

[0053] The molding processability of this embodiment is good, and the moisture permeability (WVTR) of the breathable film can reach 2050g / (m 2 ·24hrs), the flame retardant effect can reach DIN4102-B2.

Example Embodiment

[0054] Example 3

[0055] 65 parts of linear low density polyethylene;

[0056] 13 parts of high pressure low density polyethylene;

[0057] Styrene thermoplastic elastomer-SEPS 5 parts;

[0058] 1 part of flame retardant A-NOR116;

[0059] 6 parts of flame retardant B-FM-2100;

[0060] Surface treatment agent-titanate coupling agent 3 parts;

[0061] Filler-50 parts of calcium carbonate;

[0062] Lubricant-0.4 parts of oleic acid amide and

[0063] Antioxidant-IRGAFOS38 0.5 parts.

[0064] The molding processability of this example is good, and the moisture permeability (WVTR) of the breathable film prepared in the example can reach 2430g / (m 2 ·24hrs), the flame retardant effect can reach DIN4102-B2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a material special for a breathable film with antiflaming effect and a preparation method of the material special for the breathable film with the antiflaming effect. The material special for the breathable film with the antiflaming effect is composed of the following component: by weight, 55-76 parts of linear low density polyethylene, 12-15 parts of high pressure low density polyethylene, 4-6 parts of styrene thermoplastic elastomer, 0.5-3 parts of antiflaming agent A, 3-8 parts of antiflaming agent B, 2-4 parts of surface treating agent, 35-65 parts of filling agent, 4-6 parts of styrene thermoplastic elastomer, 0.3-0.5 part of lubricant, and 0.4-0.6 part of antioxidizer. The components are put in a blender or a high-speed blending machine to be fully premixed in proportion, and then a double screw extruder is used for fusing and blending to extract granulation. The material special for the breathable film with the antiflaming effect has good processing features, and water vapor transmission rate (WVTR) of the breathable film prepared from the material special for the breathable film with the antiflaming effect can achieve 1800-200 grams/ (m 2* 24 hrs), and antiflaming effect can achieve DIN 4102-B2.

Description

technical field [0001] The invention relates to a preparation method of a film, in particular to a special PE material for a breathable film with a flame-retardant effect and a preparation method thereof. Background technique [0002] The breathable film can be prepared by mixing a specific thermoplastic polymer with a certain proportion of mineral fillers to prepare the corresponding special material for the breathable film, cast into a film or blown into a film through an extruder, and then stretch it longitudinally or transversely. , with waterproof and breathable function. The market prospect of breathable film is still generally optimistic in the industry, and it can be widely used in textiles, sanitary products, construction, medical treatment and other fields. These industries have higher and higher requirements for the multi-functionality of membrane products. Among them, especially in the construction field, the flame retardancy of breathable membranes is more and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/08C08L23/06C08L53/00C08L53/02C08K13/06C08K9/04C08K5/03C08K3/26C08K3/34C08K3/30C08K5/20B29C47/92B29C48/92
CPCB29C48/04B29C48/08B29C48/40
Inventor 欧阳环赵勤宽
Owner 福建奥峰科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap