Aging-resistant PPO (Polyphenylene Oxide) - PPS (Polyphenylene Sulfite) plastic alloy

A PPO-PPS, plastic alloy technology, applied in the field of plastic alloys, can solve the problems of poor anti-aging performance and achieve excellent thermal aging performance

Inactive Publication Date: 2013-10-16
浙江丞达新材料科技有限公司
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the current PPO-PPS plastic alloys have poor aging resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Each raw material was weighed according to the data corresponding to Example 1 in Table 1. Add each component into a high-speed mixer, control the speed at 350 rpm at room temperature, mix for 8 minutes, take it out and transfer it to a screw extruder, extrude and granulate at a temperature of 300°C to obtain anti-aging PPO- PPS plastic alloy.

[0021] Table 1: Anti-aging PPO-PPS plastic alloy formula table Unit: kg

[0022]

Example 1

Example 2

Example 3

Example 4

PPO resin

100

100

100

100

PPS resin

50

50

50

50

Compatibilizer ABS-g-MAH

6

6

6

6

4,4'-Thiobis(6-tert-butyl-3-methylphenol)

0.4

0.8

/

0.5

1,1,3-tris(2-methyl-4-hydroxy-5-tert-butylphenyl)butane

0.4

/

0.8

0.5

Dioctadecyl Thiodipropionate

0.2

0.2

0.2

/

[0023] The PPS resin is selected from the PPS resin of Japan Toray Company brand A503;

...

Embodiment 2-4

[0026] Each raw material was weighed according to the data corresponding to Examples 2-4 in Table 1. The method described in Example 1 was used to prepare the anti-aging PPO-PPS plastic alloy.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aging-resistant PPO-PPS plastic alloy, which is composed of the following components in weight part: 100 parts of PPO, 40-60 parts of PPS, 4-8 parts of compatibilizer and 0.5-1.5 parts of age resister. The aging-resistant PPO-PPS plastic alloy disclosed by the invention is an alloy material with excellent overall performances, mostly retains the advantages of PPS in respects of mechanical property, thermal tolerance, flame retardance and the like, and integrates excellent electrical performances of PPO. The aging-resistant PPO-PPS plastic alloy is suitable for fields of electric appliances such as thermotolerant breaker frameworks and electric appliance connectors.

Description

technical field [0001] The invention relates to a plastic alloy, in particular to an anti-aging PPO-PPS plastic alloy. Background technique [0002] Polyphenylene oxide, referred to as PPO, English name: Polyphenylene Oxide, is one of the world's five general-purpose engineering plastics. It has the advantages of high rigidity, high heat resistance, flame retardant, high strength and excellent electrical properties. In addition, polyphenylene ether also has the advantages of wear resistance, non-toxicity, and pollution resistance. The dielectric constant and dielectric loss of PPO are one of the smallest varieties among engineering plastics, and they are hardly affected by temperature and humidity, and can be used in low, medium and high frequency fields. The load deflection temperature of PPO can reach above 190°C, and the embrittlement temperature is -170°C. As one of the world's top five general-purpose engineering plastics, PPO material is non-toxic and has a low rela...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L71/12C08L81/02C08K5/375C08K5/13C08K5/372
Inventor 黄美蓉
Owner 浙江丞达新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com