Nano-composite environment-friendly water permeable brick and production method thereof

A nano-composite and production method technology, applied in the field of building materials, can solve problems such as affecting the beauty of urban roads, permeable bricks are easy to seep, not easy to remove, etc., and achieve the effects of reducing urban waste, low cost and reducing pressure.

Inactive Publication Date: 2013-09-11
CHINA STATE CONSTR HAILONG TECH CO LTD
View PDF7 Cites 55 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Permeable bricks made of ceramic or concrete are easy to seep, and the stains are not easy to remove, which greatly affects the appearance of urban roads

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0057] The preparation method of the mortar material is as follows: weighing each raw material according to the mass fraction of each raw material of the mortar surface layer; 2 Add water reducing agent and water reducing agent into the water, and stir evenly; then add the pre-mixed mixture of sand and cement, and stir to obtain the mortar material. The sand and cement are mixed in advance to facilitate their uniform mixing in the mortar material to form a mortar material with high uniformity.

[0058] The preparation method of concrete materials is as follows: weigh each raw material according to the mass fraction of each raw material at the bottom of the concrete; pour sand, recycled aggregate, natural aggregate and 70% water into a mixer, and stir evenly; then pour in cement and pulverized coal ash, and stir evenly; then add the remaining water for gelatinization and stirring; finally add a water reducing agent and stir evenly to obtain concrete materials.

[0059] S2. Loa...

Embodiment 1

[0064] The nano-composite environmentally friendly permeable brick includes a concrete bottom layer and a mortar surface layer arranged on the concrete bottom layer, and the concrete bottom layer and the mortar surface layer are combined to form an integrated structure. The ratio of the thickness of the mortar surface layer to the concrete bottom layer is 1:5.

[0065] The concrete bottom layer is made of the following raw materials by mass: 32 parts of cement, 15.2 parts of water, 8 parts of fly ash, 58.8 parts of recycled aggregates, 58.8 parts of natural coarse aggregates, 75.2 parts of sand and 0.15 parts of water reducing agent. Among them, the cement is preferably China Resources P·O42.5 grade cement. The fly ash is preferably Class II fly ash, with a loss on ignition of 5.4%, a fineness of 20.3% and a moisture content of 0.65%. The recycled aggregate selects waste concrete blocks with a particle size of 5-10mm. The natural coarse aggregate is crushed stone with a part...

Embodiment 2

[0075] The nano-composite environmental protection permeable brick includes a concrete bottom layer and a mortar surface layer arranged on the concrete bottom layer, and the concrete bottom layer and the mortar surface layer are combined to form an integrated structure. The ratio of the thickness of the mortar surface layer to the concrete bottom layer is 1:3.

[0076] The concrete bottom layer is made of the following raw materials by mass: 20 parts of cement, 10 parts of water, 5 parts of fly ash, 50 parts of recycled aggregate, 50 parts of natural coarse aggregate, 65 parts of sand and 0.05 part of water reducing agent. Among them, the cement is preferably China Resources P·O42.5 grade cement. The fly ash is preferably Class II fly ash, with a loss on ignition of 5.4%, a fineness of 20.3% and a moisture content of 0.65%. The recycled aggregate selects waste concrete blocks with a particle size of 10-15mm. The natural coarse aggregate is crushed stone with a particle size ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-composite environment-friendly water permeable brick and a production method thereof. The nano-composite environment-friendly water permeable brick comprises a concrete bottom layer and a mortar surface layer arranged on the concrete bottom layer, wherein the concrete bottom layer and the mortar surface layer are compounded to form an integrated structure; the concrete bottom layer is prepared from the following raw materials in parts by weight: 20-40 parts of cement, 10-20 parts of water, 5-15 parts of fly ash, 50-65 parts of recycled aggregate, 50-65 parts of natural coarse aggregate, 65-85 parts of sand and 0.05-0.2 part of water-reducing agent; and the mortar surface layer is prepared from the following raw materials in parts by weight: 70-100 parts of cement, 5-20 parts of nano-TiO2, 30-60 parts of water, 200-400 parts of sand and 0.1-1.0 part of water-reducing agent. The nano-composite environment-friendly water permeable brick disclosed by the invention is integrally formed and has the advantages of high compressive strength, high flexural strength, good water permeability and good water retention, and a ground surface laid by the nano-composite environment-friendly water permeable bricks can timely dredge and drain rainwater, is conductive to growth of surrounding vegetation and can effectively supplement groundwater, reduce the pressure of a municipal drainage system and reduce the influence of surface gathered water on the traffic; and the nano-composite environment-friendly water permeable brick has a photocatalytic self-cleaning function and can decompose and remove organic stains on the surface of the brick and beautify the urban environment.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a nano-composite environment-friendly permeable brick and a production method thereof. Background technique [0002] Most of the raw materials used in traditional concrete pavement bricks are natural aggregates, and natural aggregates are not inexhaustible. Large-scale mining of natural aggregates will lead to a lack of rock resources and damage to the environment. At present, the ground of city squares, commercial streets, sidewalks, community activity places and other occasions are mainly paved with materials with low water permeability such as granite, marble ceramic tiles, etc. The ground made of these materials with low water permeability is impermeable to water , it will increase the burden of urban drainage facilities and affect the health of urban vegetation; and when it rains, rainwater cannot directly penetrate into the ground, resulting in ground water and m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C5/06C04B28/00B28B1/08B28B11/24
Inventor 杨卫东施汉盛张宗军刘新伟薛建新周光星
Owner CHINA STATE CONSTR HAILONG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More