Epoxy resin and polyurethane composite heat transfer printing adhesive and preparation method thereof

A technology of epoxy resin and polyurethane, used in epoxy resin glue, polyurea/polyurethane adhesive, adhesive and other directions, can solve the problem of unsatisfactory properties such as scratch resistance, adhesion, water resistance and high temperature resistance of transfer patterns and other problems, to achieve the effect of improving oxidation resistance, corrosion resistance and weather resistance

Active Publication Date: 2013-09-04
ANHUI YICAI GLASSWARE
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The quality problem of thermal transfer adhesives in the prior art leads to unsatisfactory properties such as scratch resistance, adhesion, water resistance and high temperature resistance of the transfer pattern

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0010] A composite thermal transfer adhesive of epoxy resin and polyurethane, made of the following raw materials in parts by weight (kg): polyurethane resin (KL-540E) 25, E-12 epoxy resin 10, sorbitan fatty acid ester 12 , polyglycerin fatty acid ester 5, epoxidized triglyceride 3, epoxy tetrahydrophthalate dioctyl 3, silane coupling agent KH550 5, ethylene glycol 6, tert-butyl peroxybenzoate 3 , Alkylphenol polyoxyethylene ether 8, antioxidant DLTP1, antioxidant DSTP3, 1-hydroxyethyl-2-oleyl imidazoline 2, HDI trimer 2, propylenediamine 1, acetone 35, xylene 65.

[0011] Include the following steps:

[0012] (1) Put sorbitan fatty acid ester and polyglycerol fatty acid ester into acetone, heat to 70-80°C, then add cumene hydroperoxide, silane coupling agent KH550, ethylene glycol , stirred and reacted for 40-50 minutes, heated to 110-120°C, added epoxy tetrahydrophthalate dioctyl, antioxidant DSTP, 1-hydroxyethyl-2-oleyl imidazoline, stirred and reacted 2- 3 hours;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy resin and polyurethane composite heat transfer printing adhesive. The adhesive is prepared from the following raw materials in parts by weight: 20-25 parts of polyurethane resin (KL-540E), 8-10 parts of E-12 epoxy resin, 10-12 parts of sorbitan fatty acid ester, 5-6 parts of polyglycerol fatty acid ester, 3-5 parts of epoxidized triglyceride, 2-3 parts of epoxy tetrahydrodioctyl phthalate, 5-8 parts of silane coupling agent KH550, 4-6 parts of ethylene glycol, 2-3 parts of tert-butyl peroxybenzoate, 5-8 parts of alkylphenol ethoxylate, 1-2 parts of antioxidant DLTP, 2-3 parts of antioxidant DSTP, 2-3 parts of 1-hydroxyethyl-2-oleic imidazoline, 1-2 parts of HDI tripolymer, 1-2 parts of propane diamine, 35-40 parts of acetone and 60-65 parts of dimethylbenzene. Compared with the prior art, the adhesive has the advantages that the adhesive is firm in bonding and enables the product not to break, shed or yellow easily, and has the effect on improving the product quality. The antioxidants are added in the formula, thus greatly improving the oxidation resistance of the heat transfer pattern and improving the weatherability. 1-hydroxyethyl-2-oleic imidazoline enables the corrosion resistance to be greatly improved.

Description

technical field [0001] The invention relates to a thermal transfer adhesive, which belongs to the field of printing materials. Background technique [0002] Thermal transfer printing is to directly contact the patterned transfer film with the substrate, and the graphic layer on the transfer film is melted and transferred to the substrate. The thermal transfer film includes a carrier layer, a release layer, a protective layer, an ink layer, and an adhesive layer. The coatings are closely related and affect each other. Among them, the bonding layer is the substrate adhesive used to bond the ink information layer and various materials, and must have high adhesion, high temperature resistance, scratch resistance, water resistance, cooking resistance and chemical resistance performance. The quality problem of the thermal transfer adhesive in the prior art leads to unsatisfactory properties such as scratch resistance, adhesion, water resistance and high temperature resistance of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/04C09J163/02C09J11/06
Inventor 朱儒彬张金富
Owner ANHUI YICAI GLASSWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap