A kind of storage medium material and its preparation method and data storage method

A storage medium and data technology, applied in the field of storage medium materials and their preparation, can solve the problems of increased use cost, large energy consumption, unfavorable environmental protection, etc.

Inactive Publication Date: 2016-06-08
THE NAT CENT FOR NANOSCI & TECH NCNST OF CHINA
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the pitch of the recording points is too close (storage density close to 1Tbit / inch 2 ), the adjacent erasing effect will appear, that is, when a data point is recorded with a high-temperature probe, the original data points around it will be eliminated due to heat radiation or heat conduction
In addition, when erasing and writing phase-change materials, the needle tip is often required to rise to a very high temperature (about 600°C), and the heat conducted to the tip of the needle tip accounts for less than 1% of the heat of the entire microprobe, which makes energy consumption very high. Large, increases the cost of use and is not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of storage medium material and its preparation method and data storage method
  • A kind of storage medium material and its preparation method and data storage method
  • A kind of storage medium material and its preparation method and data storage method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The preparation method of the storage medium material provided by the invention comprises sequentially forming a polymer layer and a graphite layer on a substrate, and the thickness of the graphite layer is not more than 10 nanometers, preferably 0.35-2 nanometers.

[0025] According to the present invention, the method for forming the polymer layer may be various existing methods, for example, may include coating a solution containing a polymer on a substrate and drying it. Generally speaking, the concentration of the polymer-containing solution can be 1-10% by volume, so that the solution can be more uniformly coated on the substrate. The polymer is used in an amount such that the thickness of the polymer layer is preferably 0.05-1 micron. The method of coating the solution containing the polymer on the substrate is well known to those skilled in the art, for example, methods such as spray coating, spin coating, flow coating, brush coating, and dipping can be used to ...

preparation example 1

[0040] This preparation example is used to illustrate the storage medium material and its preparation method provided by the present invention.

[0041] A silicon wafer with a thickness of 0.3 mm and a nano-level flat surface (purchased from SQI company, full name SiliconQuest International, Inc, the same below) was soaked in acetone, ethanol and deionized water for 10 minutes and ultrasonically cleaned for 10 minutes, wherein the ultrasonic frequency was 20kHz, ultrasonic power is 800W. Spin-coat an acetone solution of polystyrene (Young's modulus 3GPa) with a concentration of 1% by volume on the treated substrate at a rotation speed of 800rpm, and dry at 150°C for 15 minutes to obtain a thickness of 0.05 Micron polymer layer. Use scotch tape to evenly stick the graphite powder, and stick the graphite powder side of the scotch tape to the polymer layer closely, remove the scotch tape, and use Raman spectroscopy to find a thickness of 0.35 nanometers on the polymer layer gra...

preparation example 2

[0043] This preparation example is used to illustrate the storage medium material and its preparation method provided by the present invention.

[0044] A silicon nitride wafer (purchased from SQI company, full name SiliconQuest International, Inc) with a thickness of 1 mm and a nano-level flat surface was soaked in acetone, ethanol and deionized water for 10 minutes, and ultrasonic cleaning was performed for 10 minutes, wherein the ultrasonic frequency was 20KHz , Ultrasonic power is 800W. Concentration is 10 volume % polymethyl methacrylate (Young's modulus is 4GPa) acetone solution is spin-coated on the treated substrate, the rotating speed of spin-coating is 800rpm, and at 150 ℃, dry 15 minutes, obtain Polymer layer with a thickness of 1 micron. Use scotch tape to evenly stick the graphite powder, and stick the graphite powder side of the scotch tape to the polymer layer closely, remove the scotch tape, and use Raman spectroscopy to find a thickness of 2 nanometers on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a storage medium material, a preparation method of the storage medium material, and a data storage method. The storage medium material comprises a substrate, a polymer layer and a graphite layer which are sequentially laminated, wherein the thickness of the graphite layer is not more than 10 nanometers. When the storage medium material provided by the invention is used for data storage, data with high storage density and high quality can be acquired, the wear to the point of a needle can be effectively reduced, and a polymer material can be prevented from turning outwards.

Description

technical field [0001] The invention relates to a storage medium material, a preparation method thereof and a data storage method. Background technique [0002] With the development of science and technology and the explosive growth of people's demand for information, it has become an inevitable trend for the size of electronic and optical devices to develop to the nanometer level. In recent years, researchers have done a lot of research on micro- and nano-precision processing methods and storage medium materials. Among them, the surface ultra-high density storage technology is mainly based on the maskless processing method of mechanical probes (such as atomic force microprobe ), which can effectively change the surface morphology, crystal structure or optical and electrical properties of a specific storage medium material at the nanoscale, is considered to be one of the powerful means to achieve high-density information storage. Studies have shown that finding a suitable s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G11C13/02
Inventor 王锐王圣楠王小伟裘晓辉
Owner THE NAT CENT FOR NANOSCI & TECH NCNST OF CHINA