Preparation method of POE (polyolefin elastomer) chemically-grafted maleic anhydride
A technology of polyolefin elastomer and maleic anhydride, which is applied in the field of preparation of polyolefin elastomer chemically grafted maleic anhydride, can solve problems such as incompatibility, prevent gel and yellowing, reduce odor and yellowing , the effect of low gel content
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0016] Example 1
[0017] A method for grafting maleic anhydride with polyolefin elastomer, dissolving maleic anhydride, initiator, heat stabilizer and polyolefin elastomer with acetone, and then putting the mixture into a single-screw extruder to melt, blend, and extrude granulation , The grafted POE-g-MAH of polyolefin elastomer and maleic acid was prepared; when pelletizing, the screw length-diameter ratio of the single-screw extruder was 30:1, and the shearing thread length was 35cm. The speed of the machine is 45HZ, the temperature of the extruder is 80-250℃, and the vacuum pressure is controlled at 0.08MPa.
[0018] In the implementation of this scheme, the initiator is dicumyl peroxide, the heat stabilizer is 3.5-di-tert-butyl-4-hydroxyphenylpropionic acid stearyl carbonate, and the grafting monomer is maleic anhydride; In points: 97.4 parts of polyolefin elastomer, 0.9 parts of maleic anhydride, 0.3 parts of initiator, 1 part of acetone, and 0.4 parts of heat stabilizer.
Example Embodiment
[0019] Example 2
[0020] A method for grafting maleic anhydride with polyolefin elastomer, dissolving maleic anhydride, initiator, heat stabilizer and polyolefin elastomer with acetone, and then putting the mixture into a single-screw extruder to melt, blend, and extrude granulation , The grafted POE-g-MAH of polyolefin elastomer and maleic acid was prepared; when granulating, the screw length-diameter ratio of the single-screw extruder was 35:1, the shear thread length was 35cm, and the extrusion The speed of the machine is 45HZ, the temperature of the extruder is 80-250℃, and the vacuum pressure is controlled at 0.08MPa.
[0021] In the implementation of this scheme, the initiator is dicumyl peroxide, the heat stabilizer is 3.5-di-tert-butyl-4-hydroxyphenylpropionic acid stearyl carbonate, and the grafting monomer is maleic anhydride; In points: 97.4 parts of polyolefin elastomer, 0.9 parts of maleic anhydride, 0.3 parts of initiator, 1 part of acetone, and 0.4 parts of heat st...
Example Embodiment
[0022] Example 3
[0023] A method for grafting maleic anhydride with polyolefin elastomer, dissolving maleic anhydride, initiator, heat stabilizer and polyolefin elastomer with acetone, and then putting the mixture into a single-screw extruder to melt, blend, and extrude granulation , The grafted POE-g-MAH of polyolefin elastomer and maleic acid was prepared; when granulating, the screw length-diameter ratio of the single-screw extruder was 40:1, the shear thread length was 35cm, and the extrusion The speed of the machine is 45HZ, and the temperature of the extruder is 80-250℃, and the vacuum pressure is controlled at 0.08MPa.
[0024] In the implementation of this scheme, the initiator is dicumyl peroxide, the heat stabilizer is 3.5-di-tert-butyl-4-hydroxyphenylpropionic acid stearyl carbonate, and the grafting monomer is maleic anhydride; In points: 97.4 parts of polyolefin elastomer, 0.9 parts of maleic anhydride, 0.3 parts of initiator, 1 part of acetone, and 0.4 parts of hea...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap