Regeneration method for honeycomb type SCR (Selective Catalytic Reduction) denitration catalyst

A technology of SCR catalyst and denitrification catalyst, which is applied in the field of regeneration of honeycomb SCR denitrification catalyst, can solve the problems of increasing regeneration cost, adjusting load capacity, increasing regeneration cost, etc., and achieves reducing regeneration cost, simplifying regeneration process, and good solubility Effect

Inactive Publication Date: 2013-12-11
HUANENG POWER INT INC +3
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above regeneration idea can effectively restore the denitrification activity of the poisoned catalyst, there are the following problems in engineering application: the solubility of the commonly used active substance precursor ammonium metavanadate in water is very small (5g / L, 20℃), so it is very difficult to It is difficult to adjust the loading amount (supplementary amount) on the SCR catalyst by controlling the concentration of the solution, but it can only be adjusted by repeated "dipping-drying" process, which has been reported in patent CN101574671 and patent CN102114422, which not only increases The process operation is cumbersome and increases the cost of regeneration; at the same time, another commonly used active material precursor, ammonium metatungstate, has a high price and is the main factor affecting the production cost of SCR catalysts. If it is used in catalyst regeneration, it will increase high regeneration cost
In short, the above problems can lead to high catalyst regeneration costs, which is not conducive to the engineering application of regeneration technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for regenerating a honeycomb SCR denitration catalyst, comprising the following steps:

[0021] 1) Immerse the poisoned honeycomb SCR catalyst in 500ml of dilute sulfuric acid solution with a mass concentration of 1%, take it out after being treated for 1.5h under the action of 40KHZ ultrasonic waves, put it in an oven, and dry it at 110°C for 4h;

[0022] 2) Immerse the honeycomb SCR catalyst treated in step 1) in 0.3 mol / L cerium nitrate aqueous solution for 3 hours and take it out;

[0023] 3) Roast the honeycomb SCR catalyst treated in step 2), heat up to 110°C at a rate not greater than 3°C / min, keep it warm for 4 hours, and then heat up to 300°C at a rate not greater than 3°C / min, Insulate for 8 hours to obtain a regenerated honeycomb SCR denitration catalyst.

[0024] The poisoned honeycomb SCR catalyst and the regenerated honeycomb SCR catalyst were respectively placed in the SCR denitration activity test device, and the denitration efficiency was test...

Embodiment 2

[0026] A method for regenerating a honeycomb SCR denitration catalyst, comprising the following steps:

[0027] 1) Immerse the poisoned honeycomb SCR catalyst in 500ml of dilute sulfuric acid solution with a mass concentration of 1%, take it out after being treated for 1h under the action of 50KHZ ultrasonic waves, put it in an oven, and dry it at 100°C for 6h;

[0028] 2) Immerse the honeycomb SCR catalyst treated in step 1) in 0.6 mol / L cerium nitrate aqueous solution for 2 hours and take it out;

[0029] 3) Roast the honeycomb SCR catalyst treated in step 2, heat up to 110°C at a rate not greater than 3°C / min, keep it warm for 3 hours, and then heat up to 300°C at a rate not greater than 3°C / min, Insulate for 9 hours to obtain a regenerated honeycomb SCR denitration catalyst.

[0030] The poisoned honeycomb SCR catalyst and the regenerated honeycomb SCR catalyst were respectively placed in the SCR denitration activity test device, and the denitration efficiency was tested ...

Embodiment 3

[0032] A method for regenerating a honeycomb SCR denitration catalyst, comprising the following steps:

[0033] 1) Immerse the poisoned honeycomb SCR catalyst in 500ml of dilute sulfuric acid solution with a mass concentration of 2%, take it out after being treated for 0.5h under the action of 60KHZ ultrasonic waves, put it in an oven, and dry it at 120°C for 3h;

[0034] 2) Immerse the honeycomb SCR catalyst treated in step 1) in 0.9 mol / L cerium nitrate aqueous solution for 1 hour and take it out;

[0035] 3) Roast the honeycomb SCR catalyst treated in step 2), heat up to 110°C at a rate not greater than 3°C / min, keep it warm for 5 hours, and then heat up to 300°C at a rate not greater than 3°C / min, Insulate for 10 hours to obtain a regenerated honeycomb SCR denitration catalyst.

[0036]The poisoned honeycomb SCR catalyst and the regenerated honeycomb SCR catalyst were respectively placed in the SCR denitration activity test device, and the denitration efficiency was teste...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a regeneration method for a honeycomb type SCR (Selective Catalytic Reduction) denitration catalyst, and belongs to the technical field of power environment protection. The regeneration method comprises the following steps: 1) dipping a poisoned honeycomb type SCR catalyst into a diluted sulfuric acid solution, carrying out ultrasonic treatment, then taking out and drying; 2) putting the honeycomb type SCR catalyst treated in the step 1 into a cerous nitrate solution, dipping for 1-3 hours and then taking out; 3) roasting the honeycomb type SCR catalyst treated in the step 2, raising the temperature to be 110 DEG C at the speed of no greater than 3 DEG C / min, subsequently preserving the temperature for 3-5 hours, furthermore, raising the temperature to be 300 DEG C at the speed of no greater than 3 DEG C / min, and preserving the temperature for 8-10 hours to obtain the regenerated honeycomb type SCR denitration catalyst. The active precusor substance cerous nitrate used in the regeneration method is wide in source and good in solvability; the activity of the catalyst subjected to regeneration treatment can be recovered to be more than 80% as compared with the activity of the catalyst which is not poisoned; meanwhile, the regeneration process is simplified, the regeneration cost is lowered, and the regeneration method is simple and convenient to operate, environment-friendly and applicable to large-scale industrial production and application.

Description

technical field [0001] The invention belongs to the technical field of electric power environmental protection, and relates to a regeneration method of a denitration catalyst, in particular to a regeneration method of a honeycomb SCR denitration catalyst. Background technique [0002] Nitrogen oxide (NOx) emission control of coal-fired power plants is a key task in the field of energy conservation and environmental protection during the country's "Twelfth Five-Year Plan". The most stringent control standard (100mg / m3) in the world has been formulated. With the promulgation of these national policies, how to effectively control NOx emissions has become one of the important issues to be solved in the field of power environmental protection. [0003] At present, the flue gas denitrification (DeNOx) of coal-fired power stations mainly adopts the selective catalytic reduction (SCR) technology, which uses ammonia as the reducing agent and uses the SCR catalyst to reduce the NOx i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J38/64B01J23/30
Inventor 程广文张强张发捷徐晓涛杨世极舒凯
Owner HUANENG POWER INT INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products