A kind of noise reduction gear grease composition and preparation method thereof

A technology of gear grease and composition, which is applied in the field of noise-reducing gear grease composition and its preparation, and can solve problems such as high noise, low service life, and insufficient lubricating oil function

Inactive Publication Date: 2016-03-23
DONGGUAN VNOVO LUBRICATION TECH
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It solves the problems of severe wear, high noise and low service life of mechanical products caused by insufficient lubricating oil function in the machinery industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The implementation method of the noise reduction gear grease composition of the present invention has the following steps:

[0010] Table 1

[0011] Material composition Specific material composition Metering formula (parts by weight) A Polyalphaolefin, 100cts 100 B Polyisobutylene 650cts 5 C EPDM 8 D Lithium 12-hydroxystearate 10 E Di-tert-butyl-p-cresol 1.5 F Molybdenum dithiophosphate 2

[0012] Add 60 parts by weight of polyalphaolefin, 5 parts by weight of polyisobutylene and 8 parts by weight of binary ethylene propylene rubber into the reaction kettle at the same time, raise the temperature to 100°C while stirring, and keep stirring at a constant temperature of 100°C for 2 hours. The speed of the stirrer is 500~3000rpm, after the binary ethylene propylene rubber is completely melted in the base oil, then add 10 parts by weight of the thickener 12-hydroxylithium stearate, continue stirring, stop heating af...

Embodiment 2

[0014] The implementation method of the noise reduction gear grease composition of the present invention has the following steps:

[0015] Table 2

[0016] Material composition Specific material composition Metering formula (parts by weight) A polyalphaolefin, 100cts 60 B Trimethylolpropane 80cts 40 C EPDM 6 D Lithium 12-hydroxystearate 10 E Dialkyldiphenylamine 1 F Zinc dialkyldithiocarbamate 1

[0017] Add 60 parts by weight of polyalphaolefin and 6 parts by weight of binary ethylene propylene rubber into the reaction kettle at the same time, raise the temperature to 100°C while stirring, and keep stirring at a constant temperature of 100°C for 2 hours. The speed of the stirrer is 500~3000rpm. The ethylene propylene rubber is completely melted in the base oil, then add 10 parts by weight of thickener 12-hydroxy lithium stearate, continue to stir, stop heating after raising the temperature to 210°C, add 40 parts by we...

Embodiment 3

[0019] The present invention produces the lubricating grease composition through above-mentioned secondary example, and its detection result is as shown in table 3 and table 4.

[0020] The experimental conditions in Table 4 are: the power supply voltage of the drive motor of the reduction gearbox is 24V, and the speed is 4500rpm; the casing of the reduction gearbox is made of nylon material, the gear is polyoxymethylene POM, straight teeth, four-stage reduction, and the output speed of the gear is 260rpm. Test the noise at the level of the gearbox and 10cm away from the gearbox.

[0021] table 3

[0022] name Implementation one Implementation two experiment method Cone penetration (1 / 10mm) 290 286 GB / T269-1991 NLGI consistency grade 2 2 DIN 51818-1981 Evaporation loss (100℃, 24h) 0.5 0.6 SH / T0189-1992 Dropping point (°C) 189 194 GB / T3498-2008 Corrosion (99℃, 24h) 1a 1a GB5096-1985

[0023] Table 4

[0024] ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a grease composition and preparation method thereof, especially relates to a noise reduction gear grease composition and preparation method thereof. The grease composition contains base oil, EP rubbers, densifier, anti-oxidant and anti-wear reagent at extreme pressure, and when the base oil amount is 100 parts (by weight), the EP rubbers amount is 2-25 parts (by weight), the densifier amount is 4-20 parts (by weight), and the anti-oxidant is 1-2.5 parts (by weight) and the anti-wear reagent at extreme pressure amount is 1-5 parts (by weight). The purpose of the present invention is to provide a grease composition with excellent noise reduction, shearing resistance, low temperature resistance performances and preparation technology of the grease composition, and the invention solves the problems of severe wearing, large noise, short service life or the like caused by insufficient lubricating oil function in the mechanical industry.

Description

technical field [0001] The invention relates to a lubricating grease composition and a preparation method thereof, in particular to a noise reduction gear lubricating grease composition and a preparation method thereof. Background technique [0002] With the rapid development of industry, various industries have put forward more stringent requirements for product comfort, durability, product quality and other indicators. Especially in the machinery industry, the requirements for parts and components are even higher. Due to the processing error or insufficient assembly precision of the friction parts and accessories of many products, and the improper use of lubricating grease and other factors, it often leads to accelerated wear and excessive noise of mechanical parts. , thus affecting the normal function of mechanical equipment, which in turn affects the quality and final service life of the product. The processing error or assembly precision of parts is closely related to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/00C10N40/04C10N30/06C10N30/00
Inventor 马志宽余丹黄增和
Owner DONGGUAN VNOVO LUBRICATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com