A kind of lead-acid battery electrolyte and its preparation method and lead-acid battery

A lead-acid battery and electrolyte technology, applied in the direction of lead-acid battery, lead-acid battery construction, final product manufacturing, etc., can solve the problems of poor acid-fixing ability, short service life, large internal resistance, etc., and achieve low cost and excellent quality Thickening, reducing water loss effect

Inactive Publication Date: 2016-01-20
ZHEJIANG BOSSE POWER
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Ordinary electrolyte has high internal resistance, poor acid-fixing ability and short service life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] A kind of lead-acid accumulator electrolyte solution, comprises

[0039] 49.75wt% sulfuric acid,

[0040] 0.46wt% nano fumed silica,

[0041] 0.13 wt% potassium sulfate,

[0042] 0.20 wt% zinc sulfate,

[0043] 0.10 wt% ammonium sulfate,

[0044] 0.45 wt% magnesium sulfate,

[0045] 0.58wt% aluminum sulfate,

[0046] 0.85 wt% sodium sulfate,

[0047] 0.15 wt% nickel sulfate,

[0048] 0.05 wt% cobalt sulfate,

[0049] 0.48wt% lead sulfate,

[0050] 0.11 wt% lithium iodide,

[0051] 0.26 wt% hydroxymethylcellulose,

[0052] 0.41wt% polyvinyl alcohol,

[0053] 0.53 wt% polyethylene glycol ether,

[0054] 0.35 wt% sodium edetate,

[0055] The balance is deionized water.

[0056] A kind of preparation method of lead-acid storage battery electrolyte, it is characterized in that comprising the following steps:

[0057] A. Slowly pour 49.75wt% sulfuric acid into deionized water, and stir at a constant speed of 5-10r / min, so that the heat can be evaporated quickly...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lead-acid storage battery electrolyte, a preparation method thereof and a lead-acid storage battery, comprising sulfuric acid, nano fumed silicon dioxide, potassium sulfate, zinc sulfate, ammonium sulfate, magnesium sulfate, aluminum sulfate, sodium sulfate, nickel sulfate, Cobalt Sulfate, Lead Sulfate, Lithium Iodide, Hydroxymethylcellulose, Polyvinyl Alcohol, Polyethylene Glycol Ether, Sodium EDTA, and Deionized Water. The invention can solve the deficiencies of the prior art, can significantly increase the use times of the lead-acid storage battery, and is easy to popularize and use.

Description

technical field [0001] The invention relates to the technical field of lead-acid batteries, in particular to a lead-acid battery electrolyte, a preparation method thereof and a lead-acid battery. Background technique [0002] Since the lead-acid battery was invented in 1958, it has a history of more than 100 years. Lead-acid batteries have the advantages of simple structure, reliable performance, convenient use, easy access to raw materials and low price. They are widely used in many fields of national economy such as transportation, communication and national defense, and have become indispensable in social production and human life. energy products. [0003] The five major components of a lead-acid battery are the positive electrode, the negative electrode, the diaphragm, the electrolyte, and the battery case, among which the electrolyte is one of the main factors affecting battery performance. Ordinary electrolytes have large internal resistance, poor acid-fixing abilit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M10/10H01M10/12
CPCY02E60/10Y02P70/50
Inventor 钦辰钱建忠
Owner ZHEJIANG BOSSE POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com