A flame retardant polypropylene cable material

A flame-retardant polypropylene and cable material technology, which is applied in the field of cable materials, can solve the problems of large shrinkage rate and easy sagging of thick-walled products, and achieve the effects of improved fluidity, good compatibility and reasonable formula

Inactive Publication Date: 2016-04-20
安徽华鸿电气股份有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Good formability, but due to large shrinkage (1%~2.5%), thick-walled products are easy to sag, and it is difficult to meet the requirements for some parts with high dimensional accuracy. The surface of the product has good gloss and is easy to color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] A flame-retardant polypropylene cable material, which is made from the following raw materials in parts by weight (kg): chlorinated polyethylene 100, isotactic polypropylene 20, magnesium stearate 2, aluminum hydroxide 15, magnesium hydroxide 4. Dibutyl maleate 2, calcium oxide 1.9, zinc oxide 1, zinc stearate 0.6, phthalic acid polyester 0.3, epoxy soybean oil 2, barium sulfate 2, modified dolomite powder 70, Methyltrimethoxysilane 1.72, antioxidant DLTP1.8;

[0017] Modified dolomite powder is made from the following raw materials in parts by weight:

[0018] Dolomite 25, heavy calcium carbonate 2, steel slag 2, antioxidant 22460.5, zinc oxide 2, chlorinated paraffin 1, zinc borate 6, toluene diphenyl phosphate 3.5, aluminum hydroxide 10;

[0019] The preparation method is to mix dolomite, heavy calcium carbonate, and steel slag, and then calcinate at 830°C for 3.5 hours, then take it out, add an appropriate amount of water to grind it together with aluminum hydroxid...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant polypropylene cable material. The flame-retardant polypropylene cable material is prepared from 100-110 weight parts of chlorinated polyethylene, 10-20 weight parts of isotactic polypropylene, 1-2 weight parts of magnesium stearate, 10-15 weight parts of aluminum hydroxide, 2-4 weight parts of magnesium hydroxide, 1-2 weight parts of dibutyl maleate, 1.5-3 weight parts of calcium oxide, 0.8-1 weight part of zinc oxide, 0.4-0.6 weight parts of zinc stearate, 0.3-0.5 weight parts of phthalic polyester, 1-2 weight parts of epoxidized soybean oil, 1-2 weight parts of barium sulfate, 60-70 weight parts of modified dolomite powder, 1-2 weight parts of methyltrimethoxysilane and 1.4-3 weight parts of an anti-oxidant DLTP.

Description

technical field [0001] The invention relates to the field of cable materials, in particular to a flame-retardant polypropylene cable material. Background technique [0002] Polypropylene is a non-toxic, odorless, tasteless milky white highly crystalline polymer with a density of only 0.90--"0.91g / m3. It is one of the lightest types of all plastics at present. It is particularly stable to water. The water absorption rate is only 0.01%, and the molecular weight is about 80,000 to 150,000. The formability is good, but due to the large shrinkage rate (1%~2.5%), thick-walled products are easy to sag, and it is difficult to achieve some parts with high dimensional accuracy. Requirements, the surface of the product has good gloss and is easy to color. [0003] Special resins for wire and cable include cable insulation materials and cable sheath materials, and the raw materials used are mainly polyethylene and polyvinyl chloride. [0004] Polyethylene is a crystalline thermoplasti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/28C08L23/12C08K13/06C08K9/00C08K3/34C08K3/26C08K3/22C08K5/523C08K3/38
CPCC08K2201/014C08L23/286C08L2201/02C08L2203/202C08L2205/03H01B3/441C08L23/12C08L67/02C08K13/06C08K9/00C08K2003/265C08K2003/267C08K2003/2296C08K5/12C08K5/523C08K3/38
Inventor 陈太锁
Owner 安徽华鸿电气股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com