Bituminous concrete crack self-healing microcapsule and preparation method of same

A technology of asphalt concrete and microcapsules, which is applied in the field of asphalt concrete crack repair, can solve the problems of low effect, difficult hollow fiber manufacturing process, and high cost, and achieve the effects of asphalt self-healing and ability improvement, simple preparation method, and low cost

Inactive Publication Date: 2013-11-20
杨林江
View PDF4 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Adding lime powder can improve the self-healing and performance of asphalt mixture, but the effect is very small; when adding hollow fibers in the asphalt mixture mixing process, when cracks appear on the road surface, the fibers will break and the healing agent inside will be released to achieve The purpose of repairing, but this method has many disadvantages. First, during the mixing process of asphalt mixture, the fibers are easy to break, and the healing agent inside is released in advance, and the purpose of healing cannot be achieved; secondly, the fiber radius is too small. , the hollow fiber manufacturing process is extremely difficult and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bituminous concrete crack self-healing microcapsule and preparation method of same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] In order to deepen the understanding of the present invention, the present invention will be further described below in conjunction with examples, which are only used to explain the present invention, and do not constitute a limitation to the protection scope of the present invention.

[0020] Under normal temperature, quality is silane coupling agent 16g, modified aliphatic amine curing agent 65g, curing accelerator 2,4,6-tris(dimethylaminomethyl)phenol 19g, epoxy resin is the raw material reagent of 300g weighing Measure and reserve. Pre-mix the coupling agent, curing agent, and curing accelerator in the reactor, and after 3600 r min -1 The high-speed shear emulsifier emulsifies evenly, and under ultrasonic vibration until the three components are completely dissolved to obtain a uniform and stable emulsion; under stirring conditions, add film-forming substance epoxy resin to the emulsion, and obtain a suspension through internal phase volatilization; the suspension ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a bituminous concrete crack self-healing microcapsule and a preparation method of the same. The bituminous concrete crack self-healing microcapsule is composed of epoxy resin film forming matter and repairing liquid, and the weight ratio of the film forming matter to the repairing liquid is 3:1, wherein the repairing liquid is composed of 10-20% of coupling agent, 50-75% of curing agent and 18-30% of curing accelerator by weight. The preparation method of the microcapsule comprises the following steps of: orderly adding the coupling agent, curing agent and curing accelerator into a reaction kettle, stirring evenly by a high-speed shearing emulsifying machine, adding the film forming matter, namely the epoxy resin, and by means of internal phase vaporization, suspension centrifuging, washing and drying, thus obtaining the microcapsule product. The microcapsule provided by the invention can obviously enhance the bitumen self-healing capability and prolong the service life of pavement.

Description

Technical field: [0001] The invention relates to the field of asphalt concrete crack repair, in particular to a self-healing asphalt concrete crack, microcapsules and a preparation method. Background technique: [0002] Fatigue cracking is one of the main problems in the application of asphalt pavement. The fatigue damage of asphalt concrete can be attributed to the initiation and propagation of internal cracks in asphalt concrete under repeated loads. The crack initiation and propagation process is accompanied by stress relaxation in the crack area and for Reducing the interface self-healing and crack surface energy to proceed spontaneously. However, if these cracks or damages cannot be repaired and dealt with in a timely and effective manner, it will not only affect the normal performance and service life of the asphalt concrete structure, but also may cause macroscopic cracks and lead to structural brittle fractures, eventually resulting in serious disasters sex accident...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L63/00C08K5/54C08G59/50C04B24/28
Inventor 杨林江
Owner 杨林江
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap