Novel direct continuous casting slag washing mixed material and preparation process thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of direct slag washing and mixing materials, applied in the field of direct slag washing mixed materials and its preparation, can solve problems such as insufficient refining capacity, and achieve the effects of improving slag composition, strong adsorption of inclusions, and fast melting speed
Inactive Publication Date: 2014-12-31
涟源市飞达冶金炉料厂
View PDF7 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] In my country's iron and steel industry, most of them are small and medium-sized converter iron and steel enterprises, and the casting method is basically based on continuous casting. Some iron and steel enterprises have no refining equipment, and some enterprises have refining equipment but insufficient refining capacity, resulting in no Directly enter the continuous casting process through refining
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0025] The mixed material for direct slag washing in this embodiment is composed of the following components in parts by weight: 5 parts of aluminum powder, 65 parts of alumina powder, 20 parts of quicklime, 6 parts of silicon dioxide powder, and 4 parts of magnesium oxide powder.
[0026] Its preparation process comprises the following steps:
[0027] (1) Ball milling: Weigh the aluminum powder, alumina powder, quicklime, silicon dioxide powder, and magnesium oxide powder in the above proportions with a balance, put them into a ball mill pot respectively, and mill them on a roller ball mill for 20 hours at a speed of 1000r / min. Obtain micron powder;
[0028] (2) Drying: Put the slurry obtained in step 1 into a vacuum drying oven for vacuum drying. The vacuum degree is 0-0.35Pa, and the drying temperature is controlled at 35-100°C for 20 ~54h;
[0029] (3) Mixing: Take the dried micron powder obtained in step 2, except the aluminum powder, weigh the raw materials of each com...
Embodiment 2
[0034] The mixed material for direct slag washing in this embodiment is composed of the following components in parts by weight: 15 parts of aluminum powder, 55 parts of alumina powder, 20 parts of quicklime, 6 parts of silicon dioxide powder, and 4 parts of magnesium oxide powder.
[0035] Its preparation process is with embodiment 1.
Embodiment 3
[0037] The mixed material for direct slag washing in this embodiment is composed of the following components in parts by weight: 25 parts of aluminum powder, 45 parts of alumina powder, 20 parts of quicklime, 6 parts of silicon dioxide powder, and 4 parts of magnesium oxide powder.
[0038] Its preparation process is with embodiment 1.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention relates to a novel direct continuous casting slag washing mixed material and a preparation process thereof, and belongs to the field of special-performance alloy and powder metallurgy novel material in metal materials of the novel materials. The novel heating slag washing mixed material comprises the following components in parts by weight: 30-65 parts of aluminum oxide powder, 30-50 parts of quick lime, 1-6 parts of magnesium oxide powder, 0-6 parts of fluorite and 5-6 parts of silicon dioxide powder. The preparation process of the novel heating slag washing mixed material comprises the following steps of: ball-milling the materials in a ball mill to obtain particle powder; press-moulding the ball-milled particle powder by a ball press, smelting in an electric-arc furnace; and adding 5-40 parts of aluminum powder to the molten liquid during a turning down process, and crushing the cooled material into particles. The novel direct continuous casting slag washing mixed material disclosed by the invention can be used for filtering deoxidized desulfurized molten steel very well, so that produced deoxidation products can be caught effectively and modification of impurities in the steel is promoted, so that the purpose of evolving the molten steel is reached.
Description
Technical field [0001] The present invention involves a straight washing mixed material and its preparation process, which belongs to the special performance alloy and powder metallurgical material field in metal materials in new materials. Background technique [0002] my country's steel production has continued to develop, steel production has increased, and steel varieties and quality have been close to or reached the international advanced level. The steelmaking steelmaking is still the most important steelmaking method in China. In 2008, 540 million tons, the proportion of steelmaking in the furnace increased from about 80%of 1998 to about 90%.The casting technology has also made great progress, and the variety and output of cast steel have continued to increase. The cast -to -cast ratio increased from 68.8%of 1998 to 98.86%in 2008. With the improvement of the Lianfang ratio, the proportion rate also increased significantly. It has made important contributions to the increas...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more