Manufacturing method of pearl flash organic glass plate

A technology of plexiglass plate and production method, which is applied in the field of plexiglass production, can solve problems such as high cost, impact on sustainable development, and high price of pearlescent pigments, and achieve the effects of low price, simple production, and wide source

Inactive Publication Date: 2013-09-11
GUANGDONG OCEAN UNIVERSITY
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pearlescent pigments are expensive, and it takes a lot of cost to process them, and pearlescent pigments are non-renewable chemical raw material resources, which have a certain impact on China's sustainable development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] (1) Separation of the nacre: Soak the pearl shells in 3% NaOH solution for 4 days at room temperature. After the horny layer, prismatic layer and nacre of the pearl shells are completely separated, wash the nacre with clean water and dry them;

[0020] (2) Preparation of nacre granules: crush the nacre into particles with a diameter of 1-1.5 mm, then polish and separate them with corn cobs;

[0021] (3) Make pearl glitter plexiglass board:

[0022] A. Preparation of prepolymer: Measure 90mL of MMA (methyl methacrylate), pour it into a 250mL conical flask, add 0.3g of BPO (benzoyl peroxide), stir and dissolve; put the stopper on the conical flask and place it in a constant temperature water bath at 80°C , shake regularly; when the viscosity of the polymerization system is close to that of glycerin, immediately remove the Erlenmeyer flask, cool to room temperature, pour the pearl layer particles in step (2) into the freshly prepared prepolymer, and stir evenly;

[0023]...

Embodiment 2

[0028] (1) Separation of the nacre: Soak the pearl shells in 3% NaOH solution for 4 days at room temperature. After the horny layer, prismatic layer and nacre of the pearl shells are completely separated, wash the nacre with clean water and dry them;

[0029] (2) Preparation of nacre granules: crush the nacre into particles with a diameter of 1-1.5 mm, then polish and separate them with corn cobs;

[0030] (3) Make pearl glitter plexiglass board:

[0031] A. Preparation of prepolymer: Measure 90mL of MMA (methyl methacrylate), pour it into a 250mL conical flask, add 0.3g of BPO (benzoyl peroxide), stir and dissolve; put the stopper on the conical flask and place it in a constant temperature water bath at 85°C , shake regularly; when the viscosity of the polymerization system is close to that of glycerin, immediately remove the Erlenmeyer flask, cool to room temperature, pour the pearl layer particles in step (2) into the freshly prepared prepolymer, and stir evenly;

[0032]...

Embodiment 3

[0037] (1) Separation of the nacre: Soak the pearl shells in 3% NaOH solution for 4 days at room temperature. After the horny layer, prismatic layer and nacre of the pearl shells are completely separated, wash the nacre with clean water and dry them;

[0038] (2) Preparation of nacre granules: mash the nacre into particles with a diameter of 1-1.5 mm, and then polish them with corncobs to separate the nacre granules;

[0039] (3) Make pearl glitter plexiglass board:

[0040] A. Prepolymer preparation: Measure 90mL of MMA (methyl methacrylate), pour it into a 250mL conical flask, add 0.3g of BPO (benzoyl peroxide), stir and dissolve; put the stopper on the conical flask and place it in a constant temperature water bath at 90°C , shake regularly; when the viscosity of the polymerization system is close to that of glycerin, remove the conical flask immediately, cool to room temperature to obtain the prepolymer, and pour the pearl layer particles in step (2) into the prepolymer j...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a manufacturing method of a pearl flash organic glass plate, and belongs to the technical field of organic glass production. The method comprises the following steps of: soaking pearl shells in a NaOH solution at ordinary temperature, washing the pearl layer after completely separating of a horny layer, a prismatic layer and the pearl layer of each pearl shell, drying the pearl layers, and stamping the pearl layers into particles; utilizing a corn cob to polish, pouring the particles of the pearl layers into the prepared prepolymer, uniformly stirring the particles of the pearl layers, pouring into a mould, sealing the mould, putting the particles into a thermostat so as to polymerize, and demoulding the particles so as to obtain the product. A pearl flash organic glass plate is poured by the particles of the pearl layers, the particles of the pearl layers have nacreous luster, the organic glass plate has brilliant rays under illumination, compared with other chemical materials, the color is natural and intensive, and cheerful enjoyment is provided for the people in vision; a raw material is extracted from the waste pearl shells, the source is wide, the price is low, the manufacture is simple and convenient, and the raw material belongs to a green environment-friendly material.

Description

technical field [0001] The invention relates to a method for making a pearl glitter organic glass plate, belonging to the technical field of organic glass production. Background technique [0002] There are currently four types of plexiglass: colorless, colored, pearlescent, and embossed plexiglass. Among them, pearlescent plexiglass is cast by adding pearlescent powder or fluorescent powder to ordinary plexiglass, which has a unique artistic effect. However, pearlescent pigments are expensive, and the treatment will cost a lot, and pearlescent pigments are non-renewable chemical raw material resources, which have a certain impact on China's sustainable development. [0003] Pearl flash plexiglass board is made of nacre particles, which have pearly luster, and can emit the unique light of pearls and natural bright iridescence under the light. Compared with other chemical materials, the color is more natural and richer, giving people A visual delight. And its raw material ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L33/12C08K3/26C08F120/14
Inventor 刘志刚黄苑媚郑树城陈家锋关静张罗忠
Owner GUANGDONG OCEAN UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap