A kind of brushing method of anti-mold and formaldehyde-removing paint
A coating and brushing technology, which is applied in antifouling/underwater coatings, devices for coating liquid on the surface, coatings, etc., can solve the problems of short duration and poor anti-mildew ability, and achieve simple operation and surface The layer is smooth and beautiful, and the brushing effect is beautiful and practical
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0023] A kind of brushing method of mildew-resistant and formaldehyde-removing paint, the composition ratio (by weight) of the paint is as follows: 100 parts of polystyrene-acrylic acid copolymer, 26 parts of talcum powder less than 100 microns, 8 parts of wetting agent, 6 parts of titanium dioxide, 10 parts of anti-mildew bactericide, 3 parts of bamboo charcoal, 40 parts of water, the anti-mold bactericide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1:1:0.5, the described brushing method includes the following steps:
[0024] 1) In the pre-treatment process, the wall surface to be painted is first polished with sandpaper, and then the surface is dedusted;
[0025] 2) Brush the primer, first brush the pre-treated wall with ordinary primer, dry at 43°C for 3 hours and then polish;
[0026] 3) Brush the primer again, step 2...
Embodiment 2
[0033] A method for painting an anti-mold and formaldehyde-removing paint. The composition ratio (by weight) of the paint is as follows: 100 parts of polyacrylic acid copolymer, 30 parts of talcum powder less than 100 microns, 3 powders of dispersant, 4 parts of wetting agent 10 parts, 10 parts of ultramarine blue, 8 parts of antimold bactericide, 5 parts of diatomaceous earth, 50 parts of water, and described antimold bactericide is nano-TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =2:1:0.5, the described brushing method includes the following steps:
[0034] 1) In the pre-treatment process, the wall surface to be painted is first polished with sandpaper, and then the surface is dedusted;
[0035] 2) Brush the primer, first brush the pre-treated wall with ordinary primer, dry at 47°C for 3 hours and then polish;
[0036] 3) Brush ...
Embodiment 3
[0043] A kind of brushing method of mildew-resistant and formaldehyde-removing paint, the composition ratio (by weight) of this paint is as follows: 100 parts of polyvinyl acetate-acrylic acid copolymer, 28 parts of talcum powders less than 100 microns, 2 parts of dispersant, moistening agent 2 parts of wet agent, 2 parts of defoamer, 2 parts of thickener, 8 parts of titanium dioxide, 9 parts of anti-mold and fungicide, 2 parts of activated carbon, 1 part of diatomaceous earth, 1 part of perlite, 45 parts of water, the Antifungal and fungicide is nano TiO 2 , Nano ZnO and ZrO 2 mixture of nano-TiO 2 , The particle size of nano-ZnO is 30-50 nanometers, ZrO 2 The particle size is -400 mesh, and the ratio of the three is TiO 2 :ZnO:ZrO 2 =1.5:1:0.5, the described brushing method comprises the following steps:
[0044] 1) In the pre-treatment process, the wall surface to be painted is first polished with sandpaper, and then the surface is dedusted;
[0045] 2) Brush the prim...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
particle size | aaaaa | aaaaa |
antibacterial rate | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com