A method for preparing solar cell silver wire grid electrodes based on photolithographic mask method and liquid phase method

Abstract

The invention discloses a method for preparing a solar battery silver wire grid electrode based on a photolithography mask method and a liquid phase method. The method includes the following steps: (1) Spin-coating photoresist template to uniformly spin-coat the photoresist on the surface of the silicon substrate, after exposure, development, film hardening and other steps, copy the specific pattern designed on the mask plate to On the silicon substrate; (2) chemical method deposits Ag particles and deposits Ag particles on the photoresist template by the method of electrochemical reaction; (3) removes photoresist template and removes photoresist with photoresist film remover; ( 4) Annealing and sintering The closely arranged Ag particles are heated at a high temperature and connected to each other to form Ag electrodes. The micron-sized silver electrode prepared by the method has excellent electrical conductivity and low reflectivity, and the preparation process is simple and the resource consumption is low. It is not only a favorable substitute for screen-printed electrodes, but also can improve the efficiency of solar cells and reduce costs.

Description

technical field [0001] The invention belongs to the technical fields of photovoltaic application and touch display, and in particular relates to a method for preparing a silver wire grid electrode of a solar cell based on a photolithography mask method and a liquid phase method. Background technique [0002] Solar energy is an inexhaustible clean energy. With the depletion of non-renewable energy sources such as coal and oil, the research, development and utilization of solar cells are undoubtedly the current hot spots. Improving the photoelectric conversion efficiency of solar cells and reducing the preparation cost are the directions of research and development of solar cells. The transparent conductive front electrode is one of the important components in solar cells, which directly affects the fill factor and short-circuit current of the cell device, and then affects the photoelectric conversion efficiency of the cell. Generally speaking, a transparent conductive elect...

AI Technical Summary

Problems solved by technology

However, this large-scale grid line electrode has a significant shadow effect on the front surface of the battery, increasing the reflectance of the front surface to incident light (~15% of the total surface reflectance); and these grid lines are very large. To obtain better conductivity, the emitter on the surface of the battery is heavily doped with n++, resulting in a significant increase in the recombination probability of the surface emitter carrier, reducing the short-wave absorption rate of the battery, thereby reducing the performance of the entire emitter and the efficiency of the battery

The upper limit of the theoretical efficiency of monocrystalline silicon solar cells reaches ~33%, while the average efficiency of existing industrialized cells is about 16-20%. Traditional grid electrodes and their existing processes are one of the sources of efficiency differences.

In addition, its expensive preparation methods (screen printing, ion beam and electron beam etching, etc.) also greatly increase the cost of the battery

Images