Cathode electrophoresis paint with combined bottom surfaces and preparation method and application method thereof
A cathodic electrophoretic coating, bottom surface technology, applied in electrophoretic coatings, polyurea/polyurethane coatings, coatings, etc., can solve problems such as technical difficulties and no mature products.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0039] Example one
[0040] A preparation method of cathode electrophoretic paint with one bottom surface, including the following steps:
[0041] (1) Preparation of curing agent
[0042] It is prepared by mixing trimethylolpropane and alcohol ether solvents and heating, adding isocyanate dropwise before the temperature reaches 60°C, and then holding it at 60°C for 1 hour, then heating to 70°C, and holding it at 70°C for 2 hours. Curing agent, wherein the molar ratio of isocyanate, alcohol ether solvent and trimethylolpropane is 2:1:1;
[0043] (2) Preparation of main resin
[0044] (1) Take a low molecular weight epoxy resin with a molar ratio of 7:4:1, bisphenol A and isooctanoic acid to react at 120°C for 3 hours to prepare a medium molecular weight epoxy resin with a resin average molecular weight of 1000;
[0045] (2) Take the middle molecular weight epoxy resin, N-methylethanolamine and ketimine with a molar ratio of 4:4:1 under the conditions of 110°C for a reaction time of 2 hou...
Example Embodiment
[0075] Example 2
[0076] A preparation method of cathode electrophoretic paint with one bottom surface, including the following steps:
[0077] (1) Preparation of curing agent
[0078] It is prepared by mixing trimethylolpropane and alcohol ether solvents and heating, adding isocyanate dropwise before the temperature reaches 60°C, then keeping it at 60°C for 2 hours, heating it to 70°C, and keeping it at 70°C for 2 hours. Curing agent, wherein the molar ratio of isocyanate, alcohol ether solvent and trimethylolpropane is 2.5:2:1.5;
[0079] (2) Preparation of main resin
[0080] (1) Take a low molecular weight epoxy resin with a molar ratio of 9:4:1, bisphenol A and isooctanoic acid to react at 130°C for 4 hours to prepare a medium molecular weight epoxy resin with a resin average molecular weight of 2000;
[0081] (2) Take the medium molecular weight epoxy resin, N-methylethanolamine and ketimine with a molar ratio of 5:5:1 and react at 20°C for 3 hours to prepare the main resin;
[...
Example Embodiment
[0102] Example three
[0103] A preparation method of cathode electrophoretic paint with one bottom surface, including the following steps:
[0104] (1) Preparation of curing agent
[0105] It is prepared by mixing trimethylolpropane and alcohol ether solvents and heating, adding isocyanate dropwise before the temperature reaches 60°C, and then holding at 60°C for 1.5 hours, then heating to 70°C, and holding at 70°C for 2 hours. Curing agent, wherein the molar ratio of isocyanate, alcohol ether solvent and trimethylolpropane is 2.3:1.5:1.2;
[0106] (2) Preparation of main resin
[0107] (1) A low molecular weight epoxy resin with a molar ratio of 8:4:1, bisphenol A and isooctanoic acid were reacted at 125°C for 3.5 hours to prepare a medium molecular weight epoxy resin with a resin average molecular weight of 1500;
[0108] (2) Take the middle molecular weight epoxy resin, N-methylethanolamine and ketimine with a molar ratio of 4.5:4.6:1 at 115°C for a reaction time of 2.5 hours to pre...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Fineness | aaaaa | aaaaa |
Coulombic efficiency | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap