A kind of water-based composite exterior wall paint and preparation method thereof

An exterior wall coating, water-based technology, applied in the direction of coating, can solve the problems of high temperature resistance, weather resistance and water resistance, poor adhesion and environmental protection, and achieve the effect of huge market demand, good high temperature resistance and good application prospects.

Active Publication Date: 2015-09-16
广东施彩新材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In recent years, the research on exterior wall coatings has achieved certain results, but there are still many problems to be solved, such as defects such as high temperature resistance, weather resistance, water resistance, adhesion, and relatively poor environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of water-based composite exterior wall paint and preparation method thereof
  • A kind of water-based composite exterior wall paint and preparation method thereof
  • A kind of water-based composite exterior wall paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] 1. The mass percentage content of each component of the coating is:

[0012]

[0013] The particle size of the calcite powder, wollastonite powder, silicon dioxide powder, mica powder and talc powder is all 1000.

[0014] Two, the preparation method is:

[0015] According to the formula, first add water to the container of the mixer, start the mixer at a speed of 1500rP / min, add 930 rutile titanium dioxide, calcite powder, wollastonite powder and stir for 19-23 minutes; add silica sol emulsion and stir for 19-23 minutes After 10 minutes, add silica powder, mica powder and talcum powder respectively and continue to stir for 19-23 minutes, then add GHNK high temperature resistant emulsion and continue to stir for 19-23 minutes, then add alcohol fat twelve and stir for 29-33 minutes, and finally add GH5050 dispersant, leveling agent 2, 102 thickener, 981 preservative, and 202 defoamer continue to stir for 39-43 minutes, filter and pack into barrels to obtain a water-ba...

Embodiment 2

[0020] 1. The mass percentage content of each component of the coating is:

[0021]

[0022] The particle size of the calcite powder, wollastonite powder, silicon dioxide powder, mica powder and talc powder is all 1200 mesh.

[0023] Two, preparation method is with embodiment 1.

[0024] Three, the beneficial effects of this embodiment (compared with the prior art) are as follows in Table 2:

[0025] Table 2 Common Exterior Wall Paint and Example 2 Exterior Wall Paint Conventional Performance Test Comparison

[0026]

[0027]

Embodiment 3

[0029] 1. The mass percentage content of each component of the coating is:

[0030]

[0031] The particle size of the calcite powder, wollastonite powder, silicon dioxide powder, mica powder and talc powder is all 1300 mesh.

[0032] Two, preparation method is with embodiment 1.

[0033] Three, the beneficial effects of this embodiment (compared with the prior art) are as follows in Table 3:

[0034] Table 3 Common Exterior Wall Paint and Example 3 Exterior Wall Paint Conventional Performance Test Comparison

[0035]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a water-based composite exterior wall coating and a preparing method thereof. The coating includes the following components in mass percentage: 8-11% of water, 17-22% of silica sol emulsion, 18-21% of GHNK high temperature resistant emulsion, 10-15% of 930 rutile titanium dioxide, 5-8% of alcohol ester-12, 5-8% of calcite powder, 5-8% of wollastonite powder, 5-7% of silicon dioxide powder, 3-6% of mica powder, 5-8% of talcum powder, 0.3-0.9% of a GH5050 dispersing agent, 1.0-1.6% of a flatting agent 2, 0.1-0.5% of a 102 thickening agent, 0.1-0.2% of a 981 antiseptic agent and 0.1-0.2% of a 202 defoaming agent. The coating provided by the invention has the advantages of excellent high temperature resistance, weather resistance, water resistance, strong adhesive force, scrubbing resistance, artificial aging resistance and the like, meets the requirements of and is far superior to the national standards of GB / T9755-2001 and GB18583-2001, is a novel environment-friendly product for upgrading the building emulsion, and has excellent application prospect.

Description

technical field [0001] The invention relates to architectural paint technology, in particular to a novel water-based high-performance composite exterior wall paint and a preparation method thereof. Background technique [0002] Exterior wall coatings are mainly used to decorate and protect the exterior walls of buildings, so that the appearance of buildings is neat and beautiful, so as to achieve the purpose of beautifying the urban environment. decorative and protective effects. The exterior wall decoration is directly exposed to nature and is subjected to wind, rain, and sun exposure. Therefore, the coating is required to have water resistance, color retention, pollution resistance, aging resistance, and good adhesion. It also has good freeze-thaw resistance and film-forming properties. Features such as low temperature. In recent years, the research on exterior wall coatings has achieved certain results, but there are still many problems to be solved, such as high temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D183/04C09D7/12
Inventor 郭文录
Owner 广东施彩新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com