Completely biodegradable stone paper material and preparation method thereof
A technology of biodegradation and stone paper, which is applied in the field of stone paper materials, can solve the problems of non-biodegradability, and achieve the effects of low cost, simple and easy preparation method, and easy popularization and application
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] Mix 55% heavy calcium carbonate (1250 mesh), 5% talc powder (3000 mesh), 25% PBAT (melting point: 110-120°C, melting index: 4.5), 5% PBS (melting point: 114°C, melting index: 6.2), 3.5% acetyl tributyl citrate, 0.5% succinic acid, 1% di(dioctyl pyrophosphate) glycolate titanate (KR138S), 2% N,N-ethylene bisstearamide ( EBS), 3% PE wax (melting point: 95-100°C) were sequentially added to the high-speed mixer with oil bath heating, the oil bath temperature was set to 40°C, and high-speed (1400rpm) stirring for 120s, after pre-plasticization Release; then add the pre-plasticized material to the parallel twin-screw extruder with an aspect ratio of 48 to further plasticize, extrude and granulate to obtain stone paper materials. The 12 zones of the extruder are 120-140-145-150- 150-150-150-150-150-145-145-140°C.
Embodiment 2
[0033] Mix 30% heavy calcium carbonate (1250 mesh), 45% sodium sulfate (2000 mesh), 18% P3,4-HB (melting point: 110-120°C, melting index: 6.0), 2% PLA (melting point: 160- 170°C, melt index: 4.3), 1% dioctyl phthalate, 1% glycerin, 2% γ-aminopropyltriethoxysilane (KH550), 1% erucamide were added to the oil In the high-speed mixer heated by the bath, the temperature of the oil bath is set at 55°C, stirred at high speed (1000rpm) for 80s, pre-plasticized and released; then the pre-plasticized material is added to the parallel twin-screw extruder with an aspect ratio of 48 Further plasticizing, extruding and granulating to obtain the stone paper material, the temperature of each zone in the 12 zones of the extruder is 130-150-155-160-160-160-160-160-160-155-155-150°C.
Embodiment 3
[0035]Mix 32% light calcium carbonate (3000 mesh), 20% mica powder (2000 mesh), 20% PBST (melting point: 110-120°C, melting index: 3.0), 10% PBSA (melting point: 85-95°C, melting Index: 8.5), 5% PCL (melting index: 23.1), 3.5% trioctyl citrate, 1.5% monoglyceride stearate, 0.5% malic acid, 1% adipic acid, 2.5% tri(dodecane phenylsulfonyl) isopropyl titanate (KR-9S), 1% calcium stearate, 3% N,N-bisstearamide (EBS) were sequentially added to a high-speed mixer with oil bath heating, Set the temperature of the oil bath at 30°C, stir at high speed (800rpm) for 150s, and release the pre-plasticized material; then add the pre-plasticized material to the parallel twin-screw extruder with an aspect ratio of 48 for further plasticizing, extruding and granulating To obtain the stone paper material, the temperature of each zone in the 12 zones of the extruder is 110-120-130-130-130-130-130-130-130-130-125-120°C.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap