A kind of high-strength and low-shrinkage industrial yarn of creep-resistant polyester and its preparation method

A creep-resistant, industrial yarn technology, applied in the direction of single-component copolyester rayon, conjugated synthetic polymer rayon, melt spinning, etc., to improve hydrolysis resistance, increase relative molecular weight, The effect of expanding the range of application

Active Publication Date: 2015-08-05
JIANGSU HENGLI CHEM FIBER
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are few studies on creep resistance of polyester fibers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of high-strength and low-shrinkage industrial yarn of creep-resistant polyester and its preparation method
  • A kind of high-strength and low-shrinkage industrial yarn of creep-resistant polyester and its preparation method
  • A kind of high-strength and low-shrinkage industrial yarn of creep-resistant polyester and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0055] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 1.5% of 15mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl) ethylene] diphenol mass, at room temperature Stir the reaction for 16 hours; then cool to room temperature, then add 5mol / L of 30% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol Sodium hydroxide solution, the sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 10 h; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick like liquid, which was added to absolute ethanol for recrystallization to obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]dip...

Embodiment 2

[0064] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0065] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 2.0% 10mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol mass, at room temperature Stir the reaction for 18 hours; cool to room temperature, then add 40% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol of 3mol / L Sodium hydroxide solution, sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 15 hours; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick liquid, add it to absolute ethanol for recrystallization, and obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl Crys...

Embodiment 3

[0074] Preparation of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl ether:

[0075] In a nitrogen atmosphere, mix epichlorohydrin and 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylidene]diphenol at a molar ratio of 4:1 , add 1.8% of 12mol / L sodium hydroxide solution of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol mass, at room temperature Stir the reaction for 17h; cool to room temperature, then add 35% of the mass of 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol of 4mol / L Sodium hydroxide solution, sodium hydroxide solution is a solution saturated with anhydrous sodium carbonate, stirred and reacted at room temperature for 13h; then extracted with chloroform, and the resulting organic phase was obtained by distilling off chloroform and excess epichlorohydrin to obtain a thick liquid, add it to absolute ethanol for recrystallization, and obtain 4,4'-[2,2,2-trifluoro-1-(trifluoromethyl)ethylene]diphenol diglycidyl Crystals of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
elongation at breakaaaaaaaaaa
shrinkageaaaaaaaaaa
Login to view more

Abstract

The invention relates to creep-resistant polyester high-strength low-shrinkage industrial yarn and preparation method thereof. The method comprises the preparation of creep-resistant polyester high-viscosity slice and the preparation of the creep-resistant polyester high-strength low-shrinkage industrial yarn. According to the invention, polyester is subjected to tackifying through solid-phase polycondensation; the polyester is subjected to a blending reaction with a fluorine-containing epoxy compound, such that the creep-resistant polyester high-viscosity slice is obtained; the creep-resistant polyester high-viscosity slice is subjected to measuring, extruding, cooling, oiling, stretching, heat setting, and winding, such that the creep-resistant polyester high-strength low-shrinkage industrial yarn is prepared. The creep-resistant polyester high-strength low-shrinkage industrial yarn has certain creep resistance, hydrolysis resistance, and performance stability. The yarn can be applied in high-temperature high-humidity environments for a long time. The yarn has great application prospect in the fields such as plastic packaging, waterproof fabrics, ropes, cables, marine fiber, and the like.

Description

technical field [0001] The invention relates to a high-strength and low-shrinkage industrial yarn of creep-resistant polyester and a preparation method thereof, in particular to a high-strength and low-shrinkage industrial yarn of creep-resistant polyester modified by using a fluorine-containing epoxy compound as an end-capping agent. Silk and its preparation method. Background technique [0002] Polyester (PET) is one of the most widely used synthetic polymers by humans. It has high strength, high modulus and good heat resistance. It is the earliest linear thermoplastic polymer to achieve industrial applications. It is used in plastic packaging, film And chemical fiber and other fields have been widely used. High-strength and low-shrinkage polyester industrial yarn is a large category of polyester. Due to its high strength, low thermal shrinkage rate, and excellent impact resistance, the fabric or rubber products made of it have good dimensional stability and heat resistan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/84D01F8/14D01D5/08D01D5/088C08G81/00
Inventor 于兆强王丽丽李文刚汤方明康爱旗
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap