Oil casing pipe coupling composite surface layer and treating method
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composite surface and treatment method technology, applied in the field of oil-casing joint composition and its coating treatment, can solve problems such as environmental protection and environmental pollution, and achieve industrial implementation, high bonding strength, and easy operation Effect
Active Publication Date: 2013-07-31
BAOSHAN IRON & STEEL CO LTD
View PDF6 Cites 9 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, thread grease contains heavy metal powders mainly lead and zinc. These heavy metal powders will cause serious pollution to the environment and cannot meet the requirements of environmental protection.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] 45% polyamideimide (PAI), 12% modified molybdenum disulfide {10% molybdenum disulfide (MoS 2 ), 1.5% γ-aminopropyl triethoxysilane, 0.5% fatty alcohol polyoxyethylene ether (Pingpingjia), this ratio is the percentage of the total mass of the final organic bonding solid lubricating coating, the same below}, 5 % Melamine Cyanurate (MCA), 38% Water. PAI is a water-soluble suspension (20% solid content), the same below.
[0019] Coating process: the pressure of the spray gun is 0.25MPa, and the temperature is kept at 70°C for 0.5 hours in a drying oven, and then raised to 380°C for 1 hour.
[0020] Results: After the above treatment, the bonding strength between the coating and the P110 steel grade was grade 1. It shows that the anti-sticking performance is excellent.
[0023] Coating process: the pressure of the spray gun is 0.25MPa, and the temperature is kept at 80°C for 1 hour in a drying oven, and then raised to 300°C for 1 hour.
[0024] Results: After the above treatment, the bonding strength between the coating and the P110 steel grade was grade 1.
[0027] Coating process: The spray gun pressure is 0.25MPa, and the temperature is kept at 50°C for 1 hour in a drying oven, and then raised to 350°C for 1 hour.
[0028] Results: After the above treatment, the bonding strength between the coating and the P110 steel grade was grade 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention provides an oil casing pipe coupling composite surface layer which comprises a phosphate chemical conversion coating layer directly contacted with the oil casing pipe, as well as an organic bonding solid lubrication coating which is coated on the phosphate chemical conversion coating layer, wherein the coating comprises 20%-45% of PAI Polyamide-imide, 5%-35% of modified molybdenum disulfide, 2%-10% of melamine cyanurate and water. The treating method comprises the steps that after the components are mixed sufficiently and uniformly, the components are sprayed on the phosphate chemical conversion coating layer on the thread surface of an oil casing pipe coupling; all components are placed in a heating device, and heated to the temperature ranging from 50 DEG C to 80 DEG C, and heat preservation is performed for 0.2-1 hour; and then the components are heated to the temperature ranging from 300 DEG C to 380 DEG C, and the heat preservation is performed for 0.5-1hour. According to the oil casing pipe coupling composite surface layer provided by the invention, bumps and spaces of the phosphate chemical conversion coating layer can enhance the bonding strength between the solid lubrication coating and a matrix; and the treating method can control the bonding strength of the coating conveniently, the technology is simple, and the industrialized implementation is facilitated.
Description
technical field [0001] The invention relates to a composition, in particular to a composition for oil casing joints and a coating treatment method thereof. Background technique [0002] Oil and gas exploration and development must use oil and casing products. The casing is threaded to form a casing string to form an oil and gas recovery channel, and the oil pipe is threaded to form a tubing string for oil and gas recovery. It is one of the important performance indicators that the repeated make-up and break-out of the oil casing joint does not cause sticking. Apply thread compound to ensure that no adhesive failure occurs at the joint connection. However, thread grease contains heavy metal powders mainly lead and zinc, which will cause serious pollution to the environment and cannot meet the requirements of environmental protection. In the use of oil and casing products, it is necessary to ensure the non-stick performance of make-up and breakout, and to meet environmental ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more