Release agent for scratch-resistant high temperature-resistant OPP (Oriented Polypropylene) heat transfer film and preparation method thereof

A thermal transfer film and release agent technology, applied in the direction of copying/marking, printing, coating, etc., can solve the problems of low temperature resistance, poor high temperature resistance, easy to scratch, etc., to achieve good scratch resistance, Good high temperature resistance, anti-ultraviolet effect

Inactive Publication Date: 2014-01-08
太仓市鸿运包装材料有限公司
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Due to the poor high temperature resistance of the base film material OPP film of the current OPP thermal transfer film, the prepared thermal transfer film has poor overall performance, is not resistant to high temperature, and is easy to be scratched.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film, mainly made of the following raw materials in parts by weight: 30 parts of polymethyl methacrylate, 10 parts of nano-titanium dioxide, 5 parts of microcrystalline wax, dithiodioxide 3 parts of dilauryl propionate, 50 parts of toluene.

[0020] A preparation method for a release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film, comprising the following steps:

[0021] 1) Weigh the raw materials in the above parts by weight;

[0022] 2) Acidification and alcoholization: Add 20 parts by weight of nitric acid to nano-titanium dioxide, react for 20 minutes, then add absolute ethanol, and heat at 80°C to obtain alcoholized nano-titanium dioxide;

[0023] 3) Dissolve polymethyl methacrylate in an organic solvent, add alcoholized nano-titanium dioxide, dilauryl thiodipropionate and microcrystalline wax at the same time, stir at 520rpm / min for 30mi...

Embodiment 2

[0028] A release agent for scratch-resistant and high-temperature resistant OPP thermal transfer film, mainly made of the following raw materials in parts by weight: 60 parts of polymethyl methacrylate, 30 parts of nano-titanium dioxide, 10 parts of Nano-R 1003, thio 5 parts of dilauryl dipropionate, 100 parts of toluene.

[0029] A preparation method for a release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film, comprising the following steps:

[0030] 1) Weigh the raw materials in the above parts by weight;

[0031] 2) Acidification and alcoholization: Add 30 parts by weight of nitric acid to nano-titanium dioxide, react for 30 minutes, then add absolute ethanol, and heat at 90°C to obtain alcoholized nano-titanium dioxide;

[0032] 3) Dissolve polymethyl methacrylate in an organic solvent, add alcoholized nano-titanium dioxide, dilauryl thiodipropionate and Nano-R 1003 at the same time, stir at 600rpm / min for 60min, and heat at 130°C ;...

Embodiment 3

[0037] A release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film, mainly made of the following raw materials in parts by weight: 45 parts of polymethyl methacrylate, 20 parts of nano-titanium dioxide, 7 parts of Nano-R 1003, thio 4 parts of dilauryl dipropionate, 75 parts of toluene.

[0038] A preparation method for a release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film, comprising the following steps:

[0039] 1) Weigh the raw materials in the above parts by weight;

[0040] 2) Acidification and alcoholization: Add 25 parts by weight of nitric acid to nano-titanium dioxide, react for 25 minutes, then add absolute ethanol, and heat at 85°C to obtain alcoholized nano-titanium dioxide;

[0041] 3) Dissolve polymethyl methacrylate in an organic solvent, add alcoholized nano-titanium dioxide, dilauryl thiodipropionate and Nano-R 1003 at the same time, stir at 560rpm / min for 45min, and heat at 125°C ; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a release agent for a scratch-resistant high temperature-resistant OPP (Oriented Polypropylene) heat transfer film. The release agent is prepared from the following raw materials in parts by weight: 30-60 parts of polymethyl methacrylate, 10-30 parts of nanometer titanium dioxide, 5-10 parts of scratch-resistant auxiliary agent, 3-5 parts of dilauryl thiodipropionate and 50-100 parts of organic solvents. The invention also discloses a preparation method of the release agent. According to the release agent for the scratch-resistant high temperature-resistant OPP heat transfer film, the polymethyl methacrylate is modified by the nanometer titanium dioxide, good scratch-resistant property is achieved through addition of a microcrystalline wax or Nano-R 1003 serving as the scratch-resistant auxiliary agents, and good high temperature-resistant property can be obtained by addition of the dilauryl thiodipropionate. The obtained release agent can be used for a preparation process of the heat transfer film and the prepared heat transfer film has the functions of ultraviolet prevention, scratch resistance, high temperature resistance and the like; the obtained OPP heat transfer film can be used in the fields of heat transfer printing, optics, advertising graphics, and the like.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a release agent for scratch-resistant and high-temperature-resistant OPP thermal transfer film and a preparation method thereof. Background technique [0002] Thermal transfer film is a polar material that is moisture-resistant, air-tight, soft, strong, resistant to acids, alkalis, greases and solvents, and is not afraid of high and low temperatures. The thermal transfer film currently produced on the market is prone to adhesion between the films due to the added release agent, and cannot be reused. [0003] The release agent is a low-viscosity transparent resin with release properties, film-forming properties and adhesive properties. Because the solvent in the release agent evaporates quickly, it is necessary to pay attention to controlling the viscosity during the coating process, that is, to control The solid content of the release agent is generally co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/12C09D7/12B41M5/382
Inventor 王向东
Owner 太仓市鸿运包装材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com