Copper complex having electrocatalytic activity on hydrogen peroxide and preparation method thereof

A technology of copper complexes and organic ligands, applied in the field of material chemistry, can solve the problems of poor stability of semiconductor oxides, low catalytic activity, complex catalyst preparation process, etc., and achieve good electrocatalytic activity.

Active Publication Date: 2013-12-25
菏泽建数智能科技有限公司
View PDF2 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Semiconductor oxides have relatively poor stability and low catalytic activity, and are still in the research and development stage; phthalocyanine and porphyrin macrocyclic conjugated complexes have good electrocatalytic activity due to their special macrocyclic conjugated structures. And it can be structurally adjustable by changing the substituent on its conjugated ring and the central metal atom and molecular aggregation mode, which endows it with a broad space for the development of electrocatalyst performance, and is one of the promising substitutes for platinum-based catalysts. One, but the preparation process of the catalyst is too complicated and there are many by-products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Copper complex having electrocatalytic activity on hydrogen peroxide and preparation method thereof
  • Copper complex having electrocatalytic activity on hydrogen peroxide and preparation method thereof
  • Copper complex having electrocatalytic activity on hydrogen peroxide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Weigh CuSO 4 ·5H 2 O (2.497g, 10mmol), H 4 Add L (0.269g, 1.0mmol) and 1,10-phenanthroline (0.180g, 1.0mmol) to 5.0mL distilled water, stir to dissolve; seal the reaction device and heat at 60°C for 60min, then take it out and cool to Room temperature; then use dilute KOH solution to adjust the mixed solution to be weakly acidic (pH=5); let it stand at room temperature, and slowly evaporate the solvent until crystals are precipitated. The solution was removed, and the massive crystals obtained by natural air drying were copper complexes.

[0021] Wherein, the ligand 5-(bis(carboxymethyl)amino)-2-hydroxybenzoic acid (H 4 L) Preparation method: KOH solution (12M, 20mL) was added dropwise into sodium chloroacetate (13.978g, 0.12mol) aqueous solution (20mL) and stirred, then 5-aminosalicylic acid (4.59g, 0.03mmol) Slowly added to the above mixture, reacted at 85°C for 30h. After the reaction, cool to room temperature, acidify with HCl solution (6mol / L) until precipitat...

Embodiment 2

[0023] Weigh CuCl 2 2H 2 O (0.170g, 1.0mmol), H 4 Add L (2.692g, 10mmol) and 1,10-phenanthroline (1.802g, 10mmol) to 40mL of distilled water, stir to dissolve; seal the reaction device and heat at 90°C for 15min, then take it out and cool to room temperature; Use dilute KOH solution to adjust the mixed solution to be weakly acidic (pH=7); let it stand at room temperature, and slowly evaporate the solvent until crystals are precipitated. The solution was removed, and the massive crystals obtained by natural air drying were copper complexes.

Embodiment 3

[0025] Weigh Cu(NO 3 ) 2 ·3H 2 O (0.483g, 2.0mmol), H 4 Add L (2.692g, 10mmol) and 1,10-phenanthroline (1.802g, 10mmol) to 15mL of distilled water, stir to dissolve; seal the reaction device and heat at 80°C for 30min, then take it out and cool to room temperature; Use dilute KOH solution to adjust the mixed solution to be weakly acidic (pH=6); let it stand at room temperature, and slowly evaporate the solvent until crystals are precipitated. The solution was removed, and the massive crystals obtained by natural air drying were copper complexes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a copper complex and a preparation method thereof, and the copper complex is characterized by having good electrocatalytic activity on hydrogen peroxide, the molecular formula of the copper complex is C46H34N6O14Cu2, the crystal system is clinorhomboidal, the space group is P-1, the cell parameters are as follows: alpha is equal to 99.90 degrees, beta is equal to 101.2 degrees and gamma is equal to 93.69 degrees. The copper complex is prepared from a mixing reaction of a copper salt, 5-(di(carboxymethyl) amino)-2-hydroxybenzoic acid and 1,10-phenanthroline according to a certain proportion, the copper complex has a specific spatial structure and an accurate molecular formula, the synthesis steps are simple, and the yield can reach 30-70%. The copper complex prepared in the invention has good electrocatalytic activity, thereby having a broad application prospect of being used as a potential electrocatalytic active material.

Description

technical field [0001] The invention relates to the field of material chemistry, in particular to a copper complex having electrocatalytic activity for hydrogen peroxide and a preparation method thereof. Background technique [0002] Electrocatalysis is a kind of catalysis that accelerates the reaction by charge transfer at the electrode-electrolyte interface. Electrocatalysis covers two aspects of electrode reaction and catalysis, so electrocatalysts must have these two functions at the same time: (1) be able to conduct electricity and transfer electrons relatively freely; (2) be able to effectively catalytically activate the substrate . Mainly used in electrocatalytic treatment of fuel cells and organic sewage; electrocatalytic degradation of chromium-containing wastewater; electrolytic desulfurization of flue gas and raw coal; simultaneous removal of NO by electrocatalysis x and SO 2 ; Electrolytic reduction of carbon dioxide; Electrolytic reduction of formaldehyde, hy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F1/08
Inventor 李星赵亚云赵秀华张洁康晶燕
Owner 菏泽建数智能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com