Eureka AIR delivers breakthrough ideas for toughest innovation challenges, trusted by R&D personnel around the world.

Matte wet and unsmooth feeling treating agent for synthetic leather and preparation method of treating agent

A technology for synthetic leather and treatment agent, applied in the field of innovative back-end material and preparation, matte wet astringency treatment agent for synthetic leather and its preparation field, achieving the effect of simple preparation process and increased cost

Inactive Publication Date: 2013-08-21
JIANGSU BAOZE POLYMER MATERIAL
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the original mature and ordinary synthetic leather surface treatment agent can no longer meet the increasing requirements of consumers for beauty and feel, and needs more unique feel to meet the needs of customers.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Under normal temperature and pressure, put 30 parts by weight of modified polyurethane resin, 30 parts by weight of DMF, 30 parts by weight of butyl acetate and 5 parts by weight of silica matting powder into a 1L reactor, stir at room temperature for at least 30 minutes and filter , discard the filter residue; add 4 parts by weight of lanolin, 3 parts by weight of polyoxyethylene ether and 3 parts by weight of castor oil in the obtained mixture, stir at room temperature; then add 2 parts by weight of silicone leveling agent and the remaining 10 parts by weight of the modified polyurethane resin was uniformly stirred at room temperature for at least 30 minutes. When the viscosity is stable, filter and discard the filter residue to obtain a clear, slightly yellowish liquid without precipitation, that is, the finished product of the matte-surface strong permeable wet astringent treatment agent for synthetic leather of the present invention.

[0026] The methods such as st...

Embodiment 2

[0028] Under normal temperature and pressure, put 30 parts by weight of modified polyurethane resin, 25 parts by weight of DMF, 20 parts by weight of butyl acetate and 4 parts by weight of silica matting powder in a 1L reactor, stir at room temperature for at least 30 minutes and then filter , discard the filter residue; add 4 parts by weight of lanolin, 3 parts by weight of polyoxyethylene ether and 3 parts by weight of castor oil in the obtained mixture, stir at room temperature; then add 2 parts by weight of silicone leveling agent and the remaining 10 parts by weight of the modified polyurethane resin was uniformly stirred at room temperature for at least 30 minutes. When the viscosity is stable, filter and discard the filter residue to obtain a clear, slightly yellowish liquid without precipitation, that is, the finished product of the matte-surface strong permeable wet astringent treatment agent for synthetic leather of the present invention.

[0029] The methods such as...

Embodiment 3

[0031] Under normal temperature and pressure, put 20 parts by weight of modified polyurethane resin, 20 parts by weight of DMF, 20 parts by weight of butyl acetate and 4 parts by weight of silica matting powder into a 1L reactor, stir at room temperature for at least 30 minutes and then filter ; Add 1 weight part of lanolin, 1 weight part of polyoxyethylene ether and 1 weight part of castor oil in the mixture of gained, stir at room temperature; Add 1 weight part of silicone leveling agent and remaining modified polyurethane resin again 10 parts by weight, uniformly stirred at room temperature for at least 30 minutes. After the viscosity is stable, filter and discard the filter residue to obtain a clear, slightly yellowish liquid without precipitation, that is, the finished product of the matte wet astringency treatment agent for synthetic leather of the present invention.

[0032] The methods such as stirring and filtration adopted in the above preparation process are convent...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a matte wet and unsmooth feeling treating agent for synthetic leather and a preparation method of the treating agent. The matte wet and unsmooth feeling treating agent for the synthetic leather is formed by the following components: modified polyurethane resin, DMF (Dimethyl Formamide), n-butyl acetate, silicon dioxide extinction powder, wool grease, polyoxyethylene ether, castor oil and an organic silicon flatting agent. Compared with a conventional common matte leather surfactant, the matte wet and unsmooth feeling treating agent for the synthetic leather, disclosed by the invention, can obviously enable the matte extinction effect of the surface of a leather face to be good after treatment of the synthetic leather, so that the leather face has the unique wet and unsmooth wax feeling and the genuine leather effect of the leather face is strong; and the synthetic leather applying the matte wet and unsmooth feeling treating agent has the wet and unsmooth hand feeling and the comprehensive effect is good.

Description

technical field [0001] The invention relates to a surface treatment agent for synthetic leather and a preparation method thereof, in particular to a matte wet astringency treatment agent for synthetic leather used in the back-end process of synthetic leather and a preparation method thereof, belonging to innovative back-end materials and preparation method . Background technique [0002] At present, synthetic leather has been widely used in the production of luggage, clothing, footwear and other products. PU leather has the characteristics of good physical properties, resistance to twists and turns, good softness, high tensile strength, and air permeability. Therefore, PU leather is widely used in the fabrics of footwear or the parts of luggage that bear the weight. The surface of PU leather often needs to use some surface treatment agents to obtain leather with different performance characteristics. [0003] In recent years, as consumers have higher and higher requirement...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M15/564D06M11/79D06M15/53D06M13/224D06M13/50
Inventor 陈勇刚
Owner JIANGSU BAOZE POLYMER MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com