Alkali-resistant glass fiber jet yarn sizing

A technology of alkali-resistant glass fiber and sizing agent, which is applied in the field of glass fiber surface treatment agent, can solve the problems of poor sizing agent clustering, low stiffness, and weak bonding between fibers and fibers, and achieves good clustering, good chopped sexual effect

Active Publication Date: 2015-08-19
陕西汇友友基新材料有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0010] (1) The sizing protective layer coated on the surface of the glass fiber has poor textile resistance and is prone to hairiness when unwinding and plying;
[0011] (2) The sizing agent coated on the surface of the glass fiber has poor clustering property, the bonding between the fibers is not strong, and it is easy to open the fibers when spraying under pressure, which affects the uniformity of dispersion;
[0012] (3) The stiffness is low, which affects the short-cut dispersion of fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] (1) Add 1 kg of 80-90 ℃ deionized water to 0.1 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir to a uniform transparent liquid;

[0043] (2) Add 0.1 kg of 30-50 ℃ deionized water to 0.05 kg of antistatic agent SN, and stir to a uniform transparent liquid;

[0044] (3) in 0.1 kilogram of lithium nitrate and 1 kilogram of lithium nitrate lithium chloride mixture, add 3 kilograms of 50-70 ℃ deionized water, stir to uniform transparent liquid;

[0045] (4) add 6 kilograms of deionized water to 3.0 kilograms of modified polyacrylate film-forming agent YG111 (produced by Xi'an Youji Composite Materials Co., Ltd.);

[0046] To 4.0 kilograms of water-soluble epoxy film former YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.), add 4 kilograms of deionized water;

[0047] To 4.0 kilograms of polyvinyl acetate and acrylate copolymer film former YG2016 (produced by Xi'an Anyouji Composite Materials Co....

Embodiment 2

[0052] (1) Add 3.0 kg of 80-90 ℃ deionized water to 0.3 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir to a uniform transparent liquid;

[0053] (2) Add 1.5 kg of 30-50 ℃ deionized water to 0.15 kg of antistatic agent SN, and stir to a uniform transparent liquid;

[0054] (3) in the mixture of 0.1 kilogram of lithium nitrate, 0.1 kilogram of lithium chloride and 0.1 kilogram of ammonium chloride, add 4.5 kilograms of 50-70 ℃ deionized water, stir to uniform transparent liquid;

[0055] (4) 13.5 kilograms of deionized water were added to 4.5 kilograms of modified polyacrylate film-forming agent YG111 (produced by Xi'an Youji Composite Materials Co., Ltd.);

[0056] Add 8.0 kg of deionized water to 4.0 kg of water-soluble epoxy film-forming agent YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.);

[0057] Add 11.0 kilograms of deionized water to 5.5 kilograms of polyvinyl acetate and acrylate copol...

Embodiment 3

[0062] (1) Add 4.0 kg of 80-90 ℃ deionized water to 0.4 kg of imidazoline cationic lubricant ZB09 (produced by Xi'an Zhongchuang Composite Materials Co., Ltd.), and stir to a uniform transparent liquid;

[0063] (2) Add 2.5 kg of 30-50 ℃ deionized water to 0.25 kg of antistatic agent SN, and stir to a uniform transparent liquid;

[0064] (3) add 4.5 kilograms of 50-70 ℃ deionized water to 0.25 kilograms of lithium nitrate, 0.1 kilograms of lithium chloride and 0.1 kilograms of ammonium chloride, and stir to a uniform transparent liquid;

[0065] (4) 14.0 kilograms of deionized water were added to 7.0 kilograms of modified polyacrylate film-forming agent YG111 (produced by Xi'an Youji Composite Materials Co., Ltd.);

[0066] Add 10.0 kg of deionized water to 5.0 kg of water-soluble epoxy film-forming agent YG801 (produced by Xi'an Anyouji Composite Materials Co., Ltd.);

[0067] Add 14.0 kilograms of deionized water to 7.0 kilograms of polyvinyl acetate and acrylate copolymer ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a glass fibre surface treating agent containing an inorganic material. An alkali-resistant glass fibre jet yarn impregnating compound disclosed by the invention comprises a film-forming agent, a lubricating agent, an antistatic agent and water, wherein the film-forming agent is a mixture of a polyacrylate film-forming agent, a water-soluble epoxy film-forming agent, polyvinyl acetate and an acrylate copolymer film-forming agent; and the mass ratio of the polyacrylate film-forming agent to the water-soluble epoxy film-forming agent to the polyvinyl acetate and to the acrylate copolymer film-forming agent is (3.0-10.0): (2.0-9.0):(4.0-10.0). By adopting the alkali-resistant glass fibre jet yarn impregnating compound disclosed by the invention, the alkali-resistant glass fibre jet yarn has good bundling property, lubricating property, and spinning property in the processing process; and the alkali-resistant glass fibre jet yarn has good choppability, dispersibility and antistatic property in the technical process of a reinforced cement product.

Description

technical field [0001] The present invention relates to a glass fiber surface treatment agent containing organic materials. Background technique [0002] The alkali-resistant glass fiber jet yarn is mainly used to strengthen the reinforcing material of cement products (referred to as GRC). After the wire drawing is coated with sizing agent, it is rolled into a raw yarn drum, and then dried at 120-160 ° C, unwinding and plied into continuous fibers. The fibers are chopped and dispersed on the abrasive tool by a spray gun under a certain air pressure. Therefore, it is necessary to use a sizing agent with excellent performance when making continuous fibers to ensure the clustering, stiffness and lubricity of the glass fibers in the unwinding and plying, and at the same time to ensure the short-cutting and dispersibility of the fibers in the jet. [0003] Existing alkali-resistant glass fiber jet yarn sizing contains (wt%) [0004] Polyvinyl acetate film former 15.0-30.0 [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/42
Inventor 任川荣张棋任二室
Owner 陕西汇友友基新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com