Composite film for medicine packaging, and making method thereof

A packaging and composite film technology, applied in the field of pharmaceutical packaging, can solve the problems of high cost of glass glue and difficult to open packaging bags, etc., and achieve the effect of high peel strength, good heat sealing performance, and tight composite

Inactive Publication Date: 2013-06-26
常州市华健药用包装材料有限公司
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] A technical problem to be solved by the present invention is: Based on the above problems, the present invention provides an easy-to-tear and easy-to

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite film for medicine packaging, and making method thereof
  • Composite film for medicine packaging, and making method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A 1100mm wide gravure rotary high-speed printing machine is used to add benzene and ketone-free inks for printing; the non-printing surface of the aluminum foil is coated with a screen roll as a coating roll, coated with a two-component polyurethane resin glue, and then passed through 50 ° C, Dry the solvent in a three-stage oven at 60°C and 70°C, enter the composite roller and polyethylene film, and then wind up to form a composite semi-finished product; put the above composite semi-finished product in a curing room at 50°C for 36 hours; put the composited The packaging film is cut into roll film with a 1000mm wide slitting machine; the cut roll film is made into a center seal bag or a three side seal bag or other Shaped bag.

[0024] The composite film for pharmaceutical packaging prepared in this example has clear layers, beautiful appearance, pressure resistance, compact composite, no blistering, no rupture, high peel strength, good heat sealing performance, and goo...

Embodiment 2

[0026] A 1100mm wide gravure rotary high-speed printing machine is used to add benzene and ketone-free inks for printing; the non-printing surface of the aluminum foil is coated with a screen roll as a coating roll, and coated with a two-component polyurethane resin glue. Dry the solvent in a three-stage oven at 65°C and 75°C, enter the composite roll and heat the polyethylene film, and then wind up to form a composite semi-finished product; put the above composite semi-finished product in a curing room at 55°C for 48 hours; put the composited The packaging film is cut into roll film with a 1000mm wide slitting machine; the cut roll film is made into a center seal bag or a three side seal bag or other Shaped bag.

[0027] The composite film for pharmaceutical packaging prepared in this example has clear layers, beautiful appearance, pressure resistance, compact composite, no blistering, no rupture, high peel strength, good heat sealing performance, and good tearability and eas...

Embodiment 3

[0029] A 1100mm wide gravure rotary high-speed printing machine is used to add benzene and ketone-free inks for printing; the non-printing surface of the aluminum foil is coated with a screen roll as a coating roll, and coated with a two-component polyurethane resin glue. Dry the solvent in a three-stage oven at 70°C and 80°C, enter the composite roll and heat the polyethylene film, and then wind up to form a composite semi-finished product; put the above composite semi-finished product in a curing room at 60°C for 60 hours; put the composited The packaging film is cut into roll film with a 1000mm wide slitting machine; the cut roll film is made into a center seal bag or a three side seal bag or other Shaped bag.

[0030] The composite film for pharmaceutical packaging prepared in this example has clear layers, beautiful appearance, pressure resistance, compact composite, no blistering, no rupture, high peel strength, good heat sealing performance, and good tearability and eas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a composite film for medicine packaging, and a making method thereof. The composite film for medicine packaging comprises an aluminum foil layer and a modified polyethylene layer from top to bottom, an aqueous binder is coated between the aluminum foil layer and the polyethylene layer, and the aqueous binder is a polyurethane binder. The making method of the composite film for medicine packaging sequentially comprises the operations of printing, compounding, curing, slitting, and bag making. The composite film for medicine packaging has the advantages of distinct gradation, beauty, pressure resistance, close compounding, no bubbles, no fracture, large peeling strength, good heat sealing performance, easy tearing and easy uncovering.

Description

technical field [0001] The invention belongs to the technical field of medicine packaging, and in particular relates to a composite film for medicine packaging and a preparation method thereof. Background technique [0002] The composite flexible packaging industry began to develop in the middle of the 20th century, and it has increasingly shown its importance in pharmaceutical packaging. This type of composite film consists of substrates, laminating adhesives, barrier materials, heat-sealing materials, printing and protection layer of paint etc. [0003] There are many kinds of medicine package products, and different contents have different requirements for packaging materials. Many medicines require light-shielding, water-blocking, oxygen-blocking, and good formability, especially some medicines require easy tearing, and many directional materials The composite membranes produced, while exhibiting excellent performance in other respects, were deficient in this respect. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B15/085B32B15/20B32B27/06B32B27/32B32B1/02B32B7/12B32B37/06B32B37/12B32B38/00B32B38/14
Inventor 顾锁忠顾锁娟陈祥华王宓刘兴兵
Owner 常州市华健药用包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap